Product Description | ||||
Tenac™ -C G455S is an Acetal (POM) Copolymer product filled with glass fiber. It is available in Africa & Middle East, Asia Pacific, Europe, or North America. Applications of Tenac™ -C G455S include engineering/industrial parts and housings. Characteristics include: Flame Rated Copolymer Creep Resistant Fatigue Resistant High Stiffness |
||||
General | ||||
Form | ||||
Filler | Glass Fiber | |||
Feature | Creep Resistance Excellent Fatigue Good Hardness Medium Viscosity |
|||
UL Yellow Card E48285-102392583 | ||||
Uses | Engineering Parts Gear Wheels Housing | |||
Physical | Nominal Value | Test Method | ||
Density / Specific Gravity | 1.58 g/cm³ | ASTM D792;ISO 1183 |
||
Melt Mass-Flow Rate, MFR(190 °C;2.16 kg) | 3.0 g/10min | ISO 1133 | ||
Molding Shrinkage, Flow | 0.40 - 0.60 % | Internal Method | ||
Molding Shrinkage, Across Flow | 1.0 - 1.2 % | Internal Method | ||
Water Absorption(50% RH;24 hr;23 °C) | 0.20 % | ASTM D570 | ||
Mechanical | Nominal Value | Test Method | ||
Tensile Modulus | 8400 MPa | ISO 527-2 | ||
Tensile Stress, Yield | 143 MPa | ISO 527-2 | ||
Tensile Elongation, Break | 2.0 % | ISO 527-2 | ||
Flexural Modulus | 8200 MPa | ISO 178 | ||
Charpy Notched Impact Strength | 10 kJ/m² | ISO 179 | ||
Thermal | Nominal Value | Test Method | ||
Heat Deflection Temperature, Unannealed(1.8 MPa) | 162 °C | ISO 75-2/A | ||
CLTE, Flow | 3.0E-5 cm/cm/°C | ISO 11359-2 | ||
CLTE, Transverse | 1.0E-4 cm/cm/°C | ISO 11359-2 | ||
Flame Rating(0.75 mm) | HB | UL 94 |
Product Description | ||||
A semi-conductive grade of acetal copolymer for applications requiring rapid dissipation of static build- up.Information provided by Celanese Corporation. | ||||
General | ||||
Form | Resin | Pellets | ||
Physical | Nominal Value | Test Method | ||
Density / Specific Gravity | 1.40 g/cm³ | |||
Water Absorption | 0.21 % | ASTM D570 | ||
Moisture Absorption at Equilibrium | 0.80 % | ASTM D570 | ||
Linear Mold Shrinkage | 2.2 % | |||
Linear Mold Shrinkage, Transverse | 1.8 % | |||
Hardness, Rockwell R | 111 | ASTM D785 | ||
Mechanical | Nominal Value | Test Method | ||
Tensile Strength, Yield | 37.0 MPa | ASTM D638 | ||
Elongation at Break | 30 % | ASTM D638 | ||
Flexural Strength | 52.0 MPa | ASTM D790 | ||
Flexural Modulus | 2100 MPa | ASTM D790 | ||
Compressive Strength | 66.0 MPa | ASTM D695 | ||
Shear Strength | 40.0 MPa | ASTM D732 | ||
Izod Impact, Notched Temperature; 23 °C Temperature; -29 °C |
50 J/m 30 J/m |
ASTM D256 | ||
Thermal | Nominal Value | Test Method | ||
Deflection Temperature Pressure; 0.46 MPa Pressure; 1.8 MPa |
152 °C 106 °C |
ASTM D648 | ||
Flammability, UL94 | HB | UL 94 |