| Feature: | Plastics |
|---|---|
| CAS No.: | 25766-59-0 |
| Formula: | C6h4c(CH3)2c6h4oco2-]N |
| Samples: |
25kg/bag
|
|---|
| Customization: |
|---|
|
Shipping Cost:
Estimated freight per unit. |
about shipping cost and estimated delivery time. |
|---|
| Payment Method: |
|
|---|---|
| Initial Payment Full Payment |
| Currency: | US$ |
|---|
| Return&refunds: | You can apply for a refund up to 30 days after receipt of the products. |
|---|
Suppliers with verified business licenses
Audited Supplier | Product Description | |||||||||||
| UL rated HB as of 10/97. 200 series recommended when V-2 rating required. Nonhalogenated. 7.0 MFR, for thicker sections without sinks. UV Stabilized for outdoor and lighting. Internal mold release. | |||||||||||
| General | |||||||||||
| Form | Resin Pellets | ||||||||||
Feature |
Outdoor | F1 | Non-Brominated & Non- Chlorinated Flame Retardant |
||||||||
| UL Yellow Card | E45587-103028650 | ||||||||||
| Appliances | Lighting Applications | Lenses | |||||||||
| Lawn And Garden | |||||||||||
| Uses | Equipment | ||||||||||
| Constraction | Household Applications | Outdoor | |||||||||
| Rail | Electrical | Medical | |||||||||
| Physical | Nominal Value | Test Method | |||||||||
| Density / Specific Gravity | 1.19 - 1.20 g/cm³ | ASTM D792 | |||||||||
| Specific Volume | 0.830 cm³/g | ASTM D792 | |||||||||
| Melt Mass-Flow Rate, MFR(300 °C;1.2 kg) | 7.0 g/10min | ASTM D1238 | |||||||||
| Molding Shrinkage, Flow(3.2 mm) | 0.50 - 0.70 % | Internal Method | |||||||||
| Water Absorption(24 hr) | 0.15 % | ASTM D570 | |||||||||
| Water Absorption, Equilibrium | ASTM D570 | ||||||||||
| 23 °C | 0.35 % | ||||||||||
| 100 °C | 0.58 % | ||||||||||
| Outdoor Suitability | f1 | UL 746C | |||||||||
| Rockwell Hardness, M-Scale | 70 | ASTM D785 | |||||||||
| Rockwell Hardness, R-Scale | 118 | ASTM D785 | |||||||||
| Mechanical Nominal Value | Test Method | ||||||||||
| Tensile Strength, Yield(50 mm/min;Type I) 62.0 MPa | ASTM D638 | ||||||||||
| Tensile Strength, Break(50 mm/min;Type I) 65.0 MPa | ASTM D638 | ||||||||||
| Tensile Elongation, Yield(50 mm/min;Type I) 7.0 % | ASTM D638 | ||||||||||
| Tensile Elongation, Break(50 mm/min;Type I) 110 % | ASTM D638 | ||||||||||
| Flexural Modulus(1.3 mm/min;50 mm;Span) 2340 MPa | ASTM D790 | ||||||||||
| Flexural Strength, Yield(1.3 mm/min;50 mm;Span) 93.0 MPa | ASTM D790 | ||||||||||
| Taber Abrasion Resistance(1.0e+3 Cycles;1.0e+3 g;CS-1710.0 mg Wheel) |
ASTM D1044 | ||||||||||
| Notched Izod Impact(23 °C) 910 J/m | ASTM D256 | ||||||||||
| Unnotched Izod Impact(23 °C) 3200 J/m | ASTM D4812 | ||||||||||
| Gardner Impact(23 °C) 169 J | ASTM D3029 | ||||||||||
| Tensile Impact Strength(Type S) 546 kJ/m² | ASTM D1822 | ||||||||||
| Thermal Nominal Value | Test Method | ||||||||||
| Deflection Temperature Under Load, Unannealed 0.45 MPa;6.4 mm 1.8 MPa;6.4 mm |
137 °C 132 °C |
ASTM D648 | |||||||||
| Vicat Softening Temperature(50 °C/h;50 N;Rate A;Loading 2) | 154 °C | ASTM D1525 | |||||||||
| CLTE, Flow(-40 - 95 °C) 6.8E-5 cm/cm/°C | ASTM E831 | ||||||||||
| Specific Heat 1250 J/kg/°C | ASTM C351 | ||||||||||
| Thermal Conductivity 0.19 W/m-K | ASTM C177 | ||||||||||
| RTI Elec 130 °C | UL 746 | ||||||||||
| RTI Imp 130 °C | UL 746 | ||||||||||
| RTI Str 130 °C | UL 746 | ||||||||||
| Flame Rating(0.76 mm) HB | UL 94 | ||||||||||
| Electrical | Nominal Value | Test Method | |||||||||
| Volume Resistivity | > 1.0E+17 ohms ·cm | ASTM D257 | |||||||||
| Dielectric Strength, in Air(3.2 mm) | 15 kV/mm | ASTM D149 | |||||||||
| Dielectric Constant 60 Hz 5.0e+4 Hz 1.0e+6 Hz |
3.17 3.17 2.96 |
ASTM D150 | |||||||||
| Dissipation Factor 50 Hz 60 Hz 1.0e+6 Hz |
9.0E-4 9.0E-4 0.010 |
ASTM D150 | |||||||||
| Comparative Tracking Index, CTI | PLC 2 | UL 746 | |||||||||
| High Amp Arc Ignition, HAI, Surface | PLC 1 | UL 746 | |||||||||
| High Voltage Arc Tracking Rate, HVTR | PLC 2 | UL 746 | |||||||||
| Hot-wire Ignition, HWI | PLC4 | UL 746 | |||||||||
| Optical | Nominal Value | Test Method | |||||||||
| Refractive Index | 1.586 | ASTM D542 | |||||||||
| Transmittance (2.5e+3 µm) | 88.0 % | ASTM D1003 | |||||||||
| Haze(2.5e+3 µm) | 1.00 % | ASTM D1003 | |||||||||
| Processing | Nominal Value | ||||||||||
| Drying Temperature<Injection> | 120 °C | ||||||||||
| Drying Time<Injection> | 3.0 - 4.0 hr | ||||||||||
| Suggested Max Moisture<Injection> | 0.020 % | ||||||||||
| Suggested Shot Size<Injection> | 40 - 60 % | ||||||||||
| Rear Temperature<Injection> | 290 - 310 °C | ||||||||||
| Middle Temperature<injection> | 300 - 320 °C | ||||||||||
| Front Temperature<Injection> | 310 - 330 °C | ||||||||||
| Nozzle Temperature<Injection> | 305 - 325 °C | ||||||||||
| Processing Temp, Melt<Injection> | 310 - 330 °C | ||||||||||
| Mold Temperature<Injection> | 80 - 115 °C | ||||||||||
| Back Pressure<Injection> | 0.300 - 0.700 MPa | ||||||||||
| Screw Speed <Injection> | 40 - 70 rpm | ||||||||||
| Vent Depth <Injection> | 0.025 - 0.076 mm | ||||||||||
| Drying Time, Cumulative<Injection> | 48 hrs | ||||||||||