Basfse PA6 GF15 Ultramid B3eg3/A3eg3 Bk00564 Polyamide 6 Nylon6 Resin 15% Glass Fiber Reinforced Plastic Raw Material Pellets

• Feature: Oxidative Degradable
• Material: Polyamide(Nylon 6.66)/PA
• Usage: General Plastics, Engineering Plastics, Specialty Plastics
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Injection
• Color: White
• Form: Resin Pellets
• Chemical Substances: Nylon
• Processing Mode: Injection Molding/Extrusion
• UV: Fr
• Use: Electrical Appliances, Auto Parts, Office Supplies
• Certificates: ISO9001:2008.SGS.RoHS
• Filler: 15% Glass Fiber
• Transport Package: Bag
• Specification: 25KG
• Trademark: Forever
• Origin: China
• HS Code: 390740000
• Production Capacity: 50000t/Year

Product Description

BASFSE PA6 GF15 Ultramid B3EG3/A3EG3 BK00564 Polyamide 6 Nylon6 Resin 15% Glass Fiber Reinforced plastic raw material pellets

  216 gf30 BK Z/4 is a polyamide 6, reinforced with 30% of glass fibre, for injection moulding. This grade has good mechanical properties and offering an excellent combination between thermal and mechanical           properties.

Product Description
216 gf30 BK Z/4 is a polyamide 6, reinforced with 30% of glass fibre, for injection moulding. This grade has good mechanical properties and offering an excellent combination between thermal and mechanical               properties.
General
Form	Resin Pellets
Filler	30 % Glass Fiber
Feature	Rohs	Ec 1907/2006 (Reach)
Uses	Automotive	Handles
Physical		Nominal Value	Test Method
Density		1.36 g/cm³	ISO 1183
Water Absorption(24 hr;23 °C)		1.1 %	ISO 62
Molding shrinkage, parallel(50% RH;23 °C;72 hr)		0.25 %	ISO 294-4, ISO 2577
Molding shrinkage, normal(50% RH;23 °C;72 hr)		0.75 %	ISO 294-4, ISO 2577

 

Mechanical	Nominal Value	Test Method
Dry: Tensile Modulus(1 mm/min)	9600 MPa	ISO 527-1/-2
Condition: Tensile Modulus(1 mm/min)	6200 MPa	ISO 527-1/-2
Dry: Stress at break	175 MPa	ISO 527-1/-2
Condition: Stress at break	110 MPa	ISO 527-1/-2
Dry: Strain at break	3.4 %	ISO 527-1/-2
Condition: Strain at break	6 %	ISO 527-1/-2
Dry: Flexural Modulus(2 mm/min)	8700 MPa	ISO 178
Condition: Flexural Modulus(2 mm/min)	5300 MPa	ISO 178
Flexural Modulus(2 mm/min)	8000 MPa	ASTM D790
Dry: Flexural Strength(2 mm/min)	280 MPa	ISO 178
Condition: Flexural Strength(2 mm/min)	150 MPa	ISO 178
Flexural Strength(2 mm/min)	235 MPa	ASTM D790
Dry: Charpy Impact Strength(23 °C)	80 kJ/m²	ISO 179/1eU
Condition: Charpy Impact Strength(23 °C)	100 kJ/m²	ISO 179/1eU
Dry: Charpy Notched Impact Strength(23 °C)	10 kJ/m²	ISO 179 1eA
Condition: Charpy Notched Impact Strength(23 °C)	18 kJ/m²	ISO 179 1eA
Dry: Izod Notched Impact Strength(23 °C)	9 kJ/m²	ISO 180/1A
Condition: Izod Notched Impact Strength(23 °C)	19 kJ/m²	ISO 180/1A
Thermal	Nominal Value	Test Method
Melting Temperature(10°C/min)	222 °C	ISO 11357-1
Temp. of deflection under load(1.8 MPa)	205 °C	ISO 75
Flammability 1.5 mm 3 mm	HB HB	UL 94
Glow Wire Flammability Index(1.5 mm)	650 °C	IEC 60695-2-12
Oxygen Index	23 %
Electrical	Nominal Value	Test Method
Volume Resistivity	1E+11 ohms·cm	IEC 62631-3-1
Surface Resistivity	1.0E+14 Ohms	IEC 62631-3-1

 

 

Mechanical	Nominal Value	Test Method
Dry: Tensile Modulus	9500 MPa	ISO 527-2
Condition: Tensile Modulus	6000 MPa	ISO 527-2
Dry: Tensile Stress, Break	185 MPa	ISO 527-2
Condition: Tensile Stress, Break	125 MPa	ISO 527-2
Dry: Tensile Strain, Break	5.0 %	ISO 527-2
Condition: Tensile Strain, Break	10 %	ISO 527-2
Dry: Charpy Notched Impact Strength -30 °C 23 °C	8.0 kJ/m² 11 kJ/m²	ISO 179 1eA
Condition: Charpy Notched Impact Strength -30 °C 23 °C	9.0 kJ/m² 20 kJ/m²	ISO 179 1eA
Dry: Charpy Unnotched Impact Strength -30 °C 23 °C	65 kJ/m² 75 kJ/m²	ISO 179 1eU
Condition: Charpy Unnotched Impact Strength -30 °C 23 °C	70 kJ/m² 90 kJ/m²	ISO 179 1eU
Thermal	Nominal Value	Test Method
Dry: Heat Deflection Temperature, Unannealed 1.8 MPa 8 MPa	205 °C 135 °C	ISO 75-2/A ISO 75-2/C
Dry: Continuous Use Temperature Long Term Short Term	90.0 - 110 °C 160 °C	ISO 2578 Internal Method
Dry: Melting Temperature(10 °C;min)	222 °C	ISO 11357-3
Dry: CLTE - Flow	2.0E-5 cm/cm/°C	ISO 11359-2
Dry: CLTE - Transverse	1.1E-4 cm/cm/°C	ISO 11359-2
Dry: Flammability Classification(0.8 mm)	HB	IEC 60695-11-10, - 20

                                                                                                                  Forever Co.,Ltd

With almost 20 years in the modified engineering plastics,Forever Plastics is a high-tech manufacture integrating R&D, production and sales of high-performance resin or polymer ,including PC,PP,PA6,PA66, PBT,PET, PC/ABS, PC/PBT, PC/PET alloy compounds,TPE,TPU, PE for rotomolding with the property of the flame retardant, glass fiber reinforced, high glossy, UV resistance.....with the annual output value of USD 65 million in 2021. 

Our customers are Osram,Cree,,Siemens,etc. for years in the electrical&electronics components, Automotive parts, House appliance,LED lights.....