Natural UV Light Stabilized Standard Flow Grade Acetal Copolymer POM Resin

• Application: Motor, Electric Cars, Motorcycle, Machinery, Marine, Toy, Agricultural Machinery, Car
• Hardness: Hardened Tooth Surface
• Gear Position: Internal Gear
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Model NO.: POM-M90UVXH
• Manufacturing Method: Injection
• Toothed Portion Shape: Curved Gear
• Material: Plastic
• Type: Circular Gear
• Name: Polyformaldehyde
• Appearance: Resins Granules Polyesters
• Impact Improved: Yes
• Applications: Gear Valve Buckles
• Filler: Glass Fiber
• Flame Retardant: Hb
• Transport Package: 25kg/Bag
• Trademark: FOREVER
• Origin: China
• HS Code: 3907400000
• Production Capacity: 10000
• Package Size: 75.00cm * 55.00cm * 15.00cm
• Package Gross Weight: 25.010kg

Product Description

Company Profile

Product Description

Product Parameters

Certifications

Packaging & Shipping

ITEM NO: POM M90UV-XH
FEATURE: Injection grade
 

M90UV-XH is a natural UV light stabilized standard flow grade acetal copolymer designed to provide excellent performance in various molding applications. It is specifically formulated to be a natural acetal resin that does not undergo discoloration, while still offering protection against UV light exposure.

 

General
Form		Resin Pellets
Feature		Outdoor
Physical			Nominal Value	Test Method
Density / Specific Gravity			1.41 g/cm³	ISO 1183
Melt Volume-Flow Rate, MVR(190 °C;2.16 kg)			8.0 cm³/10 min	ISO 1133
Water Absorption, Saturation(23 °C)			0.75 %	ISO 62
Water Absorption, Equilibrium(50% RH;23 °C)			0.20 %	ISO 62
Mechanical			Nominal Value	Test Method
Tensile Modulus			2600 MPa	ISO 527-2/1A
Tensile Stress, Yield			65.0 MPa	ISO 527-2/1A/50
Tensile Strain, Yield			10 %	ISO 527-2/1A/50
Flexural Modulus(23 °C)			2550 MPa	ISO 178
Flexural Stress(3.5% Strain)			70.0 MPa	ISO 178
C harpy Notched Impact Strength(23 °C)			6.1 kJ/m²	ISO 179 1eA
Notched Izod Impact Strength(23 °C)			5.8 kJ/m²	ISO 180/1A
Thermal			Nominal Value	Test Method
Heat Deflection Temperature, Unannealed(1.8 MPa)			101 °C	ISO 75-2/A
Vicat Softening Temperature			161 °C	ISO 306/B50
Melting Point			165 °C	ISO 11357-3
CLTE, Flow			1.1E-4 cm/cm/°C	ISO 11359-2
CLTE, Transverse			1.2E-4 cm/cm/°C	ISO 11359-2

 

 

Processing	Nominal Value
Drying Temperature<Injection>	100 - 120 °C
Drying Time<Injection>	3.0 - 4.0 hr
Rear Temperature<Injection>	170 - 180 °C
Middle Temperature<injection>	180 - 190 °C
Front Temperature<Injection>	180 - 190 °C
Nozzle Temperature<Injection>	190 - 200 °C
Processing Temp, Melt<Injection>	180 - 200 °C
Mold Temperature<Injection>	80 - 120 °C
Injection Rate<Injection>	Slow-Moderate
Back Pressure<Injection>	< 4.00 MPa
Zone4 temperature<Injection>	190 - 200 °C
Hot Runner Temperature<Injection>	180 - 200 °C

NOTICE: The data contained are based on our current knowledge and experience. This information may be subject to revision without informing in advance as new knowledge and experience become available. Because use conditions and applicable laws may differ from one location to another and may change with time, Customer is responsible for determining whether products and the information in t his document are appropriate for Customer's use and for ensuring that Customer's workplace and disposal practices are in compliance with applicable laws. Seller assumes no obligation or liability for the information in this document.