| Feature: | Oxidative Degradable |
|---|---|
| CAS No.: | 32131-17-2 |
| Formula: | (C12h22n2o2)N |
| Samples: |
BAG
|
|---|
| Customization: |
|---|
|
Shipping Cost:
Estimated freight per unit. |
about shipping cost and estimated delivery time. |
|---|
| Payment Method: |
|
|---|---|
| Initial Payment Full Payment |
| Currency: | US$ |
|---|
| Return&refunds: | You can apply for a refund up to 30 days after receipt of the products. |
|---|
Suppliers with verified business licenses
Audited Supplier Resin Pellets PPA with 45 % Glass Fiber for High Mechanical Strength And Rigidity
https://forever-plastics.en.made-in-china.com/product/rJwRvlcdZpWD/China-Nylon-PA6-GF33-PA66-Granules-PA6-with-30GF-Polyamide-PA66-30-GF-PA6-Material.html Heat-conducting nylon
| Product Description | ||||
| A-1565 HS is a 65% glass and mineral-reinforced polyphthalamide (PPA) designed to be cost-effective in applications requiring high stiffness, good dimensional stability and good retention of stiffness at elevated temperatures. This grades also exhibits a high deflection temperature and flexural modulus. Black: A-1565 HS BK 324 | ||||
| General | ||||
| Form Resin Pellets | ||||
| Filler 65 % Glass Fiber/Mineral | ||||
| Low Warpage Low Clte Chemical Resistant | ||||
| Feature Creep Resistance Good Dimensional Good Thermal | ||||
| Enhanced Stiffness | ||||
| Uses | Hood | Pump Parts Automotive | ||
| Housing | ||||
| Physical Nominal Value Test Method | ||||
| Density, dry 1.90 g/cm³ ISO 1183/A | ||||
| Dry: Molding Shrinkage, Flow 0.30 % ASTM D955 | ||||
| Dry: Molding Shrinkage, Across Flow 0.50 % ASTM D955 | ||||
| Dry: Water Absorption(24 hr) 0.10 % ASTM D570 | ||||
| Mechanical Nominal Value Test Method | ||||
| Dry: Tensile Modulus | ||||
| 20700 MPa ASTM D638 | ||||
| 23 °C 19700 MPa ISO 527-2 | ||||
| 100 °C 15400 MPa ISO 527-2 | ||||
| 150 °C 5720 MPa ISO 527-2 | ||||
| 175 °C 5100 MPa ISO 527-2 | ||||
| Condition: Tensile Modulus 20800 MPa ASTM D638 | ||||
| Dry: Tensile Stress, Break ISO 527-2 | ||||
| 23 °C 138 MPa | ||||
| 100 °C 91.7 MPa | ||||
| 150 °C 46.2 MPa | ||||
| 175 °C 32.4 MPa | ||||
| Dry: Tensile Stress 131 MPa ASTM D638 | ||||
| Condition: Tensile Stress 123 MPa ASTM D638 | ||||
| Dry: Tensile Elongation, Break | 1.2 % | ASTM D638 | ||
| 23 °C | 1.0 % | ISO 527-2 | ||
| 100 °C | 1.3 % | ISO 527-2 | ||
| 150 °C | 2.4 % | ISO 527-2 | ||
| 175 °C | 1.8 % | ISO 527-2 | ||
| Condition: Tensile Elongation, Break | 1.2 % | ASTM D638 | ||
| Dry: Flexural Modulus | 17900 MPa | ASTM D790 | ||
| 23 °C | 9100 MPa | ISO 178 | ||
| 100 °C | 6830 MPa | ISO 178 | ||
| 150 °C | 2480 MPa | ISO 178 | ||
| 175 °C | 2280 MPa | ISO 178 | ||
| Condition: Flexural Modulus | 18000 MPa | ASTM D790 | ||
| Dry: Flexural Strength | 210 MPa |
ASTM D790 |
||
| 23 °C | 211 MPa | ISO 178 | ||
| 100 °C | 163 MPa | ISO 178 | ||
| 150 °C | 69.6 MPa | ISO 178 | ||
| 175 °C | 55.8 MPa | ISO 178 | ||
| Condition: Flexural Strength | 196 MPa | ASTM D790 | ||
| Dry: Compressive Strength(13 mm) | 189 MPa | ASTM D695 | ||
| Dry: Shear Strength | 71.0 MPa | ASTM D732 | ||
| Condition: Shear Strength | 49.6 MPa | ASTM D732 | ||
| Dry: Charpy Notched Impact Strength(23 °C) | 3.4 kJ/m² | ISO 179 1eA | ||
| Dry: Charpy Unnotched Impact Strength(23 °C) | 44 kJ/m² | ISO 179 1eU | ||
| Dry: Notched Izod Impact | 37 J/m |
ASTM D256 |
||
| 23 °C | 4.0 kJ/m² | ISO 180/1A | ||
| Izod Notched Impact: condition | 32 J/m | ASTM D256 | ||
| Dry: Unnotched Izod Impact | 410 J/m |
ASTM D256 |
||
| 23 °C | 32 kJ/m² | ISO 180/1U | ||
| Thermal | Nominal Value | Test Method | ||
| Dry: Deflection Temperature Under Load, Unannealed(1.8 MPa) | 271 °C | ISO 75-2/A;ASTM D648 | ||
| Dry: Melting Temperature | 311 °C | ASTM D3418;ISO 11357-3 | ||
| Dry: CLTE, Flow 0 - 100 °C 100 - 200 °C |
2.0E-5 cm/cm/°C 1.7E-5 cm/cm/°C |
ASTM E831 | ||
| Dry: CLTE, Transverse 0 - 100 °C 100 - 200 °C |
3.7E-5 cm/cm/°C 8.1E-5 cm/cm/°C |
ASTM E831 | ||
| Electrical | Nominal Value | Test Method | ||
| Dry: Volume Resistivity | 4.0E+14 ohms ·cm | ASTM D257 | ||
| Dry: Arc Resistance | 125 sec | ASTM D495 | ||
| Dry: Comparative Tracking Index, CTI | 600 V | UL 746 | ||
| Processing | Nominal Value | |||
| Drying Temperature<Injection> | 120 °C | |||
| Drying Time<Injection> | 4.0 hr | |||
| Suggested Max Moisture<Injection> | 0.030 - 0.060 % | |||
| Hopper Temperature<Injection> | 79 °C | |||
| Rear Temperature<Injection> | 304 - 318 °C | |||
| Front Temperature<Injection> | 316 - 329 °C | |||
| Processing Temp, Melt<Injection> | 321 - 343 °C | |||
| Mold Temperature<Injection> | 135 °C | |||