Audited Supplier RZL16 compound is based on Nylon 66 resin containing 30% milled glass 5% PTFE
https://forever-plastics.en.made-in-china.com/product/rJwRvlcdZpWD/China-Nylon-PA6-GF33-PA66-Granules-PA6-with-30GF-Polyamide-PA66-30-GF-PA6-Material.html Heat-conducting nylon
| Product Description | ||||||
| RZL16 compound is based on Nylon 6/6 resin containing 30% milled glass, 5% PTFE. Added features of this grade include: Wear Resistant, Dimensional Control. | ||||||
| General | ||||||
| Form | Resin Pellets | |||||
| Filler 5 % PTFE 30 % Milled Glass Fiber | ||||||
| Feature | Low Warpage Internally Lubricated |
Good Dimensional Abrasion Resistant | ||||
| Uses Consumer Electrical Building and Construction | ||||||
| Physical Nominal Value Test Method | ||||||
| Density / Specific Gravity 1.4 1.39 g/cm³ |
ASTM D792 | |||||
| Moisture Absorption | ||||||
| 23 °C;50% RH/24 hrs 0.69 % ASTM D570 | ||||||
| 50% RH;23 °C 0.96 % ISO 62 | ||||||
| Mold Shrinkage, Flow(24 hrs) 1.8 % ASTM D955 | ||||||
| Mold Shrinkage, XFlow(24 hrs) 1.4 % ASTM D955 | ||||||
| Wear Factor Washer 44 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified: Manual |
|||||
| Wear Factor, Ring 3 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified: Manual |
|||||
| Dynamic Cof 0.49 | ASTM D3702 Modified: Manual |
|||||
| Static Cof 0.53 | ASTM D3702 Modified: Manual |
|||||
| Mechanical | Nominal Value | Test Method | ||||
| Izod Impact, Unnotched | ||||||
| 23 °C | 188 J/m | ASTM D4812 | ||||
| 80*10*4;23 °C | 19 kJ/m² | ISO 180/1U | ||||
| Izod Impact, Notched | ||||||
| 23 °C | 32 J/m | ASTM D256 | ||||
| 80*10*4;23 °C | 4 kJ/m² | ISO 180/1A | ||||
| Multiaxial Impact | 1 J | ISO 6603 | ||||
| Instrumented Dart Impact, Total Energy(23 °C) | 5 J | ASTM D3763 | ||||
| Tensile Stress, Yield | ||||||
| 5 mm/min;Type I | 63 MPa | ASTM D638 | ||||
| 5 mm/min | 64 MPa | ISO 527 | ||||
| Tensile Stress, Break | ||||||
| 5 mm/min;Type I | 62 MPa | ASTM D638 | ||||
| 5 mm/min | 63 MPa | ISO 527 | ||||
| Tensile Strain, Yield | ||||||
| 5 mm/min;Type I | 2.4 % | ASTM D638 | ||||
| 5 mm/min | 2 % | ISO 527 | ||||
| Tensile Strain, Break | ||||||
| 5 mm/min;Type I | 3.2 % | ASTM D638 | ||||
| 5 mm/min | 3 % | ISO 527 | ||||
| Tensile Modulus | ||||||
| 5 mm/min | 5420 MPa | ASTM D638 | ||||
| 1 mm/min | 5380 MPa | ISO 527 | ||||
| Flexural Stress, break(1.3 mm/min;50 mm;span) | 102 MPa | ASTM D790 | ||||
| Flexural Modulus | ||||||
| 1.3 mm/min;50 mm;span | 4410 MPa | ASTM D790 | ||||
| 2 mm/min | 4500 MPa | ISO 178 | ||||
| Flexural Stress | 90 MPa | ISO 178 | ||||
| Thermal | Nominal Value | Test Method | ||||
| Heat Deflection Temperature[HDT], Unannealed 0.45 MPa;3.2 mm 3.2 mm;1.82 MPa |
248 °C 215 °C |
ASTM D648 | ||||
| CTE, Flow(-30 - 30 °C) | 5.5e-05 1/°C | ASTM D696 | ||||
| CTE, XFlow(-30 - 30 °C) | 6.2e-05 1/°C | ASTM D696 | ||||
| HDT/Bf(0.45) | 239 °C | ISO 75/Bf | ||||
| Processing | Nominal Value | |||||
| Drying Temperature<Injection> | 80 °C | |||||
| Drying Time<Injection> | 4 hrs | |||||
| Maximum Moisture Content<Injection> | 0.15 - 0.25 % | |||||
| Melt Temperature<Injection> | 280 - 305 °C | |||||
| Front, Zone 3 Temperature<Injection> | 295 - 305 °C | |||||
| Middle, Zone 2 Temperature<Injection> | 280 - 295 °C | |||||
| Rear, Zone 1 Temperature<Injection> | 265 - 275 °C | |||||
| Mold Temperature<Injection> | 95 - 110 °C | |||||
| Back Pressure<Injection> | 0.2 - 0.3 MPa | |||||
| Screw Speed <Injection> | 30 - 60 rpm | |||||