PA6 UL94 V-0 Classified, Free of Halogens-Based Flame Retardants and Red Phosphorous

• Feature: Oxidative Degradable
• CAS No.: 32131-17-2
• Formula: (C12h22n2o2)N
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Model NO.: PA-CEG_500-V0HF1
• EINECS: 211-024-8
• Material: Polyamide(Nylon 6.66)/PA
• Usage: General Plastics, Engineering Plastics, Specialty Plastics
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Injection
• Color: Black
• Form: Resin Pellets
• Chemical Substances: Nylon
• Processing Mode: Injection Molding/Extrusion
• UV: Fr
• Use: Electrical Appliances, Auto Parts, Office Supplies
• Certificates: ISO9001:2008.SGS.RoHS
• Filler: 30% Glass Fiber
• Transport Package: Bag
• Specification: 25KG
• Trademark: Forever
• Origin: China
• HS Code: 390740000
• Production Capacity: 50000t/Year
• Package Size: 75.00cm * 55.00cm * 15.00cm
• Package Gross Weight: 25.010kg

Product Description

PA6 UL94 V-0 classified free of halogens-based flame retardants and red phosphorous

Product Description

Product Description
High thermal conductivity product based on Polyamide 6 (PA6). Glass fibres / Mineral filler. UL94 V-0 classified, free of halogens-based flame retardants and red phosphorous.
General
Form	Resin Pellets
Filler	Glass Fiber/Mineral
Feature	Thermally Conductive			Red Phosphorous Free		Non-Brominated & Non- Chlorinated Flame
Physical				Nominal Value		Test Method
Density / Specific Gravity				1.75 g/cm³
Molding Shrinkage, Across	Flow(2 mm;60 MPa)			0.50 - 0.65 %
Molding Shrinkage, Flow(2	mm;60 MPa)			0.30 - 0.45 %
Mechanical		Nominal Value			Test Method
Tensile Modulus 23 °C 60 °C 90 °C 120 °C 150 °C		10500 MPa 6500 MPa 4700 MPa 3500 MPa 2800 MPa			ISO 527-1/2
Tensile Stress, Break 23 °C 60 °C 90 °C 120 °C 150 °C		85.0 MPa 65.0 MPa 55.0 MPa 45.0 MPa 35.0 MPa			ISO 527-2/5
Elongation at Break 23 °C 60 °C 90 °C 120 °C 150 °C		1.5 % 1.8 % 2.0 % 2.5 % 2.5 %			ISO 527-2/5
C harpy Notched Impact Strength -20 °C 23 °C		3.5 kJ/m² 3.5 kJ/m²			ISO 179 1eA
C harpy Unnotched Impact Strength -20 °C 23 °C		15 kJ/m² 15 kJ/m²			ISO 179 1eU
Thermal			Nominal Value				Test Method
Heat Deflection Temperature
0.45 MPa			215 °C
1.8 MPa			200 °C
Continuous Use Temperature(2.0e+4 hr)			135 °C
Vicat Softening Temperature			210 °C				ISO 306/B50
CTE, Flow(30 - 100 °C)			1.5E-5 cm/cm/°C
Thermal Conductivity, Through Plane(Longitudinal)			1.1 W/m-K				Internal Method
Flame Rating
0.75 mm			V-1
1.5 mm			V-0
3 mm			V-0
Glow Wire Flammability Index
1 mm			960 °C
2 mm			960 °C
Glow Wire Test(1 mm)			775 °C
Oxygen Index			42 %				ASTM D2863
Electrical			Nominal Value				Test Method
Surface Resistivity			1.0E+10 ohms				ASTM D257
Processing							Nominal Value
Melt Temperature							250 - 270 °C
Mold Temperature							80.0 - 100 °C
Drying Temperature							90.0 - 100 °C
Dry Time							3 hr

                                                                                                                  Forever Co.,Ltd

 

With almost 20 years in the modified engineering plastics,Forever Plastics is a high-tech manufacture integrating R&D, production and sales of high-performance resin or polymer ,including PC,PP,PA6,PA66, PBT,PET, PC/ABS, PC/PBT, PC/PET alloy compounds,TPE,TPU, PE for rotomolding with the property of the flame retardant, glass fiber reinforced, high glossy, UV resistance.....with the annual output value of USD 65 million in 2021. 