| Feature: | Plastics |
|---|---|
| CAS No.: | 25766-59-0 |
| Formula: | C6h4c(CH3)2c6h4oco2-]N |
| Samples: |
BAG
|
|---|
| Customization: |
|---|
|
Shipping Cost:
Estimated freight per unit. |
about shipping cost and estimated delivery time. |
|---|
| Payment Method: |
|
|---|---|
| Initial Payment Full Payment |
| Currency: | US$ |
|---|
| Return&refunds: | You can apply for a refund up to 30 days after receipt of the products. |
|---|
Suppliers with verified business licenses
Audited Supplier polycarbonate (PC) siloxane copolymer resin is a transparent injection molding grade
https://forever-plastics.en.made-in-china.com/product-list-1.html
| Product Description | ||||||
| EXL1613TBL polycarbonate (PC) siloxane copolymer resin is a transparent injection molding grade with component synthesized from Bio source. This resin offers extreme lowtemperature ductility in combination with medium flow characteristics and excellent processability with opportunities for shorter IM cycle times compared to standard PC. ELCRIN EXL1613TBL resin is a general purpose product available in transparent and opaque colors and is an excellent candidate for a broad range of applications. |
||||||
| General | ||||||
| Form Resin Pellets | ||||||
| Filler Proprietary Filler | ||||||
| Good Thermal Low Temperature Impact High Impact | ||||||
| Feature Amorphous Good Surface Appearance | ||||||
| Uses | Electrical Personal Care |
Cell Phone Cases Energy Storage | Housing | |||
| Physical Nominal Value Test Method | ||||||
| Density / Specific Gravity 1.28 g/cm³ | ASTM D792;ISO 1183 | |||||
| Melt Mass-Flow Rate, MFR(300 °C;1.2 kg) 8 g/10 min ASTM D1238 | ||||||
| Melt Volume-Flow Rate, MVR(300 °C;1.2 kg) 7.5 cm³/10 min ISO 1133 | ||||||
| Molding Shrinkage, Flow 0.40 - 0.80 % Internal Method | ||||||
| Molding Shrinkage, Across Flow 0.40 - 0.80 % Internal Method | ||||||
| Water Absorption(24 hr;23°C) 0.04 % ISO 62 | ||||||
| Mechanical Nominal Value Test Method | ||||||
| Tensile Modulus | ||||||
| 50 mm/min 2100 MPa ASTM D638 | ||||||
| 2100 MPa ISO 527-1/1 | ||||||
| Tensile Strength, Yield | ||||||
| 50 mm/min;Type I 57.0 MPa ASTM D638 | ||||||
| 57.0 MPa ISO 527-2/50 | ||||||
| Tensile Strength, Break | ||||||
| 50 mm/min;Type I 49.0 MPa ASTM D638 | ||||||
| 47.0 MPa ISO 527-2/50 | ||||||
| Tensile Elongation, Yield 50 mm/min;Type I |
5.9 % 5.7 % |
ASTM D638 ISO 527-2/50 |
||||
| Tensile Elongation, Break 50 mm/min;Type I |
58 % 67 % |
ASTM D638 ISO 527-2/50 |
||||
| Flexural Modulus 1.3 mm/min;50 mm Span 2 mm/min |
2010 MPa 2100 MPa |
ASTM D790 ISO 178 |
||||
| Flexural Strength Yield(2 mm/min) | 85.0 MPa | ISO 178 | ||||
| Flexural Strength, Yield(1.3 mm/min;50 mm Span) | 90.0 MPa | ASTM D790 | ||||
| C harpy Impact Strength, Notched -30 °C;80*10*3 sp =62mm 23 °C;80*10*3 sp =62mm |
20 kJ/m² 70 kJ/m² |
ISO 179/1eA | ||||
| C harpy Impact Strength, Unnotched -30 °C;80*10*3 sp =62mm 23 °C;80*10*3 sp =62mm |
95 kJ/m² 95 kJ/m² |
ISO 179/1eU | ||||
| Notched Izod Impact -30 °C 23 °C -30 °C;80*10*3 mm 23 °C;80*10*3 mm |
690 J/m 900 J/m 20 kJ/m² 62 kJ/m² |
ASTM D256 ASTM D256 ISO 180/1A ISO 180/1A |
||||
| Unnotched Izod Impact -30 °C;80*10*3 mm 23 °C;80*10*3 mm |
130 kJ/m² 130 kJ/m² |
ASTM D4812;ISO 180/1U | ||||
| Dart Drop, Total Energy -30 °C 23 °C |
73.0 J 75.0 J |
ASTM D3763 | ||||
| Thermal | Nominal Value | Test Method | ||||
| Deflection Temperature Under Load, Unannealed | ||||||
| 1.8 MPa;3.2 mm | 122 °C | ASTM D648 | ||||
| 80*10*4 mm;1.8 MPa;4 mm;span;64 mm | 122 °C | ISO 75-2/Af | ||||
| Vicat Softening Temperature | ||||||
| 50 °C/h;50 N;Rate A;Loading 2 | 150 °C 143 °C 143 °C |
ASTM D1525 ISO 306/B120 ISO 306/B50 | ||||
| Ball Pressure Test(123 - 127 °C) | Pass | IEC 60695-10-2 | ||||
| CLTE, Flow | ||||||
| -40 - 95 °C | 7.2E-5 cm/cm/°C | ASTM E831 | ||||
| 23 - 80 °C | 7.7E-5 cm/cm/°C | ISO 11359-2 | ||||
| CLTE, Transverse | ||||||
| -40 - 95 °C | 7.6E-5 cm/cm/°C | ASTM E831 | ||||
| 23 - 80 °C | 8.3E-5 cm/cm/° | ISO 11359-2 | ||||
| Electrical | Nominal Value | Test Method | ||||
| Surface Resistivity | > 1.0E+15 Ohms | ASTM D257 | ||||
| Volume Resistivity | > 1.0E+15 Ohms ·cm | ASTM D257 | ||||
| Optical | Nominal Value | Test Method | ||||
| Transmittance (2.5e+3 µm) | 87.0 % | ASTM D1003 | ||||
| Haze(2.5e+3 µm) | 1.3 % | ASTM D1003 | ||||
| Processing | Nominal Value | |||||
| Drying Temperature<Injection> | 120 °C | |||||
| Drying Time<Injection> | 3.0 - 4.0 hr | |||||
| Suggested Max Moisture<Injection> | 0.020 % | |||||
| Suggested Max Regrind | 40 - 60 % | |||||
| Barrell Temperature - Rear | 285 - 305 °C | |||||
| Barrell Temperature - Middle | 295 - 315 °C | |||||
| Barrell Temperature - Front | 305 - 330 °C | |||||
| Nozzle Temperature | 300 - 320 °C | |||||
| Processing Temp, Melt | 300 - 330 °C | |||||
| Mold Temperature | 80 - 115 °C | |||||
| Back Pressure | 0.300 - 0.700 MPa | |||||
| Screw Speed | 40 - 70 rpm | |||||
| Vent Depth | 0.025 - 0.076 mm | |||||
| Drying Time, Cumulative | 48 hr | |||||