Feature: | Plastics |
---|---|
CAS No.: | 25766-59-0 |
Formula: | C6h4c(CH3)2c6h4oco2-]N |
Samples: |
BAG
|
---|
Customization: |
---|
Shipping Cost:
Estimated freight per unit. |
about shipping cost and estimated delivery time. |
---|
Payment Method: | |
---|---|
Initial Payment Full Payment |
Currency: | US$ |
---|
Return&refunds: | You can apply for a refund up to 30 days after receipt of the products. |
---|
Suppliers with verified business licenses
Polycarbonate/Acrylonitrile Butadiene Styrene PC/ABS electric vehicle battery energy storage equipment
https://forever-plastics.en.made-in-china.com/product-list-1.html
Product Description | ||||
CX7240B Polycarbonate/Acrylonitrile Butadiene Styrene (PC/ABS) blend is an injection moldable, medium flow, non chlorinated/brominated flame retardant grade with incorporation of renewable PC feedstock. It has a UL94 [email protected], [email protected] and [email protected] flame rating and contains around 48.3% renewable content. Renewable content certified by ISCC+ mass balance methodology. This grade has improved weld line strength and chemical resistance compared to standard PC/ABS blends and is a good candidate for thin wall applications. This grade also has good processability with opportunities for shorter injection molded cycle times compared to standard PC/ABS. ELCRIN CX7240B is a product available in wide range of opaque colors and is targeted for a variety of electronics applications such as mobile phones, tablets, audio equipment, gaming devices, thin wall industrial housings, and electric vehicle battery and energy storage equipment. |
||||
General | ||||
Form Resin Pellets | ||||
Feature |
||||
Chemical Resistant | Good Dimensional | High Impact | ||
Bio-Polymer | Good Colorability | Amorphous | ||
UL Yellow Card | E207780-474277 | |||
Appliances Batteries Building Materials | ||||
Uses |
Sporting Goods Aerospace | Thin-walled Parts Cell Phone Cases | 3d Printing Constraction |
|
Housing Rail Medical | ||||
Personal Care Energy Storage | ||||
Physical Nominal Value Test Method | ||||
Density / Specific Gravity 1.19 g/cm³ ASTM D792 1.20 g/cm³ ISO 1183 |
||||
Melt Mass-Flow Rate, MFR(260 °C;2.16 kg) 18 g/10 min ASTM D1238 | ||||
Melt Volume-Flow Rate, MVR(260 °C;2.16 kg) 15 cm³/10 min ISO 1133 | ||||
Molding Shrinkage, Flow(3.2 mm) 0.40 - 0.60 % Internal Method | ||||
Water Absorption, Saturation(23 °C) 0.20 % ISO 62 | ||||
Water Absorption, Equilibrium(50% RH;23 °C) 0.10 % ISO 62 | ||||
Outdoor Suitability f2 UL 746C | ||||
Mechanical Nominal Value Test Method |
Tensile Strength, Yield | ||
50 mm/min;Type I | 65.0 MPa 65.0 MPa |
ASTM D638 ISO 527-2/50 |
Tensile Strength, Break | ||
50 mm/min;Type I | 58.0 MPa 50.0 MPa |
ASTM D638 ISO 527-2/50 |
Tensile Elongation, Yield | ||
