| Application: | Motor, Electric Cars, Motorcycle, Machinery, Marine, Toy, Agricultural Machinery, Car |
|---|---|
| Hardness: | Hardened Tooth Surface |
| Gear Position: | Internal Gear |
| Samples: |
|---|
| Customization: |
|---|
|
Shipping Cost:
Estimated freight per unit. |
about shipping cost and estimated delivery time. |
|---|
| Payment Method: |
|
|---|---|
| Initial Payment Full Payment |
| Currency: | US$ |
|---|
| Return&refunds: | You can apply for a refund up to 30 days after receipt of the products. |
|---|
Suppliers with verified business licenses
Audited Supplier 
ITEM NO: POM FX-11XH
FEATURE: Injection grade
| General |
| Form Resin Pellets |
| Feature Abrasion Resistant |
| Uses Automotive Electronics Automotive |
| Physical Nominal Value Test Method |
| Density / Specific Gravity 1.39 g/cm³ ISO 1183 |
| Melt Mass-Flow Rate, MFR(190 °C;2.16 kg) 10 g/10min ISO 1133 |
| Melt Volume-Flow Rate, MVR(190 °C;2.16 kg) 8.60 cm³/10 min ISO 1133 |
| Molding Shrinkage, Flow(3 mm) 2.1 % Internal Method |
| Water Absorption - 60% RH(23 °C) 0.22 % Internal Method |
| Mechanical Nominal Value Test Method |
| Tensile Modulus 2700 MPa ISO 527-2/1 |
| Tensile Stress, Yield 55.0 MPa ISO 527-2/50 |
| Tensile Strain, Yield 9.0 % ISO 527-2/50 |
| Tensile Strain, Break 35 % ISO 527-2/50 |
| Flexural Modulus(2 mm/min) 2500 MPa ISO 178 |
| Flexural Stress(2 mm/min) 81.0 MPa ISO 178 |
| C harpy Notched Impact Strength(23 °C) 7.0 kJ/m² ISO 179 |
| C harpy Unnotched Impact Strength(23 °C) 200 kJ/m² ISO 179 |
| Thermal Nominal Value Test Method |
| Heat Deflection Temperature, Unannealed |
| 0.45 MPa 156 °C ISO 75-2/B |
| 1.8 MPa 95.0 °C ISO 75-2/A |
| CLTE, Flow 1.1E-4 cm/cm/°C ISO 11359-2 |
| CLTE, Transverse 1.1E-4 cm/cm/°C ISO 11359-2 |
| Flame Rating(0.8 mm) HB UL 94 |
| Electrical | Nominal Value | Test Method |
| Surface Resistivity | 1.0E+16 ohms | IEC 60093 |
| Volume Resistivity | 1.0E+14 ohms ·cm | IEC 60093 |
| Electric Strength | ||
| 1 mm | 36 kV/mm | ASTM D150;IEC 60250 |
| 3 mm | 19 kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 600 V | IEC 60112 |
| Processing | Nominal Value | |
| Drying Temperature - Hot Air Dryer<Injection> | 80 °C | |
| Drying Time - Hot Air Dryer<Injection> | 3.0 - 4.0 hr | |
| Rear Temperature<Injection> | 170 °C | |
| Middle Temperature<injection> | 180 °C | |
| Front Temperature<Injection> | 190 °C | |
| Nozzle Temperature<Injection> | 180 - 210 °C | |
| Mold Temperature<Injection> | 60 - 80 °C | |
| Injection Pressure<Injection> | 50.0 - 100 MPa | |
| Injection Rate<Injection> | Moderate | |
| Screw Speed <Injection> | 80 - 120 rpm | |
| Melting Point | 166 °C |
NOTICE: The data contained are based on our current knowledge and experience. This information may be subject to revision without informing in advance as new knowledge and experience become available. Because use conditions and applicable laws may differ from one location to another and may change with time, Customer is responsible for determining whether products and the information in t his document are appropriate for Customer's use and for ensuring that Customer's workplace and disposal practices are in compliance with applicable laws. Seller assumes no obligation or liability for the information in this document.