Product Description | |||||
LNP THERMOCOMP MX89510 compound is based on Polypropylene (PP) resin containing 10% glass fiber, 10% glass bead. | |||||
General | |||||
Form | Resin Pellets | ||||
Filler | 10 % Glass Bead | 10 % Glass Fiber | |||
Feature | Low Warpage | Good Hardness | Structural | ||
Uses | Consumer | Electrical | |||
Physical | Nominal Value | Test Method | |||
Density / Specific Gravity | 1.02 1.01 g/cm³ |
ASTM D792 | |||
Moisture Absorption | |||||
23 °C;50% RH/24 hrs | 0.02 % | ASTM D570 | |||
50% RH;23 °C | 0.02 % | ISO 62 | |||
Mold Shrinkage, Flow(24 hrs) | 0.8 - 2 % | ASTM D955 | |||
Mold Shrinkage, XFlow(24 hrs) | 0.9 - 3 % | ASTM D955 | |||
Mechanical | Nominal Value | Test Method | |||
Izod Impact, Unnotched | |||||
23 °C | 368 J/m | ASTM D4812 | |||
80*10*4;23 °C | 22 kJ/m² | ISO 180/1U | |||
Izod Impact, Notched | |||||
23 °C | 21 J/m | ASTM D256 | |||
80*10*4;23 °C | 2 kJ/m² | ISO 180/1A | |||
Multiaxial Impact | 1 J | ISO 6603 | |||
Instrumented Dart Impact, Total Energy(23 °C) | 4 J | ASTM D3763 | |||
Tensile Stress, Yield | |||||
5 mm/min;Type I | 52 MPa | ASTM D638 | |||
5 mm/min | 50 MPa | ISO 527 | |||
Tensile Stress, Break | |||||
5 mm/min;Type I | 52 MPa | ASTM D638 | |||
5 mm/min | 48 MPa | ISO 527 | |||
Tensile Strain, Yield | |||||
5 mm/min;Type I | 3 % | ASTM D638 | |||
5 mm/min | 2.9 % | ISO 527 | |||
Tensile Strain, Break | |||||
5 mm/min;Type I | 3.4 % | ASTM D638 | |||
5 mm/min | 3.4 % | ISO 527 | |||
Tensile Modulus | |||||
50 mm/min | 3820 MPa | ASTM D638 | |||
1 mm/min | 3540 MPa | ISO 527 | |||
Flexural Stress, Yield(1.3 mm/min;50 mm;span) | 80 MPa | ASTM D790 | |||
Flexural Modulus | |||||
1.3 mm/min;50 mm;span | 2800 MPa | ASTM D790 | |||
2 mm/min | 2950 MPa | ISO 178 | |||
Flexural Stress | 76 MPa | ISO 178 | |||
Thermal | Nominal Value | Test Method | |||
Heat Deflection Temperature[HDT], Unannealed 0.45 MPa;3.2 mm 3.2 mm;1.82 MPa |
156 °C 131 °C |
ASTM D648 | |||
CTE, Flow(-30 - 30 °C) | 4.3E-05 1/°C | ASTM D696 | |||
CTE, XFlow(-30 - 30 °C) | 1.2E-04 1/°C | ASTM D696 | |||
HDT/Bf(0.45) | 153 °C | ISO 75/Bf | |||
HDT/Af(1.8) | 119 °C | ISO 75/Af | |||
Processing | Nominal Value | ||||
Drying Temperature<Injection> | 80 °C | ||||
Drying Time<Injection> | 4 hrs | ||||
Melt Temperature<Injection> | 225 - 250 °C | ||||
Front, Zone 3 Temperature<Injection> | 240 - 250 °C | ||||
Middle, Zone 2 Temperature<Injection> | 215 - 225 °C | ||||
Rear, Zone 1 Temperature<Injection> | 195 - 205 °C | ||||
Mold Temperature<Injection> | 30 - 50 °C | ||||
Back Pressure<Injection> | 0.2 - 0.3 MPa | ||||
Screw Speed <Injection> | 30 - 60 rpm |