Product Description |
Flame-retardant polyamide 66, 33% glass-fiber reinforced for injection moulding. |
General |
Form Resin Pellets |
Filler 33 % Glass Fiber |
Chemical Resistant Good Surface Appearance Good Dimensional |
Feature Good Thermal Abrasion Resistant Good Electrical Properties |
Outdoor |
Physical Nominal Value Test Method |
Density, dry 1.58 g/cm³ ISO 1183 |
Dry: Water Absorption, Equilibrium(50% RH;23 °C) 1.3 % ISO 62 |
Mechanical Nominal Value Test Method |
Dry: Tensile Modulus 12000 MPa ISO 527-1 |
Condition: Tensile Modulus 10000 MPa ISO 527-1 |
Dry: Tensile Stress 170 MPa ISO 527-2 |
Condition: Tensile Stress 150 MPa ISO 527-2 |
Dry: Tensile Strain, Break 2.6 % ISO 527-2 |
Dry: Flexural Modulus 8900 MPa ISO 178 |
Condition: Flexural Modulus 7500 MPa ISO 178 |
Dry: Flexural Stress 230 MPa ISO 178 |
Condition: Flexural Stress 200 MPa ISO 178 |
Dry: Charpy Notched Impact Strength(23 °C) 11 kJ/m² ISO 179 |
Condition: Charpy Notched Impact Strength(23 °C) 13 kJ/m² ISO 179 |
Thermal Nominal Value Test Method |
Dry: Deflection Temperature Under Load, Unannealed |
0.45 MPa 250 °C ISO 75-2/B |
1.8 MPa 240 °C ISO 75-2/A |
Dry: Melting Temperature, DSC 263 °C ISO 3146 |
Dry: Flame Rating(0.8 mm) V-0 UL 94 |
Electrical |
Nominal Value |
Test Method |
Dry: Surface Resistivity |
1.0E+11 ohms |
IEC 60093 |
Condition: Surface resistivity |
1.0E+11 ohms |
IEC 60093 |
Dry: Volume Resistivity |
1.0e+15 ohms ·cm |
IEC 60093 |
Condition: Volume resistivity |
1.0E+13 ohms ·cm |
IEC 60093 |
Dry: Electric Strength(2 mm) |
21 kV/mm |
IEC 60243-1 |
Condition: Electric Strength(2 mm) |
21 kV/mm |
IEC 60243-1 |
Processing |
|
Nominal Value |
Drying Temperature<Injection> |
|
80 °C |
Drying Time<Injection> |
|
4.0 hr |
Suggested Max Moisture<Injection> |
|
0.20 % |
Rear Temperature<Injection> |
|
270 - 275 °C |
Middle Temperature<injection> |
|
280 - 285 °C |
Front Temperature<Injection> |
|
285 - 290 °C |
Mold Temperature<Injection> |
|
70 - 100 °C |
Injection Pressure<Injection> |
|
35.0 - 125 MPa |
Injection Rate<Injection> |
|
Moderate - Fast |
Back Pressure<Injection> |
|
0.138 - 0.345 MPa |
Screw Speed <Injection> |
|
80 - 200 rpm |