PA66 40% glass/mineral reinforced pigmented black injection molding grade
https://forever-plastics.en.made-in-china.com/product/rJwRvlcdZpWD/China-Nylon-PA6-GF33-PA66-Granules-PA6-with-30GF-Polyamide-PA66-30-GF-PA6-Material.html Heat-conducting nylon
Product Description | |||||
A3WGM53 BK20560 is a 40% glass/mineral reinforced, pigmented black, injection molding grade for high stiffness parts with good dimensional stability and surface finish. Applications Typical applications include automotive cylinder-head cover. | |||||
General | |||||
Form Resin Pellets | |||||
Filler 40 % Glass Fiber/Mineral | |||||
Feature | Good Dimensional Fuel Resistant | Good Surface Appearance Good Hardness Ec 1907/2006 (Reach) |
|||
Uses | Automotive Under The Hood |
||||
Physical Nominal Value Test Method | |||||
Density, dry 1.48 g/cm³ ISO 1183 | |||||
Dry: Melt Volume-Flow Rate, MVR(275 °C;5 kg) 30 cm³/10 min ISO 1133 | |||||
Dry: Water Absorption, Saturation(23 °C) 5.1 % ISO 62 | |||||
Dry: Water Absorption, Equilibrium(50% RH;23 °C) 1.4 % ISO 62 | |||||
Dry: Ball Indentation Hardness 230 MPa ISO 2039-1 | |||||
Condition: Ball Indentation Hardness 90.0 MPa ISO 2039-1 | |||||
Mechanical | Nominal Value | Test Method | |||
Dry: Tensile Modulus(23 °C) | 12100 MPa | ISO 527-2 | |||
Condition: Tensile Modulus(23 °C) | 6100 MPa | ISO 527-2 | |||
Dry: Tensile Stress, Break(23 °C) | 160 MPa | ISO 527-2 | |||
Condition: Tensile Stress, Break(23 °C) | 80.0 MPa | ISO 527-2 | |||
Dry: Tensile Strain, Break(23 °C) | 2.3 % | ISO 527-2 | |||
Condition: Tensile Strain, Break(23 °C) | 6.0 % | ISO 527-2 | |||
Dry: Flexural Modulus(23 °C) | 10100 MPa | ISO 178 | |||
Condition: Flexural Modulus(23 °C) | 5500 MPa | ISO 178 | |||
Dry: Flexural Stress(23 °C) | 225 MPa | ISO 178 | |||
Condition: Flexural Stress(23 °C) | 125 MPa | ISO 178 | |||
Dry: Charpy Notched Impact Strength -30 °C 23 °C |
6.7 kJ/m² 8.0 kJ/m² |
ISO 179 | |||
Condition: Charpy Notched Impact Strength(23 °C) | 16 kJ/m² | ISO 179 | |||
Dry: Charpy Unnotched Impact Strength -30 °C 23 °C |
50 kJ/m² 55 kJ/m² |
ISO 179 | |||
Condition: Charpy Unnotched Impact Strength(23 °C) | 62 kJ/m² | ISO 179 | |||
Dry: Notched Izod Impact Strength -30 °C 23 °C |
7.5 kJ/m² 9.5 kJ/m² |
ISO 180 | |||
Notched Izod Impact Strength: condition(23 °C) | 16 kJ/m² | ISO 180 | |||
Thermal | Nominal Value | Test Method | |||
Dry: Heat Deflection Temperature, Unannealed 0.45 MPa 1.8 MPa |
250 °C 225 °C |
ISO 75-2/B ISO 75-2/A |
|||
Dry: Melting Temperature, DSC | 260 °C | ISO 3146 | |||
Dry: CLTE - Flow | 1.5E-5 cm/cm/°C | No Standard | |||
Electrical | Nominal Value | Test Method | |||
Dry: Volume Resistivity | 1.0e+15 ohms ·cm | IEC 60093 | |||
Condition: Volume resistivity | 1.0E+12 ohms ·cm | IEC 60093 | |||
Dry: Dielectric Constant(1.0e+6 Hz) | 4.00 | IEC 60250 | |||
Processing | Nominal Value | ||||
Drying Temperature<Injection> | 80 °C | ||||
Drying Time<Injection> | 2.0 - 4.0 hr | ||||
Suggested Max Moisture<Injection> | 0.15 % | ||||
Processing Temp, Melt<Injection> | 280 - 305 °C | ||||
Mold Temperature<Injection> | 80 - 90 °C | ||||
Injection Pressure<Injection> | 3.50 - 12.5 MPa | ||||
Injection Rate<Injection> | Fast |