Feature: | Photodegradable |
---|---|
Material: | Polyacetal/POM |
Usage: | General Plastics, Engineering Plastics, Specialty Plastics |
Samples: |
---|
Customization: |
---|
Shipping Cost:
Estimated freight per unit. |
about shipping cost and estimated delivery time. |
---|
Payment Method: | |
---|---|
Initial Payment Full Payment |
Currency: | US$ |
---|
Return&refunds: | You can apply for a refund up to 30 days after receipt of the products. |
---|
Suppliers with verified business licenses
General | ||||
Form | Resin Pellets | |||
Feature Excellent Processability | ||||
Automotive Housing |
Engineering Parts | Gear Wheels | ||
Physical | Nominal Value | Test Method | ||
Density / Specific Gravity | 1.41 g/cm³ | ASTM D792;ISO 1183 |
||
Melt Mass-Flow Rate, MFR(2.16 kg;190 ºC) | 30 g/10 min | ISO 1183 | ||
Molding Shrinkage, Flow | 1.6 - 2.0 % | Internal Method | ||
Water Absorption(50% RH;24 hr;23 °C) | 0.2 % | ASTM D570 | ||
Hardness, Rockwell, M-scale | 90 | ASTM D785 | ||
Hardness, Rockwell, R-scale | 117 | ASTM D785 | ||
Mechanical | Nominal Value | Test Method | ||
Tensile Modulus | 3000 MPa | ISO 527-1 | ||
Tensile Strength, Yield | 68 MPa | ISO 527-2 | ||
Tensile Strength | 68 MPa | ASTM D638 | ||
Tensile Elongation, Break | 30 % 30 % |
ASTM D638 ISO 527-2 |
||
Flexural Modulus | 2850 MPa 2800 MPa |
ASTM D790 ISO 178 |
||
Flexural Stress | 100 MPa | ASTM D790 | ||
Charpy Impact Strength, Notched | 5 kJ/m² | ISO 179 | ||
Notched Izod Impact | 59 J/m | ASTM D256 |
Thermal | Nominal Value | Test Method |
Deflection Temperature Under Load, Unannealed | ||
0.45 MPa | 163 °C | ASTM D648 |
1.8 MPa | 124 °C | ASTM D648 |
0.45 MPa | 161 °C | ISO 75-2/B |
1.8 MPa | 105 °C | ISO 75-2/A |
CTE, Flow | 1.0E-4 cm/cm/°C | ASTM D696;ISO 11359-2 |
Specific Heat | 1470 J/kg/ºC | |
Thermal Conductivity | 0.23 W/m/K | |
Flame Rating(0.75 mm) | HB | UL 94 |
Electrical | Nominal Value | Test Method |
Surface Resistivity | 1.0E+16 - 1.0E+17 ohms | ASTM D257 |
Volume Resistivity(23 ºC) | 1.0E+15 - 1.0E+16 ohms·cm | ASTM D257 |
Product Description | ||||
A semi-conductive grade of acetal copolymer for applications requiring rapid dissipation of static build- up.Information provided by Celanese Corporation. | ||||
General | ||||
Form | Resin | Pellets | ||
Physical | Nominal Value | Test Method | ||
Density / Specific Gravity | 1.40 g/cm³ | |||
Water Absorption | 0.21 % | ASTM D570 | ||
Moisture Absorption at Equilibrium | 0.80 % | ASTM D570 | ||
Linear Mold Shrinkage | 2.2 % | |||
Linear Mold Shrinkage, Transverse | 1.8 % | |||
Hardness, Rockwell R | 111 | ASTM D785 | ||
Mechanical | Nominal Value | Test Method | ||
Tensile Strength, Yield | 37.0 MPa | ASTM D638 | ||
Elongation at Break | 30 % | ASTM D638 | ||
Flexural Strength | 52.0 MPa | ASTM D790 | ||
Flexural Modulus | 2100 MPa | ASTM D790 | ||
Compressive Strength | 66.0 MPa | ASTM D695 | ||
Shear Strength | 40.0 MPa | ASTM D732 | ||
Izod Impact, Notched Temperature; 23 °C Temperature; -29 °C |
50 J/m 30 J/m |
ASTM D256 | ||
Thermal | Nominal Value | Test Method | ||
Deflection Temperature Pressure; 0.46 MPa Pressure; 1.8 MPa |
152 °C 106 °C |
ASTM D648 | ||
Flammability, UL94 | HB | UL 94 |