30% Glass Reinforced Flame Retardant Non-Halogenated PPA High Performance Polyamide

• Feature: Oxidative Degradable
• CAS No.: 32131-17-2
• Formula: (C12h22n2o2)N
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Model NO.: PPA-FR52G30NH BK337
• EINECS: 211-024-8
• Material: Polyamide(Nylon 6.66)/PA
• Usage: General Plastics, Engineering Plastics, Specialty Plastics
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Injection
• Color: Black
• Form: Resin Pellets
• Chemical Substances: Nylon
• Processing Mode: Injection Molding/Extrusion
• UV: Fr
• Use: Electrical Appliances, Auto Parts, Office Supplies
• Certificates: ISO9001:2008.SGS.RoHS
• Filler: 10%-60% Glass Fiber
• Transport Package: Bag
• Specification: 25KG
• Trademark: Forever
• Origin: China
• HS Code: 390740000
• Production Capacity: 50000t/Year
• Package Size: 75.00cm * 55.00cm * 15.00cm
• Package Gross Weight: 25.010kg

Product Description

30% Glass Reinforced Flame Retardant Non-Halogenated PPA High Performance Polyamide
 Heat-conducting nylon

Product Description

Product Description
30% Glass Reinforced, Flame Retardant, Non-Halogenated, PPA, High Performance Polyamide
General
Form	Resin Pellets
Filler	30 % Glass Fiber
Feature	Non-Brominated & Non-   Chemical Resistant Chlorinated Flame   Retardant			Red Phosphorous Free
UL Yellow Card                         E41938-521871
Physical		Nominal Value		Test Method
Density / Specific Gravity		1.44 g/cm³		ISO 1183
Molding Shrinkage, Across Flow		1.1 %		ISO 294-4
Molding Shrinkage, Flow		0.30 %		ISO 294-4
Odor		3.50		VDA 270
Emission of organic compounds		10.0 µgC/g		VDA 277
Mechanical		Nominal Value		Test Method
Tensile Modulus		10000 MPa		ISO 527-2
Tensile Stress, Break		150 MPa		ISO 527-2
Tensile Strain, Break		2.2 %		ISO 527-2
Flexural Modulus		8700 MPa		ISO 178
Flexural Stress		230 MPa		ISO 178
Poisson's Ratio		0.34		No Standard
C harpy Notched Impact Strength(23 °C)		8.0 kJ/m²		ISO 179 1eA
Thermal		Nominal Value		Test Method
Heat Deflection Temperature, Unannealed(1.8 MPa)		283 °C		ISO 75-2/A
Melting temperature, first heat		310 °C		ISO 11357-3
RTI Elec 0.4 mm 0.75 mm 1.5 mm 3 mm		140 °C 140 °C 140 °C 140 °C		UL 746
Flame Rating 0.4 mm 1.5 mm		V-0 V-0		IEC 60695-11- 10;UL 94; IEC60695-11-20
Glow Wire Ignition Temperature [GWIT] 0.4 mm 0.75 mm 3 mm		700 °C 725 °C 775 °C		IEC 60695-2-13
Oxygen Index		37 %		ISO 4589-2
FMVSS Flammability		DNI		FMVSS 302
Electrical		Nominal Value		Test Method
Volume Resistivity		> 1E+11 ohms ·cm		IEC 62631-3-1
Electric Strength		33 kV/mm		IEC 60243-1
Relative Permittivity 1.0e+6 Hz 100 Hz		4.00 4.30		IEC 62631-2-1
Dissipation Factor 100 Hz 1.0e+6 Hz		7.0E-3 0.013		IEC 62631-2-1
Comparative Tracking Index		600 V		IEC 60112
Processing			Nominal Value
Drying Temperature<Injection>			100 °C
Drying Time - Desiccant Dryer<Injection>			6.0 - 8.0 hr
Suggested Max Moisture<Injection>			0.10 %
Processing Temp, Melt<Injection>			320 - 325 °C
Mold Temperature<Injection>			90 - 130 °C
Drying Recommended <Injection>			YES

 

                                                                                                                  Forever Co.,Ltd

 

With almost 20 years in the modified engineering plastics,Forever Plastics is a high-tech manufacture integrating R&D, production and sales of high-performance resin or polymer ,including PC,PP,PA6,PA66, PBT,PET, PC/ABS, PC/PBT, PC/PET alloy compounds,TPE,TPU, PE for rotomolding with the property of the flame retardant, glass fiber reinforced, high glossy, UV resistance.....with the annual output value of USD 65 million in 2021. 

Our customers are Osram,Cree,,Siemens,etc. for years in the electrical&electronics components, Automotive parts, House appliance,LED lights.....