| XD2322 polycarbonate (PC) copolymer resin is a UV stabilized opaque grade. This resin offers UL94 [email protected] flame retardancy based on non-bromine, non-chlorine FR system, excellent low temperature ductility characteristics and processability. XD2322 resin is an excellent candidate for a wide range of applications such as electronic vehicles (EV) and 5G devices. |
||||
| General | ||||
| Form | Resin Pellets | |||
Feature |
High Impact Non-Chlorinated |
Outdoor | Non-Brominated & Non- Chlorinated Flame Retardant |
|
| Uses | Consumer Energy Storage |
Healthcare Electrical | ||
| Physical | Nominal Value | Test Method | ||
| Density / Specific Gravity | 1.19 1.19 g/cm³ |
ASTM D792 ISO 1183 |
||
| Mold Shrinkage, Flow(3.2 mm) | 0.4 - 0.8 % | Method | ||
| Mold Shrinkage, XFlow(3.2 mm) | 0.4 - 0.8 % | Method | ||
| Melt Flow Rate[MFR](300 °C;1.2 kgf) | 16 g/10min | ASTM D1238 | ||
| Water Absorption(23 °C;saturated) | 0.4 % | ISO 62-1 | ||
| Moisture Absorption(23 °C;50% RH/Equilibrium) | 0.15 % | ISO 62-4 | ||
| Melt Volume Rate, MVR(1.2 kg;MVR at 300 °C) | 15 cm³/10 min | ISO 1133 | ||
| UV light, water exposure/immersion | f1 | UL 746C | ||
| Mechanical | Nominal Value | Test Method | ||
| Izod Impact, Notched | ASTM D256 | |||
| 23 °C | 780 J/m | |||
| -30 °C | 652 J/m | |||
| -40 °C | 360 J/m | |||
| Instrumented Dart Impact, Total Energy(23 °C) | 66 J | ASTM D3763 | ||
| Unnotched Izod Impact Strength | ISO 180/1U | |||
| unnotched;80*10*3;23 °C 0 | NB kJ/m² | |||
| unnotched;80*10*3;-30 °C 0 | NB kJ/m² | |||
| Notched Izod Impact Strength notched;80*10*3;23 °C 0 notched;80*10*3;-30 °C 0 |
63 kJ/m² 29 kJ/m² |
ISO 180/1A | ||
| Tensile Stress, Yield | ||||
| 50 mm/min;Type I | 58 MPa | ASTM D638 | ||
| 50 mm/min | 56 MPa | ISO 527 | ||
| Tensile Stress, Break | ||||
| 50 mm/min;Type I | 59 MPa | ASTM D638 | ||
| 50 mm/min | 57 MPa | ISO 527 | ||
| Tensile Strain, Yield | ||||
| 50 mm/min;Type I | 6 % | ASTM D638 | ||
| 50 mm/min | 6 % | ISO 527 | ||
| Tensile Strain, Break | ||||
| 50 mm/min;Type I | 112 % | ASTM D638 | ||
| 50 mm/min | 108 % | ISO 527 | ||
| Tensile Modulus | ||||
| 5 mm/min | 2100 MPa | ASTM D638 | ||
| 1 mm/min | 2000 MPa | ISO 527 | ||
| Flexural Strength | ||||
| 1.3 mm/min;50 mm;span | 92 MPa | ASTM D790 | ||
| 2 mm/min | 87 MPa | ISO 178 | ||
| Flexural Modulus | ||||
| 1.3 mm/min;50 mm;span | 2400 MPa | ASTM D790 | ||
| 2 mm/min | 2100 MPa | ISO 178 | ||
| Thermal | Nominal Value | Test Method | ||
| Glow Wire Flammability Index(1.5 mm) | 960 °C | IEC 60695-2-12 | ||
| Glow Wire Ignition Temperature [GWIT](1.5 mm) | 825 °C | IEC 60695-2-13 | ||
| UL Recognized ≥ 3 mm ≥ 1.5 mm |
5VA V-0 |
UL 94 | ||
| Relative Temp Index, Elec | 125 °C | UL 746B | ||
| Relative Temp Index, Mechanical with Impact | 115 °C | UL 746B | ||
| Relative Temp Index, Mechanical without Impact | 125 °C | UL 746B | ||
| Vicat Softening Temperature(Rate B/50) | 140 °C | ASTM D1525 | ||
| Heat Deflection Temperature[HDT], Unannealed(3.2 mm;1.82 MPa) | 123 °C | ASTM D648 | ||
| HDT/Af(1.8) | 118 °C | ISO 75/Af | ||
| CTE, Flow(-40 - 40 °C) | 6.1e-05 1/°C | ASTM E831 | ||
| CTE, XFlow(-40 - 40 °C) | 6.2e-05 1/°C | ASTM E831 | ||
| Electrical | Nominal Value | Test Method | ||
| Comparative tracking index M | 150 V | IEC 60112 | ||
| Comparative Tracking Index, CTI | PLC 3 | UL 746A | ||
| High Amp Arc Ignition, HAI 3 mm 1.5 mm |
PLC 0 PLC 1 |
UL 746A | ||
| Hot-wire Ignition, HWI 3 mm 1.5 mm |
PLC 2 PLC 3 |
UL 746A | ||
| Processing | Nominal Value | |||
| Drying Temperature<Injection> | 120 °C | |||
| Drying Time<Injection> | 3 - 4 hrs | |||
| Drying Time, Cumulative<Injection> | 48 hrs | |||
| Maximum Moisture Content<Injection> | 0.02 % | |||
| Melt Temperature<Injection> | 295 - 315 °C | |||
| Nozzle Temperature<Injection> | 290 - 310 °C | |||
| Front, Zone 3 Temperature<Injection> | 295 - 315 °C | |||
| Middle, Zone 2 Temperature<Injection> | 280 - 305 °C | |||
| Rear, Zone 1 Temperature<Injection> | 270 - 295 °C | |||
| Mold Temperature<Injection> | 70 - 95 °C | |||
| Back Pressure<Injection> | 0.3 - 0.7 MPa | |||
| Screw Speed <Injection> | 40 - 70 rpm | |||
| Shot To Cylinder Size<Injection> | 40 - 60 % | |||
| Vent Depth <Injection> | 0.025 - 0.076 mm | |||