Feature: | Oxidative Degradable |
---|---|
CAS No.: | 32131-17-2 |
Formula: | (C12h22n2o2)N |
Samples: |
BAG
|
---|
Customization: |
---|
Shipping Cost:
Estimated freight per unit. |
about shipping cost and estimated delivery time. |
---|
Payment Method: | |
---|---|
Initial Payment Full Payment |
Currency: | US$ |
---|
Return&refunds: | You can apply for a refund up to 30 days after receipt of the products. |
---|
Suppliers with verified business licenses
Polyamine Nylon PPA With 35%GF FOR Resin Heat Conducting Nylon Resin
https://forever-plastics.en.made-in-china.com/product/rJwRvlcdZpWD/China-Nylon-PA6-GF33-PA66-Granules-PA6-with-30GF-Polyamide-PA66-30-GF-PA6-Material.html Heat-conducting nylon
General | ||
Form Resin Pellets | ||
Filler 35 % Glass Fiber | ||
Low Warpage | High Mechanical Strengt A d Ri idit | Good Thermal |
Feature | n g y | Anti Aging |
Good Dimensional | Enhanced Stiffness | |
Uses Industria | Automotive | |
Physical | Nominal Value | Test Method |
Density / Specific Gravity | 1.46 g/cm³ | ISO 1183 |
Molding Shrinkage, Flow | 0.3 - 0.6 % | ISO 294-4 |
Molding Shrinkage, Across Flow | 0.2 - 0.4 % | ISO 294-4 |
Mechanical | Nominal Value | Test Method |
Tensile Strength(20 mm/min) | 185 MPa | ISO 527-2 |
Elongation at Break(20 mm/min) | 3 % | ISO 527-2 |
Flexural Strength(2 mm/min) | 275 MPa | ISO 178 |
Flexural Modulus(2 mm/min) | 10500 MPa | ISO 178 |
Notched Izod Impact Strength | 10 kJ/m² | ISO 180 |
Thermal | Nominal Value | Test Method |
Deflection Temperature | ASTM D648 | |
0.45 MPa | 280 °C | |
1.82 MPa | 262 °C | |
Flammability(1.6 mm) | HB | UL94 |
Processing | Nominal Value | |
Drying Temperature | 130 - 150 °C | |
Drying Time | 2 - 4 | |
Mold Temperature | 120 - 150 °C | |
Melt Temperature | 300 - 325 °C |