Polycarbonate Resin PC Fr Polycarbonate Resin Featuring High Flow with Balanced Impact

• CAS No.: 942626-09-7
• Formula: C18h18bno4
• EINECS: 323.15100
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Model NO.: PC-BFL2000B
• Material: Polycarbonates/PC
• Usage: Engineering Plastics
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Injection
• Color: White
• Form: Resin Pellets
• Chemical Substances: Polycarbonate
• Processing Mode: Injection Molding/Extrusion
• UV: Fr
• Use: Electrical Appliances, Auto Parts, Office Supplies
• Certificates: ISO9001:2008.SGS.RoHS
• Transport Package: Bag
• Specification: 25KG
• Trademark: Forever
• Origin: China
• HS Code: 39081011
• Production Capacity: 50000t/Year
• Package Size: 75.00cm * 55.00cm * 15.00cm
• Package Gross Weight: 25.010kg

Product Description

Polycarbonate resin PC  FR polycarbonate resin featuring high flow with balanced impact

 

Product Description

Product Description
BFL2000B resin is a Br- & Cl-free FR polycarbonate resin featuring high flow with balanced impact. It is available only in dark colors.
General
Form	Resin Pellets
Feature	Non-Brominated & Non-   Non-Chlorinated               Light Shielding Chlorinated Flame   Retardant
UL Yellow Card	E207780-228410   E45329-100081160
Uses                                          Backlighting Modulus
Physical		Nominal Value	Test Method
Density / Specific Gravity		1.20 g/cm 1.20 g/cm³	ASTM D792 ISO 1183
Moisture Absorption(50% RH;23 °C)		0.150 %	ISO 62
Water Absorption at Saturation		0.35 %	ISO 62
Linear Mold Shrinkage, Flow(Thickness; 3.2 mm)		0.5 - 0.7 %
Melt Flow(1.2 kg;300 °C)		29 g/10min	ASTM D1238
Mechanical		Nominal Value	Test Method
Tensile Strength, Yield(5 mm/min)		66.0 MPa	ASTM D638-1
Elongation at Yield(5 mm/min)		180 %	ASTM D638-1
Flexural Yield Strength(1.3 mm/min;50 mm;span)		93.0 MPa	ASTM D790
Flexural Modulus(1.3 mm/min;50 mm;span)		2180 MPa	ASTM D790
Izod Impact, Notched(Temperature; 23 °C)		716 J/m	ASTM D256
Thermal		Nominal Value	Test Method
Deflection Temperature(Thickness; 3.2 mm;Pressure; 1.8 MPa)		127 °C	ASTM D648
Flammability, UL94			UL 94
Thickness; 0.75 mm		V-2
Thickness; 1.5 mm		V-0
Processing		Nominal Value
Injection Molding
Drying Temperature		120 °C
Drying Time		3 - 4 hrs
Drying Time, Cumulative		48 hrs
Maximum Moisture Content		0.02 %
Melt Temperature		270 - 295 °C
Nozzle Temperature		265 - 290 °C
Front - Zone 3 Temperature		270 - 295 °C
Middle - Zone 2 Temperature		260 - 280 °C
Rear - Zone 1 Temperature		250 - 270 °C
Mold Temperature		70 - 95 °C
Back Pressure		0.3 - 0.7 MPa
Screw Speed		40 - 70 rpm
Shot to Cylinder Size		40 - 60 %
Vent Depth		0.025 - 0.076 mm

good quality UV-stabilized UL746 F1 F2 PC blend alloy equal to Covestro Makroblend TEIJIN Panlite Mitsubishi

With almost 20 years in the modified engineering plastics,Forever Plastics is a high-tech manufacture integrating R&D, production and sales of high-performance resin or polymer ,including PC,PP,PA6,PA66, PBT,PET, PC/ABS, PC/PBT, PC/PET alloy compounds,TPE,TPU, PE for rotomolding with the property of the flame retardant, glass fiber reinforced, high glossy, UV resistance.....with the annual output value of USD 65 million in 2021Our customers are Philips,Osram,Cree,Schneider,Siemens,etc. for years in the electrical&electronics components, Automotive parts, House appliance,LED lights.....