Nylon 6/6 resin containing 30% glass bead glass fiber and 5% Easy Molding PA66
https://forever-plastics.en.made-in-china.com/product/rJwRvlcdZpWD/China-Nylon-PA6-GF33-PA66-Granules-PA6-with-30GF-Polyamide-PA66-30-GF-PA6-Material.html Heat-conducting nylon
Product Description | |||||
RX05495 compound is based on Nylon 6/6 resin containing 30% glass bead, glass fiber and 5% graphite powder. Added features of this grade include: Easy Molding, Heat Stabilized, Mold Release, Wear Resistant. |
|||||
General | |||||
Form | Resin Pellets | ||||
Filler 30 % Glass Bead Glass Fiber 5 % Graphite Powder | |||||
Feature | Good Dimensional Internally Lubricated | Good Thermal Abrasion Resistant Excellent Processability |
|||
Uses Consumer | Electrical | Building and Construction | |||
Physical | Nominal Value | Test Method | |||
Density / Specific Gravity | 1.38 g/cm³ 1.38 g/cm³ |
ASTM D792 ISO 1183 |
|||
Moisture Absorption(23 °C;50% RH/24 hrs) | 0.84 % | ASTM D570 | |||
Mold Shrinkage, Flow | |||||
24 hrs | 0.5 % | ASTM D955 | |||
24 hrs | 0.46 % | ISO 294 | |||
Mold Shrinkage, XFlow | |||||
24 hrs | 1.5 % | ASTM D955 | |||
24 hrs | 1.5 % | ISO 294 | |||
Mechanical | Nominal Value | Test Method | |||
Izod Impact, Unnotched | |||||
23 °C | 667 J/m | ASTM D4812 | |||
80*10*4;23 °C | 45 kJ/m² | ISO 180/1U | |||
Izod Impact, Notched | |||||
23 °C | 53 J/m | ASTM D256 | |||
80*10*4;23 °C | 6 kJ/m² | ISO 180/1A | |||
Instrumented Dart Impact, Energy at Peak(23 °C) | 10 J | ASTM D3763 | |||
Multiaxial Impact | 2 J | ISO 6603 | |||
Tensile Stress, Break | |||||
117 MPa | ASTM D638 | ||||
112 MPa | ISO 527 | ||||
Tensile Strain, Break | |||||
2.8 % | ASTM D638 | ||||
2.9 % | ISO 527 | ||||
Tensile Modulus | |||||
50 mm/min | 7990 MPa | ASTM D638 | |||
1 mm/min | 7500 MPa | ISO 527 | |||
Flexural Stress | |||||
173 MPa | ASTM D790 | ||||
176 MPa | ISO 178 | ||||
Flexural Modulus | |||||
6130 MPa | ASTM D790 | ||||
7100 MPa | ISO 178 | ||||
Thermal | Nominal Value | Test Method | |||
Heat Deflection Temperature[HDT], Unannealed 0.45 MPa;3.2 mm 3.2 mm;1.82 MPa |
255 °C 233 °C |
ASTM D648 | |||
HDT/Af(1.8) | 229 °C | ISO 75/Af | |||
Processing | Nominal Value | ||||
Drying Temperature<Injection> | 80 °C | ||||
Drying Time<Injection> | 4 hrs | ||||
Maximum Moisture Content<Injection> | 0.15 - 0.25 % | ||||
Melt Temperature<Injection> | 280 - 305 °C | ||||
Front, Zone 3 Temperature<Injection> | 295 - 305 °C | ||||
Middle, Zone 2 Temperature<Injection> | 280 - 295 °C | ||||
Rear, Zone 1 Temperature<Injection> | 265 - 275 °C | ||||
Mold Temperature<Injection> | 95 - 110 °C | ||||
Back Pressure<Injection> | 0.2 - 0.3 MPa | ||||
Screw Speed <Injection> | 30 - 60 rpm |