This Grade Is Targeted for Electrical Vehicle Battery Pack Insulation Sheet/Film

• Feature: Plastics
• CAS No.: 25766-59-0
• Formula: C6h4c(CH3)2c6h4oco2-]N
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Model NO.: MPPE/PS-NHP8010T3
• EINECS: 618-371-8
• Material: Polycarbonates/PC
• Usage: General Plastics, Engineering Plastics, Specialty Plastics
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Injection
• Color: Black
• Form: Resin Pellets
• Chemical Substances: Polycarbonate
• Processing Mode: Injection Molding/Extrusion
• UV: Fr
• Use: Electrical Appliances, Auto Parts, Office Supplies
• Certificates: ISO9001:2008.SGS.RoHS
• Filler: 10%-50% Glass Fiber
• Transport Package: Bag
• Specification: 25KG
• Trademark: Forever
• Origin: China
• HS Code: 390740000
• Production Capacity: 50000t/Year
• Package Size: 75.00cm * 55.00cm * 15.00cm
• Package Gross Weight: 25.010kg

Product Description

 This grade is targeted for electrical vehicle battery pack insulation sheet/film

Product Description

 

 

Product Description
NHP8010T3 resin is a non-reinforced blend of polyphenylene ether (PPE) + polystyrene (PS) designed for high heat resistance and ultra-thin-wall FR. This extrusion and injection moldable grade contains non-brominated, non-chlorinated flame retardant and carries UL94 flame rating of V0 at 0.3mm.  NHP8010T3    is based on a unique co-polymer technology and exhibits high impact, high heat resistance, dimensional stability, hydrolytic stability, strong electrical performance, low moisture absorption and low specific gravity. This grade is   targeted for electrical vehicle (EV) battery pack insulation sheet/film, bus bar insulation layer and other high voltage electric component. See NHP8000VT3 resin for V0 at 0.25mm and CTI 600V/PLC 0 version.
General
Form                                        Resin Pellets
Low Warpage                    Low Shrinkage                  Non-Brominated
Feature	Chlorinated Flame   Retardant		Good Thermal   Hydrolysis Resistance Li  ht W  i  ht
Amorphous
U                                                                                           Hood
Household electrics                 Energy Storage
Physical                                                                                                                      Nominal Value                                                        Test Method
Density / Specific Gravity                                                     1.09 g/cm³                                             ISO 1183
Melt Mass-Flow Rate, MFR(300 °C;5 kg)                             16 g/10min                                             ASTM D1238
Molding Shrinkage, Flow                                                     0.77 %                                                    Internal Method
Molding Shrinkage, Across Flow                                         0.76 %                                                    Internal Method
Water Absorption, Equilibrium(50% RH;24 hrs;23 °C)        0.040 %                                                  ISO 62
Mechanical		Nominal Value		Test Method
Tensile Modulus
5 mm/min		2380 MPa 2440 MPa		ASTM D638 ISO 527-1/1
Tensile Strength, Yield
5 mm/min;Type I		62.0 MPa 63.0 MPa		ASTM D638 ISO 527-2/5
Tensile Strength, Break
5 mm/min;Type I		49.0 MPa 50.0 MPa		ASTM D638 ISO 527-2/5
Tensile Elongation, Yield
5 mm/min;Type I		4.2 % 4.2 %		ASTM D638 ISO 527-2/5
Tensile Elongation, Break
5 mm/min;Type I		11 % 36 %		ASTM D638 ISO 527-2/5
Flexural Modulus
1.3 mm/min;50 mm;span		2470 MPa		ASTM D790
2 mm/min		2450 MPa		ISO 178
Flexural Strength
1.3 mm/min;5.0% Strain;50 mm;span		102 MPa		ASTM D790
2 mm/min		106 MPa		ISO 178
Flexural Strength, Yield(1.3 mm/min;50 mm;span)		106 MPa		ASTM D790
Flexural Strength, Break(1.3 mm/min;50 mm;span)		104 MPa		ASTM D790
Notched Izod Impact
-40 °C		100 J/m		ASTM D256
23 °C		330 J/m		ASTM D256
80*10*4 mm;-40 °C		11 kJ/m²		ISO 180/1A
80*10*4 mm;23 °C		25 kJ/m²		ISO 180/1A
Unnotched Izod Impact
-40 °C		1800 J/m		ASTM D4812
23 °C		2200 J/m		ASTM D4812
80*10*4 mm;-40 °C		No Break		ISO 180/1U
80*10*4 mm;23 °C		No Break		ISO 180/1U
Thermal		Nominal Value		Test Method
Deflection Temperature Under Load, Unannealed 0.45 MPa;3.2 mm 1.8 MPa;3.2 mm 80*10*4 mm;0.45 MPa;4 mm;span;64 mm 80*10*4 mm;1.8 MPa;4 mm;span;64 mm		149 °C 132 °C 149 °C 134 °C		ASTM D648 ASTM D648 ISO 75-2/Bf ISO 75-2/Af
Vicat Softening Temperature 50 °C/h;10 N;Rate A;Loading 1 120 °C/h;10 N;Rate B;Loading 1		163 °C 165 °C		ASTM D1525
Flame Rating(0.25 mm)		V-0		UL 94
Electrical		Nominal Value		Test Method
Surface Resistivity		6.6E+16 ohms		ASTM D257
Volume Resistivity		4.6E+16 ohms ·cm		ASTM D257
CTI		600 V
Processing				Nominal Value
Drying Temperature<Injection>				100 - 120 °C
Drying Time<Injection>				3.0 - 5.0 hr
Rear Temperature<Injection>				280 - 320 °C
Middle Temperature<injection>				280 - 320 °C
Front Temperature<Injection>				280 - 320 °C
Nozzle Temperature<Injection>				250 - 320 °C
Processing Temp, Melt<Injection>				280 - 320 °C
Mold Temperature<Injection>				70 - 120 °C
Back Pressure<Injection>				3.00 - 8.00 MPa
Screw Speed <Injection>				20 - 100 rpm

                                                                                                                  Forever Co.,Ltd

 

With almost 20 years in the modified engineering plastics,Forever Plastics is a high-tech manufacture integrating R&D, production and sales of high-performance resin or polymer ,including PC,PP,PA6,PA66, PBT,PET, PC/ABS, PC/PBT, PC/PET alloy compounds,TPE,TPU, PE for rotomolding with the property of the flame retardant, glass fiber reinforced, high glossy, UV resistance.....with the annual output value of USD 65 million in 2021. 