Injection Molding Grade Engineer Plastic PBT Resin GF30 Plastic Raw Materials

• Feature: Plastics
• CAS No.: 63440-93-7
• Formula: C24h24o8
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Model NO.: PBT-WF0061iQXH
• EINECS: 618-371-8
• Material: Polybutylene Terephthalate/PBT
• Usage: General Plastics, Engineering Plastics, Specialty Plastics
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Injection
• Color: Natural Color
• Place of Origin: Guangdong, China
• Use: Radiator Front Cover.Automotive Parts
• Features: Lubricated, Good Wear Resistance, Low Friction and
• Application: Zippers Irish Flutes, Bagpipes, Practice Chanters
• Form: Resin Pellets
• Delivery Time: in 7 Days
• Applications: Appliance Handles, Spotlights, Electric Motors.
• Glass Fiber: 30%
• Transport Package: Bag
• Specification: 25KG
• Trademark: Forever
• Origin: China
• HS Code: 390740000
• Production Capacity: 50000t/Year
• Package Size: 75.00cm * 55.00cm * 15.00cm
• Package Gross Weight: 25.010kg

Product Description

PBT Containing 30% glass fiber good strength and heat resistance
   

           

The WF0061iQ-XH compound is made from Poly butylene terephthalate (PBT) resin using ELCRIN iQ upcycling technology, which incorporates a minimum of 25% Post-Consumer Recycling (PCR) weight content and 30% glass fiber. This grade offers additional advantages such as being Non-Chlorinated, Non-Brominated Flame Retardant, having a UL94V0 and 5VA Flame Rating, and displaying excellent chemical resistance. It is an ideal option for various applications that require a more sustainable flame retardant (FR) and PBT solution.

 

General
Form		Resin Pellets
Filler		30 % Glass Fiber
Feature		Good Hardness                  25 % Pcr		Non-Brominated & Non- Chlorinated Flame Retardant
		Chemical Resistant            Non-Chlorinated		Pcr
Uses                                         Automotive			Consumer	Electrical
Physical			Nominal Value	Test Method
Density / Specific Gravity			1.56 1.56 g/cm³	ASTM D792 ISO 1183
Water Absorption(23 °C;saturated)			0.23 %	ISO 62-1
Moisture Absorption(50% RH;23 °C)			0.09 %	ISO 62
Melt Volume Rate, MVR(5 kg;MVR at 250 °C)			16 cm³/10 min	ISO 1133

 

 

Mechanical	Nominal Value	Test Method
Izod Impact, Unnotched
23 °C	570 J/m	ASTM D4812
80*10*4;23 °C	37 kJ/m²	ISO 180/1U
Izod Impact, Notched
23 °C	72 J/m	ASTM D256
-30 °C	55 J/m	ASTM D256
80*10*4;23 °C	7 kJ/m²	ISO 180/1A
80*10*4;-30 °C	6 kJ/m²	ISO 180/1A
Instrumented Dart Impact, Total Energy(23 °C)	6 J	ASTM D3763
Tensile Stress, Yield
5 mm/min;Type I	105 MPa	ASTM D638
5 mm/min	108 MPa	ISO 527
Tensile Stress, Break
5 mm/min;Type I	105 MPa	ASTM D638
5 mm/min	108 MPa	ISO 527
Tensile Strain, Yield
5 mm/min;Type I	2 %	ASTM D638
5 mm/min	2 %	ISO 527
Tensile Strain, Break
5 mm/min;Type I	2 %	ASTM D638
5 mm/min	2 %	ISO 527
Tensile Modulus
5 mm/min	1.1E+04 MPa	ASTM D638
1 mm/min	1.1E+04 MPa	ISO 527
Flexural Stress, Yield
1.3 mm/min;50 mm;span	165 MPa	ASTM D790
2 mm/min	175 MPa	ISO 178
Flexural Stress, break
1.3 mm/min;50 mm;span	165 MPa	ASTM D790
2 mm/min	175 MPa	ISO 178
Flexural Modulus
1.3 mm/min;50 mm;span	9600 MPa	ASTM D790
2 mm/min	1.0E+04 MPa	ISO 178

 

 

Thermal	Nominal Value	Test Method
UL Recognized ≥ 0.8 mm ≥ 3 mm	V-0 5VB	UL 94
Glow Wire Ignition Temperature [GWIT] 3 mm 1.5 mm 0.8 mm	800 °C 775 °C 750 °C	IEC 60695-2-13
Glow Wire Flammability Index 3 mm 1.5 mm 0.8 mm	960 °C 960 °C 960 °C	IEC 60695-2-12
Heat Deflection Temperature[HDT], Unannealed 3.2 mm;1.82 MPa 0.45 MPa;3.2 mm	200 °C 214 °C	ASTM D648
CTE, Flow(-40 - 40 °C)	2.4E-05 1/°C	ASTM E831
CTE, XFlow(-40 - 40 °C)	8.0e-05 1/°C	ASTM E831
Ball Pressure Test(125°C +/- 2°C)	PASSES	IEC 60695-10-2
Relative Temp Index, Elec	75 °C	UL 746B
Relative Temp Index, Mechanical with Impact	75 °C	UL 746B
Relative Temp Index, Mechanical without Impact	75 °C	UL 746B
Electrical	Nominal Value	Test Method
Hot-wire Ignition, HWI ≥ 0.8 mm ≥ 3 mm	PLC 1 PLC 0	UL 746A
High Amp Arc Ignition, HAI( ≥ 0.8 mm)	PLC 0	UL 746A
Comparative Tracking Index	600 V	IEC 60112

 

Company Profile

Product Parameters

Our Customers

Our Certificates

 

Our Production

Our Package/Shipping

Our Advantages

 

Our Samples

 

Dongguan FOREVER Co., Ltd. Was founded in 2005 and is a national high-tech enterprise and national-level specialized giant enterprise dedicated to the research and production of polymer composite modified materials. With an annual capacity of 100, 000 tons of modified engineering plastics. Since its establishment, the company has been committed to the research of high-performance composite materials such as modified PC, PC/ABS, PBT, PA6, etc. Its products have been widely used in industries such as LED lighting, consumer electronics, new energy, security equipment, and small household appliances, providing customers with efficient delivery experience, ultimate price advantages, and strict quality assurance, contributing to the creation of a green and environmentally friendly world.

Dongguan FOREVER Co., Ltd's main products has obtained UL certification for RTI authorized temperature, outdoor weather resistance F1 and 5VA flame retardancy grades, as well as recycled-certified post-consumer low-carbon circulation products. Dongguan FOREVER Co., Ltd's products are highly recognized by customers worldwide for their reliable quality, excellent performance, and superior cost-effectiveness.

With a strong focus on research and development, Dongguan FOREVER Co., Ltd. Has established an advanced technology research and development center, equipped with state-of-the-art testing and analysis equipment and a professional R&D team that has accumulated rich experience in the field of polymer composite modified materials. Dongguan FOREVER Co., Ltd also maintains close partnerships with renowned universities and research institutions to stay at the forefront of technology and drive innovation in the industry