Product Description | ||||
LNP THERMOCOMP DC004XXAR1 compound is based on Polycarbonate (PC) resin containing 20% carbon fiber for Large Format Additive Manufacturing (LFAM) applications. Added features of this grade include: Higher Stiffness vs. glass fiber, Higher Strength, Higher Temperature Performance and Higher Throughput compared to ABS and PPE, as well as Excellent Ductility and Smooth Surface Finish. |
||||
General | ||||
Form | Resin Pellets | |||
Filler | 20 % Carbon Fiber | |||
Feature | Good Thermal High Impact | Good Hardness | ||
Uses | Industria | |||
Physical | Nominal Value | Test Method | ||
Density / Specific Gravity | 1.27 | ASTM D792 | ||
Mechanical | Nominal Value | Test Method | ||
Tensile Stress | ASTM D638 Modified | |||
XZ Orientation;5mm/min | 124 MPa | |||
ZX Orientation;5mm/min | 48 MPa |
Flexural Stress XZ Orientation;5mm/min ZX Orientation;5mm/min |
66 MPa 164 MPa |
ASTM D790 Modified |
|
Tensile Strain XZ Orientation;5mm/min ZX Orientation;5mm/min |
1.6 % 2 % |
ASTM D638 Modified |
|
Thermal | Nominal Value | Test Method | |
Heat Deflection Temperature[HDT], Annealed(3.2 mm;1.82 MPa) | 144 °C | ASTM D648 | |
Processing | Nominal Value | ||
Extruder L/D<Extrusion> | 24 | ||
Drying Temperature<Extrusion> | 120 °C | ||
Drying Time<Extrusion> | 4 hrs | ||
Maximum Moisture Content<Extrusion> | 0.02 % | ||
Barrel - Zone 1 Temperature<Extrusion> | 250 - 280 °C | ||
Barrel - Zone 2 Temperature<Extrusion> | 260 - 290 °C | ||
Barrel - Zone 3 Temperature<Extrusion> | 260 - 290 °C | ||
Barrel - Zone 4 Temperature<Extrusion> | 260 - 290 °C | ||
Nozzle Temperature<Extrusion> | 260 - 290 °C | ||
Melt Temperature<Extrusion> | 260 - 290 °C | ||
Bed Temperature<Extrusion> | 100 - 120 °C | ||
Extruder Pressure<Extrusion> | < 11 MPa |