50 mm/min;Type I | 4.1 % 4.0 % |
ASTM D638 ISO 527-2/50 |
Tensile Elongation, Break | ||
50 mm/min;Type I | 100 % 90 % |
ASTM D638 ISO 527-2/50 |
Flexural Modulus | ||
1.3 mm/min;50 mm Span | 2500 MPa | ASTM D790 |
2 mm/min | 2500 MPa | ISO 178 |
Flexural Strength | ||
1.3 mm/min;50 mm Span | 104 MPa | ASTM D790 |
2 mm/min | 96.0 MPa | ISO 178 |
C harpy Notched Impact Strength -30 °C;80*10*3 sp =62mm 23 °C;80*10*3 sp =62mm 23 °C;80*10*4 sp =62mm |
10 kJ/m² 20 kJ/m² 22 kJ/m² |
ISO 179/1eA |
Notched Izod Impact | ||
-30 °C | 180 J/m | ASTM D256 |
23 °C | 700 J/m | ASTM D256 |
-30 °C;80*10*3 mm | 10 kJ/m² | ISO 180/1A |
80*10*4 mm;-30 °C | 10 kJ/m² | ISO 180/1A |
23 °C;80*10*3 mm | 20 kJ/m² | ISO 180/1A |
80*10*4 mm;23 °C | 25 kJ/m² | ISO 180/1A |
Instrumented Dart Impact, Total Energy(23 °C) | 65.0 J | ASTM D3763 |
Thermal | Nominal Value | Test Method |
Vicat Softening Temperature 50 °C/h;50 N;Rate A;Loading 2 |
110 °C 113 °C |
ISO 306/B50;ASTM D1525 ISO 306/B120 |
Ball Pressure Test(73 - 77 °C) | Pass | IEC 60695-10-2 |
CLTE, Flow(-40 - 40 °C) | 7.5E-5 cm/cm/°C | ASTM E831;ISO 11359-2 |
CLTE, Transverse(-40 - 40 °C) | 7.5E-5 cm/cm/°C | ASTM E831;ISO 11359-2 |
Thermal Conductivity | 0.20 W/m/K | ISO 8302 |
RTI Elec | 90.0 °C | UL 746B |
RTI Imp | 90.0 °C | UL 746B |
RTI Str | 90.0 °C | UL 746B |
Flame Rating > 0.4 mm > 0.6 mm > 0.75 mm > 1.5 mm > 3 mm |
V-2 V-1 V-0 5VB 5VA |
UL 94 |
Glow Wire Flammability Index 0.75 mm 1.5 mm 2 mm 3 mm |
960 °C 960 °C 960 °C 960 °C |
IEC 60695-2-12 |
Glow Wire Flammability Index, by VDE(0.75 mm) | 960 °C | IEC 60695-2-12 |
Glow Wire Ignition Temperature [GWIT] 0.75 mm 1.5 mm 2 mm 3 mm |
800 °C 800 °C 800 °C 800 °C |
IEC 60695-2-13 |
Glow Wire Ignition Temperature, by VDE 0.75 mm 1.5 mm 3 mm |
775 °C 775 °C 775 °C |
IEC 60695-2-13 |
Oxygen Index | 34 % | ISO 4589-2 |
Electrical | Nominal Value | Test Method |
Surface Resistivity | > 1.0E+15 Ohms | IEC 60093 |
Volume Resistivity | > 1.0E+15 Ohms ·cm | IEC 60093 |
Electric Strength, in Oil 0.8 mm 1.6 mm 3.2 mm |
35 kV/mm 25 kV/mm 17 kV/mm |
IEC 60243-1 |
Comparative Tracking Index, CTI | PLC 3 | UL 746A |
High Amp Arc Ignition, HAI( > 0.75 mm) | PLC 0 | UL 746A |
Hot-wire Ignition, HWI > 0.75 mm > 3 mm |
PLC 3 PLC 1 |
UL 746A |
Processing | Nominal Value | |
Drying Temperature<Injection> | 80 - 90 °C | |
Drying Time<Injection> | 2.0 - 4.0 hr | |
Suggested Max Moisture<Injection> | 0.020 % | |
Hopper Temperature<Injection> | 60 - 80 °C | |
Rear Temperature<Injection> | 230 - 280 °C | |
Middle Temperature<injection> | 240 - 290 °C | |
Front Temperature<Injection> | 250 - 300 °C | |
Nozzle Temperature<Injection> | 250 - 300 °C | |
Processing Temp, Melt<Injection> | 250 - 300 °C | |
Mold Temperature<Injection> | 60 - 85 °C | |
Vent Depth <Injection> | 0.030 - 0.075 mm |