| Feature: | Photodegradable |
|---|---|
| CAS No.: | 9002-81-7 |
| Formula: | Na |
| Samples: |
customize according to your exact requirements
|
|---|
| Customization: |
|---|
|
Shipping Cost:
Estimated freight per unit. |
about shipping cost and estimated delivery time. |
|---|
| Payment Method: |
|
|---|---|
| Initial Payment Full Payment |
| Currency: | US$ |
|---|
| Return&refunds: | You can apply for a refund up to 30 days after receipt of the products. |
|---|
Suppliers with verified business licenses
Audited Supplier EMERGE PC 8230-14-XH Advanced Resin, a highly durable and reliable material that's perfect for countless applications. This advanced resin is ignition-resistant, just like EMERGE PC 8130-13-XH, and does not contain chlorinated, brominated, or phosphate flame retardant additives. It is also UV stabilized, which makes it ideal for outdoor applications. The resin contains a mold release agent, making it easy to work with, and has a UL f1 rating. Thanks to its unique properties, it provides a perfect balance of flow ability, high rigidity, dimensional stability, and chemical solvent resistance. This makes it an excellent choice for applications where painting or coating is not necessary. EMERGE PC 8230-14-XH Advanced Resin is suitable for a wide range of applications, including enclosures, electrical applications, and electronic accessories.
| General | |||
| Form | Resin Pellets | ||
| High Mechanical Strength Non-Brominated Non-Chlorinated | |||
| Feature | And Rigidity | Chemical Resistant Good Dimensional | |
| Excellent Processability Outdoor Combustion Resistant | |||
| Uses Electronic Accessories Electrical applications | |||
| Physical | Nominal Value | Test Method | |
| Density / Specific Gravity | 1.20 g/cm³ | ASTM D792 | |
| Melt Flow(300 °C;1.2 kg) | 13 g/10min | ASTM D1238 | |
| Molding Shrinkage, Flow | 0.50 - 0.70 % | ASTM D955;ISO 294-4 |
|
| Mechanical | Nominal Value | Test Method | |
| Tensile Modulus 1 mm/min 1 mm/min |
2300 MPa 2600 MPa |
ASTM D638 ISO 527-1/1 |
|
| Tensile Strength, Yield(50 mm/min) | 60.0 MPa | ASTM D638 | |
| Tensile Strength, Break(50 mm/min) | 65.0 MPa | ASTM D638 | |
| Elongation at Yield(50 mm/min) | 6.0 % | ASTM D638 | |
| Elongation at Break(50 mm/min) | 120 % | ASTM D638 | |
| Flexural Modulus(1.3 mm/min) | 2400 MPa | ASTM D790 | |
| Flexural Strength(1.3 mm/min) | 95.0 MPa | ASTM D790 | |
| Izod Impact, Notched(23 °C) | 650 J/m | ASTM D256 | |
| Thermal | Nominal Value | Test Method |
| Deflection Temperature Under Load, Unannealed(1.8 MPa) | 125 °C | ASTM D648 |
| CLTE, Flow(-40 - 80°C) | 6.5E-5 cm/cm/°C | ASTM D696 |
| Flame Rating 0.8 mm 1 mm 2 mm 2 mm 3 mm 3 mm |
V-1 V-0 V-0 5VB V-0 5VA |
UL 94 |
| Glow Wire Flammability Index(2 mm) | 960 °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature [GWIT](2 mm) | 850 °C | IEC 60695-2-13 |
| Oxygen Index | 37 % | ASTM D2863 |
| Electrical | Nominal Value | Test Method |
| Surface Resistivity | > 1.0E+15 Ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 Ohms·cm | IEC 60093 3 |
| Electric Strength | 17 kV/mm | IEC 60243-1 |
| Dielectric Constant 1 Hz 50 Hz |
2.70 2.70 |
IEC 60250 |
| Dissipation Factor 50 Hz 1.0e+6 Hz |
1.0E-3 2.0E-3 |
IEC 60250 |
| Arc Resistance | PLC7 | ASTM D495 |
| Comparative Tracking Index, CTI, Solution A(2 mm) | 225 V | IEC 60112 |
| Processing | Nominal Value | |
| Drying Temperature | 120 °C | |
| Drying Time | 3.0 - 4.0 hr | |
| Melt Temperature | 270 - 300 °C | |
| Mold Temperature | 70 - 110 °C |