Hr156r Is a Compound Based on Copolymer Polycarbonate Resin Higher Rti

• Feature: Plastics
• CAS No.: 25766-59-0
• Formula: C6h4c(CH3)2c6h4oco2-]N
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Model NO.: PC-HR156R
• EINECS: 618-371-8
• Material: Polycarbonates/PC
• Usage: General Plastics, Engineering Plastics, Specialty Plastics
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Injection
• Color: Natural Color
• Place of Origin: Guangdong, China
• Use: Radiator Front Cover.Automotive Parts
• Features: Lubricated, Good Wear Resistance, Low Friction and
• Application: Zippers Irish Flutes, Bagpipes, Practice Chanters
• Form: Resin Pellets
• Delivery Time: in 7 Days
• Applications: Appliance Handles, Spotlights, Electric Motors.
• Glass Fiber: 0%
• Gr: 0%
• Carbon Fiber: 0 %
• Transport Package: Bag
• Specification: 25KG
• Trademark: Forever
• Origin: China
• HS Code: 390740000
• Production Capacity: 50000t/Year
• Package Size: 75.00cm * 55.00cm * 15.00cm
• Package Gross Weight: 25.010kg

Product Description

HR156R is a compound based on Copolymer Polycarbonate resin higher RTI
  
          

Product Description
LNP ELCRES HR156R is a compound based on Copolymer Polycarbonate resin. This resin has higher RTI, better scratch resistance and higher modulus than standard PC. It offers excellent heat resistance performance, good  processability and available for opaque or limited transparent colors
General
Form	Resin Pellets
Feature	Anti-Scratch      Good Thermal	Enhanced Stiffness            Excellent Processability
Uses                                         Appliances                         Lighting Applications        Electrical Engineering
Physical		Nominal Value	Test Method
Density / Specific Gravity		1.20 g/cm³	ASTM D792;ISO 1183
Melt Mass-Flow Rate, MFR(2.16 kg;330 °C)		45 g/10min	ASTM D1238
Melt Volume-Flow Rate, MVR(2.16 kg;330 °C)		42 cm³/10 min	ISO 1133
Molding Shrinkage, Flow(3.2 mm)		0.60 - 0.90 %	Internal Method
Water Absorption, Saturation(23 °C)		0.30 %	ISO 62
Water Absorption, Equilibrium(50% RH;23 °C)		0.23 %	ISO 62
Mechanical		Nominal Value	Test Method
Tensile Modulus
5 mm/min		2620 MPa	ASTM D638
		2650 MPa	ISO 527-1/1
Tensile Strength, Yield
50 mm/min;Type I		72.0 MPa	ASTM D638
		72.0 MPa	ISO 527-2/50
Tensile Strength, Break
50 mm/min;Type I		62.0 MPa	ASTM D638
		62.0 MPa	ISO 527-2/50
Tensile Elongation, Yield
50 mm/min;Type I		6.5 %	ASTM D638
		6.5 %	ISO 527-2/50
Tensile Elongation, Break
50 mm/min;Type I		90 %	ASTM D638
		90 %	ISO 527-2/50
Flexural Modulus 1.3 mm/min;50 mm;Span 2 mm/min		2600 MPa 2500 MPa	ASTM D790 ISO 178
Flexural Strength 1.3 mm/min;50 mm;Span 2 mm/min		111 MPa 102 MPa	ASTM D790 ISO 178
C harpy Notched Impact Strength -30 °C;80 23 °C;80 23 °C;80*10*4;sp =62mm 0		10 kJ/m² 12 kJ/m² 20 kJ/m²	ISO 179/1eA
C harpy Unnotched Impact Strength -30 °C;80 23 °C;80		No Break No Break	ISO 179/1eU
Notched Izod Impact -30 °C 23 °C -30 °C;80*10*3 mm 80*10*4 mm;-30 °C 23 °C;80*10*3 mm 80*10*4 mm;23 °C		73 J/m 110 J/m 10 kJ/m² 11 kJ/m² 11 kJ/m² 12 kJ/m²	ASTM D256 ASTM D256 ISO 180/1A ISO 180/1A ISO 180/1A ISO 180/1A
Unnotched Izod Impact Strength -30 °C;80*10*3 mm 23 °C;80*10*3 mm		No Break No Break	ISO 180/1U
Instrumented Dart Impact, Total Energy(23 °C)		68.0 J	ASTM D3763
Thermal		Nominal Value	Test Method
Deflection Temperature Under Load, Unannealed
0.45 MPa;3.2 mm		155 °C	ASTM D648
1.8 MPa;3.2 mm		145 °C	ASTM D648
80*10*4 mm;0.45 MPa;4 mm;64 mm;Span		155 °C	ISO 75-2/Bf
80*10*4 mm;1.8 MPa;4 mm;64 mm;Span		142 °C	ISO 75-2/Af
Vicat Softening Temperature
50 °C/h;50 N;Rate A;Loading 2		160 °C 162 °C	ISO 306/B50;ASTM D1525 ISO 306/B120
CLTE, Flow(-40 - 40 °C)		6.0E-5 cm/cm/°C	ASTM E831;ISO 11359-2
CLTE, Transverse(-40 - 40 °C)		6.0E-5 cm/cm/°C	ASTM E831;ISO 11359-2
Processing			Nominal Value
Drying Temperature<Injection>			125 °C
Drying Time<Injection>			4.0 - 6.0 hr
Suggested Max Moisture<Injection>			0.020 %
Suggested Shot Size<Injection>			40 - 60 %
Rear Temperature<Injection>			270 - 330 °C
Middle Temperature<injection>			280 - 340 °C
Front Temperature<Injection>			290 - 350 °C
Nozzle Temperature<Injection>			285 - 345 °C
Processing Temp, Melt<Injection>			290 - 350 °C
Mold Temperature<Injection>			85 - 130 °C
Back Pressure<Injection>			0.300 - 0.700 MPa
Screw Speed <Injection>			40 - 90 rpm
Vent Depth <Injection>			0.025 - 0.080 mm

Company Profile

Product Parameters

Our Customers

Our Certificates

 

Our Production

Our Package/Shipping

Our Advantages

 

Our Samples

 

Dongguan FOREVER Co., Ltd. Was founded in 2005 and is a national high-tech enterprise and national-level specialized giant enterprise dedicated to the research and production of polymer composite modified materials. With an annual capacity of 100, 000 tons of modified engineering plastics. Since its establishment, the company has been committed to the research of high-performance composite materials such as modified PC, PC/ABS, PBT, PA6, etc. Its products have been widely used in industries such as LED lighting, consumer electronics, new energy, security equipment, and small household appliances, providing customers with efficient delivery experience, ultimate price advantages, and strict quality assurance, contributing to the creation of a green and environmentally friendly world.

Dongguan FOREVER Co., Ltd's main products has obtained UL certification for RTI authorized temperature, outdoor weather resistance F1 and 5VA flame retardancy grades, as well as recycled-certified post-consumer low-carbon circulation products. Dongguan FOREVER Co., Ltd's products are highly recognized by customers worldwide for their reliable quality, excellent performance, and superior cost-effectiveness.

With a strong focus on research and development, Dongguan FOREVER Co., Ltd. Has established an advanced technology research and development center, equipped with state-of-the-art testing and analysis equipment and a professional R&D team that has accumulated rich experience in the field of polymer composite modified materials. Dongguan FOREVER Co., Ltd also maintains close partnerships with renowned universities and research institutions to stay at the forefront of technology and drive innovation in the industry