General POM Resin Pellets Feature Low Voc Emission for Automotive Housing Engineering Parts

• Feature: Resin Pellets
• CAS No.: 25037-45-0
• Formula: 25037-45-0
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Model NO.: POM-Z4520
• EINECS: 25037-45-0
• Material: Polyacetal/POM
• Usage: General Plastics, Engineering Plastics, Specialty Plastics
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Injection
• Color: White
• Place of Origin: Guangdong, China
• Use: Fully Automatic Coffee Brewers; Knife Handles
• Features: Lubricated, Good Wear Resistance, Low Friction and
• Application: Zippers Irish Flutes, Bagpipes, Practice Chanters
• Form: Resin Pellets
• Transport Package: Bag
• Specification: 25KG
• Trademark: Forever
• Origin: China
• HS Code: 390740000
• Production Capacity: 50000t/Year
• Package Size: 75.00cm * 50.00cm * 15.00cm
• Package Gross Weight: 25.000kg

Product Description

 General POM Resin Pellets Feature Low Voc Emission for  Automotive  Housing Engineering Parts        
 
Product Description

General
Form	Resin Pellets
Feature	Low Voc Emission
Automotive   Housing		Engineering Parts		Gear Wheels
Physical		Nominal Value		Test Method
Density / Specific Gravity		1.41 g/cm³		ASTM D792;ISO 1183
Melt Mass-Flow Rate, MFR(2.16 kg;190 ºC)		9 g/10 min		ISO 1183
Molding Shrinkage, Flow		1.6 - 2.0 %		Internal Method
Water Absorption(50% RH;24 hr;23 °C)		0.2 %		ASTM D570
Hardness, Rockwell, M-scale		80		ASTM D785
Hardness, Rockwell, R-scale		115		ASTM D785
Mechanical		Nominal Value		Test Method
Tensile Modulus		2700 MPa		ISO 527-1
Tensile Strength, Yield		63 MPa		ISO 527-2
Tensile Strength		63 MPa		ASTM D638
Tensile Elongation, Break		35 % 35 %		ASTM D638 ISO 527-2
Flexural Modulus		2550 MPa 2500 MPa		ASTM D790 ISO 178
Flexural Stress		90 MPa		ASTM D790
Taber Abrasion		14 mg		ASTM D1044
Charpy Impact Strength, Notched		7 kJ/m²		ISO 179
Notched Izod Impact		77 J/m		ASTM D256

 

Thermal	Nominal Value	Test Method
Deflection Temperature Under Load, Unannealed
0.45 MPa	158 °C	ASTM D648
1.8 MPa	110 °C	ASTM D648
0.45 MPa	156 °C	ISO 75-2/B
1.8 MPa	100 °C	ISO 75-2/A
CTE, Flow	1.0E-4 cm/cm/°C	ASTM D696;ISO 11359-2
Specific Heat	1470 J/kg/ºC
Thermal Conductivity	0.23 W/m/K
Electrical	Nominal Value	Test Method
Specific surface resistivity	1.0E+16 - 1.0E+17 ohms	ASTM D257
Volume Resistivity(23 ºC)	1.0E+15 - 1.0E+16 ohms·cm	ASTM D257
Dielectric Strength	19 kV/mm	ASTM D149
Dielectric Constant(23 ºC;1 MHz)	3.9	ASTM D150
Dissipation Factor(23 ºC;1 MHz)	8.0E-3	ASTM D150
Arc Resistance	250 sec	ASTM D495

Company Profile

Product Parameters

 

Product Description
A semi-conductive grade of acetal copolymer for applications requiring rapid dissipation of static build- up.Information provided by Celanese Corporation.
General
Form	Resin	Pellets
Physical			Nominal Value	Test Method
Density / Specific Gravity			1.40 g/cm³
Water Absorption			0.21 %	ASTM D570
Moisture Absorption at Equilibrium			0.80 %	ASTM D570
Linear Mold Shrinkage			2.2 %
Linear Mold Shrinkage, Transverse			1.8 %
Hardness, Rockwell R			111	ASTM D785
Mechanical			Nominal Value	Test Method
Tensile Strength, Yield			37.0 MPa	ASTM D638
Elongation at Break			30 %	ASTM D638
Flexural Strength			52.0 MPa	ASTM D790
Flexural Modulus			2100 MPa	ASTM D790
Compressive Strength			66.0 MPa	ASTM D695
Shear Strength			40.0 MPa	ASTM D732
Izod Impact, Notched Temperature; 23 °C Temperature; -29 °C			50 J/m 30 J/m	ASTM D256
Thermal			Nominal Value	Test Method
Deflection Temperature Pressure; 0.46 MPa Pressure; 1.8 MPa			152 °C 106 °C	ASTM D648
Flammability, UL94			HB	UL 94

 

Our Customers

Our Certificates

 

Our Production

Our Package/Shipping

Our Advantages

 

Our Samples

 

Dongguan FOREVER Co., Ltd. Was founded in 2005 and is a national high-tech enterprise and national-level specialized giant enterprise dedicated to the research and production of polymer composite modified materials. With an annual capacity of 100, 000 tons of modified engineering plastics. Since its establishment, the company has been committed to the research of high-performance composite materials such as modified PC, PC/ABS, PBT, PA6, etc. Its products have been widely used in industries such as LED lighting, consumer electronics, new energy, security equipment, and small household appliances, providing customers with efficient delivery experience, ultimate price advantages, and strict quality assurance, contributing to the creation of a green and environmentally friendly world.

Dongguan FOREVER Co., Ltd's main products has obtained UL certification for RTI authorized temperature, outdoor weather resistance F1 and 5VA flame retardancy grades, as well as recycled-certified post-consumer low-carbon circulation products. Dongguan FOREVER Co., Ltd's products are highly recognized by customers worldwide for their reliable quality, excellent performance, and superior cost-effectiveness.

With a strong focus on research and development, Dongguan FOREVER Co., Ltd. Has established an advanced technology research and development center, equipped with state-of-the-art testing and analysis equipment and a professional R&D team that has accumulated rich experience in the field of polymer composite modified materials. Dongguan FOREVER Co., Ltd also maintains close partnerships with renowned universities and research institutions to stay at the forefront of technology and drive innovation in the industry.