Product Description | |||||
Features: High Rigidity; High Gloss; Medium Impact Strength | |||||
General | |||||
Form | Resin Pellets | ||||
Feature | High Mechanical Strength High Reflection And Rigidity |
Medium Impact Resistance | |||
Uses | Displays Telephone |
Tires Cosmetics package |
Copier Chassis | ||
Physical | Nominal Value | Test Method | |||
Melt Volume Rate, MVR | ISO 1133 | ||||
5 kg;200 ºC | 1.9 cm³/10 min | ||||
220 ºC;10 kg | 20 cm³/10 min | ||||
Rockwell Hardness R-Scale 105 | ASTM D785 | ||||
Density / Specific Gravity(23 ºC) 1.04 g/cm³ | ISO 1183 | ||||
Mechanical | Nominal Value | Test Method | |||
Tensile Strength(50 mm/min) 46 MPa | ISO 527 | ||||
Elongation at Break(50 mm/min) 20 % | ISO 527 | ||||
Flexural Strength(2 mm/min) 72 MPa | ISO178 | ||||
Flexural Modulus(2 mm/min) 2200 MPa | ISO178 | ||||
Notched Izod Impact Strength(23 ºC;4 mm) 18 kJ/m² | ISO 180 | ||||
Charpy impact strength(23 ºC;4 mm) 19 kJ/m² | ISO 179 | ||||
Thermal | Nominal Value | Test Method | |||
Vicat Softening Temperature(10 N;50 ºC/hr) 103 °C | ISO 306 | ||||
Deflection Temperature Under Load, Annealed(1.8 MPa) 94 °C | ISO 75-2 | ||||
Deflection Temperature Under Load, Unannealed(1.8 MPa) | 79 °C | ISO 75-2 | |||
Flammability(1.5 mm) | HB | UL-94 |
Product Description | ||||
A semi-conductive grade of acetal copolymer for applications requiring rapid dissipation of static build- up.Information provided by Celanese Corporation. | ||||
General | ||||
Form | Resin | Pellets | ||
Physical | Nominal Value | Test Method | ||
Density / Specific Gravity | 1.40 g/cm³ | |||
Water Absorption | 0.21 % | ASTM D570 | ||
Moisture Absorption at Equilibrium | 0.80 % | ASTM D570 | ||
Linear Mold Shrinkage | 2.2 % | |||
Linear Mold Shrinkage, Transverse | 1.8 % | |||
Hardness, Rockwell R | 111 | ASTM D785 | ||
Mechanical | Nominal Value | Test Method | ||
Tensile Strength, Yield | 37.0 MPa | ASTM D638 | ||
Elongation at Break | 30 % | ASTM D638 | ||
Flexural Strength | 52.0 MPa | ASTM D790 | ||
Flexural Modulus | 2100 MPa | ASTM D790 | ||
Compressive Strength | 66.0 MPa | ASTM D695 | ||
Shear Strength | 40.0 MPa | ASTM D732 | ||
Izod Impact, Notched Temperature; 23 °C Temperature; -29 °C |
50 J/m 30 J/m |
ASTM D256 | ||
Thermal | Nominal Value | Test Method | ||
Deflection Temperature Pressure; 0.46 MPa Pressure; 1.8 MPa |
152 °C 106 °C |
ASTM D648 | ||
Flammability, UL94 | HB | UL 94 |