Product Description | ||||
30% Glass Reinforced, Chemically Coupled, Copolymer Polypropylene | ||||
General | ||||
Form | ||||
Filler | ||||
Feature | Chemically Coupled | |||
UL Yellow Card E138590-101454806 | ||||
Physical | Nominal Value | Test Method | ||
Density / Specific Gravity | 1.13 g/cm³ | ASTM D792 | ||
Melt Mass-Flow Rate, MFR(230 °C;2.16 kg) | 8.0 g/10min | ASTM D1238 | ||
Molding Shrinkage, Flow | 0.20 - 0.50 % | No Standard | ||
Molding Shrinkage, Across Flow | 0.50 - 1.0 % | No Standard | ||
Mechanical | Nominal Value | Test Method | ||
Tensile Strength, Yield(23 °C) | 68.0 MPa | ASTM D638 | ||
Tensile Elongation, Break | 4.0 % | ASTM D638 | ||
Flexural Modulus | 5340 MPa | ASTM D790 | ||
Flexural Strength, Break | 124 MPa | ASTM D790 | ||
Notched Izod Impact(23 °C;3.18 mm) | 130 J/m | ASTM D256 | ||
Thermal | Nominal Value | Test Method | ||
Deflection Temperature Under Load, Unannealed 0.45 MPa 1.8 MPa |
146 °C 135 °C |
ASTM D648 | ||
Flame Rating 1.5 mm 3 mm |
HB HB |
UL 94 | ||
Processing | Nominal Value | |||
Rear Temperature<Injection> | 204 - 249 °C | |||
Middle Temperature<injection> | 216 - 260 °C | |||
Front Temperature<Injection> | 216 - 260 °C | |||
Nozzle Temperature<Injection> | 216 - 260 °C | |||
Processing Temp, Melt<Injection> | 216 - 260 °C | |||
Mold Temperature<Injection> | 27 - 60 °C | |||
Back Pressure<Injection> | 0.345 - 0.689 MPa |