Glass Reinforced with PPA Resin and Uses a Non-Halogenated Flame Retardant

• Feature: Oxidative Degradable
• CAS No.: 32131-17-2
• Formula: (C12h22n2o2)N
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Model NO.: PPA-HTNFE170016 BK337
• EINECS: 211-024-8
• Material: Polyamide(Nylon 6.66)/PA
• Usage: General Plastics, Engineering Plastics, Specialty Plastics
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Injection
• Color: Black
• Form: Resin Pellets
• Chemical Substances: Nylon
• Processing Mode: Injection Molding/Extrusion
• UV: Fr
• Use: Electrical Appliances, Auto Parts, Office Supplies
• Certificates: ISO9001:2008.SGS.RoHS
• Filler: 5%-60% Glass Fiber
• Transport Package: Bag
• Specification: 25KG
• Trademark: Forever
• Origin: China
• HS Code: 390740000
• Production Capacity: 50000t/Year
• Package Size: 75.00cm * 55.00cm * 15.00cm
• Package Gross Weight: 25.010kg

Product Description

glass reinforced with PPA resin and uses a non-halogenated flame retardant
 Heat-conducting nylon

Product Description

Product Description
HTNFE170016 BK337 is a glass reinforced, flame retardant, high performance polyamide with low warpage characteristics. It is also a PPA resin and uses a non-halogenated flame retardant.
General
Form                                        Resin Pellets
Filler                                         54 % Glass Fiber
	Non-Brominated & Non-
Feature	Chlorinated Flame
	Retardant
Physical	Nominal Value	Test Method
Resin ID	PA-GF54FR(40)	ISO 1043
Part Marking Code, ISO 11469	PA-GF54FR(40)	ISO 11469
Density, dry	1.67 g/cm³	ISO 1183
Dry: Moulding shrinkage, parallel	0 %	ISO 294-4, ISO 2577
Dry: Moulding shrinkage, normal	0.1 %	ISO 294-4, ISO 2577
Mechanical	Nominal Value	Test Method
Dry: Tensile Modulus	19200 MPa	ISO 527-1/-2
Dry: Stress at break	215 MPa	ISO 527-1/-2
Dry: Strain at break	1.7 %	ISO 527-1/-2
Dry: Flexural Modulus	19200 MPa	ISO 178
Dry: Flexural Strength	320 MPa	ISO 178
Dry: Charpy Unnotched Impact Strength		ISO 179 1eU
23 °C	55 kJ/m²
-30 °C	50 kJ/m²
Dry: Charpy Notched Impact Strength		ISO 179 1eA
23 °C	14 kJ/m²
-30 °C	15 kJ/m²
Dry: Poisson's Ratio	0.33
Thermal	Nominal Value	Test Method
Dry: Melting Temperature(First Heat)	285 °C	ISO 11357-1/-3
Dry: Temp. of deflection under load(1.8 MPa)	227 °C	ISO 75-1/-2
Dry: Burning Behav. at thickness h(0.4 mm)	V-0	IEC 60695-11-10
Flammability, UL94(0.4 mm)	V-0	UL 94
Processing		Nominal Value
Drying Recommended		YES
Drying Temperature		≥ 100 °C
Drying Time, Dehumidified Dryer		6 - 8 h
Processing Moisture Content		≤ 0.1 %
Melt Temperature		300 - 315 °C
Mold Temperature		100 - 130 °C

 

                                                                                                                  Forever Co.,Ltd

 

With almost 20 years in the modified engineering plastics,Forever Plastics is a high-tech manufacture integrating R&D, production and sales of high-performance resin or polymer ,including PC,PP,PA6,PA66, PBT,PET, PC/ABS, PC/PBT, PC/PET alloy compounds,TPE,TPU, PE for rotomolding with the property of the flame retardant, glass fiber reinforced, high glossy, UV resistance.....with the annual output value of USD 65 million in 2021. 