General | ||||||
Form | Resin Pellets | |||||
Abrasion Resistant Internally Lubricated Excellent Processability Low Friction |
||||||
Uses | Engineering | Parts | Gear Wheels | |||
Physical | Nominal Value | Test Method | ||||
Density / Specific Gravity | 1.39 g/cm³ | ASTM D792;ISO 1183 |
||||
Melt Mass-Flow Rate, MFR(2.16 kg;190 ºC) | 30 g/10 min | ISO 1183 | ||||
Molding Shrinkage, Flow | 1.6 - 2 % | Internal Method | ||||
Water Absorption(50% RH;24 hr;23 °C) | 0.2 % | ASTM D570 | ||||
Hardness, Rockwell, M-scale | 86 | ASTM D785 | ||||
Hardness, Rockwell, R-scale | 117 | ASTM D785 | ||||
Mechanical | Nominal Value | Test Method | ||||
Tensile Modulus | 2700 MPa | ISO 527-1 | ||||
Tensile Strength, Yield | 62 MPa | ISO 527-2 | ||||
Tensile Strength | 60 MPa | ASTM D638 | ||||
Tensile Elongation, Break | 20 % 15 % |
ASTM D638 ISO 527-2 |
||||
Flexural Modulus | 2800 MPa 2700 MPa |
ASTM D790 ISO 178 |
||||
Flexural Stress | 91 MPa | ASTM D790 | ||||
Charpy Impact Strength, Notched | 3 kJ/m² | ISO 179 | ||||
Notched Izod Impact | 35 J/m | ASTM D256 |
Thermal | Nominal Value | Test Method |
Deflection Temperature Under Load, Unannealed | ||
0.45 MPa | 157 °C | ASTM D648 |
1.8 MPa | 100 °C | ASTM D648 |
0.45 MPa | 157 °C | ISO 75-2/B |
1.8 MPa | 100 °C | ISO 75-2/A |
CTE, Flow | 1.0E-4 cm/cm/°C |
ASTM D696 |
1.0E-4 cm/cm/°C | ISO 11359-2 | |
Flame Rating(0.75 mm) | HB | UL 94 |
Product Description | ||||
A semi-conductive grade of acetal copolymer for applications requiring rapid dissipation of static build- up.Information provided by Celanese Corporation. | ||||
General | ||||
Form | Resin | Pellets | ||
Physical | Nominal Value | Test Method | ||
Density / Specific Gravity | 1.40 g/cm³ | |||
Water Absorption | 0.21 % | ASTM D570 | ||
Moisture Absorption at Equilibrium | 0.80 % | ASTM D570 | ||
Linear Mold Shrinkage | 2.2 % | |||
Linear Mold Shrinkage, Transverse | 1.8 % | |||
Hardness, Rockwell R | 111 | ASTM D785 | ||
Mechanical | Nominal Value | Test Method | ||
Tensile Strength, Yield | 37.0 MPa | ASTM D638 | ||
Elongation at Break | 30 % | ASTM D638 | ||
Flexural Strength | 52.0 MPa | ASTM D790 | ||
Flexural Modulus | 2100 MPa | ASTM D790 | ||
Compressive Strength | 66.0 MPa | ASTM D695 | ||
Shear Strength | 40.0 MPa | ASTM D732 | ||
Izod Impact, Notched Temperature; 23 °C Temperature; -29 °C |
50 J/m 30 J/m |
ASTM D256 | ||
Thermal | Nominal Value | Test Method | ||
Deflection Temperature Pressure; 0.46 MPa Pressure; 1.8 MPa |
152 °C 106 °C |
ASTM D648 | ||
Flammability, UL94 | HB | UL 94 |