Product Description | |||||||
LUX9612G is an injection moldable polycarbonate (PC) with an MVR (300°C/1.2kg) 7. It contains non- brominated, non-chlorinated flame retardant systems with UL-94 [email protected] rating. This UV stabilized grade has a diffusion effect and thin wall FR performance providing good color stability under heat exposure. |
|||||||
General | |||||||
Form | Resin Pellets | ||||||
Feature | Non-Brominated Diffusive | Non-Chlorinated | Outdoor | ||||
UL Yellow Card E207780-101344669 | |||||||
Uses Lighting Applications Lighting Diffusers Electronic Displays | |||||||
Physical | Nominal Value | Test Method | |||||
Density / Specific Gravity | 1.20 g/cm³ | ASTM D792;ISO 1183 | |||||
Melt Mass-Flow Rate, MFR(300 °C;1.2 kg) | 7.0 g/10min | ASTM D1238 | |||||
Molding Shrinkage, Flow(3.2 mm) | 0.60 - 0.80 % | Internal Method | |||||
Water Absorption, Saturation(23 °C) | 0.35 % | ISO 62 | |||||
Water Absorption, Equilibrium(50% RH;23 °C) | 0.15 % | ISO 62 | |||||
Mechanical | Nominal Value | Test Method | |||||
Tensile Modulus | |||||||
5 mm/min | 2300 MPa 2230 MPa |
ASTM D638 ISO 527-2/1 |
|||||
Tensile Strength, Yield | |||||||
50 mm/min;Type I | 62.0 MPa 62.0 MPa |
ASTM D638 ISO 527-2/50 |
|||||
Tensile Strength, Break | |||||||
50 mm/min;Type I | 65.0 MPa 58.0 MPa |
ASTM D638 ISO 527-2/50 |
|||||
Tensile Elongation, Yield | |||||||
50 mm/min;Type I | 6.0 % 6.0 % |
ASTM D638 ISO 527-2/50 |
|||||
Tensile Elongation, Break | |||||||
50 mm/min;Type I | 80 % 77 % |
ASTM D638 ISO 527-2/50 |
|||||
Flexural Modulus | |||||||
1.3 mm/min;50 mm;Span | 2160 MPa | ASTM D790 | |||||
2 mm/min | 2250 MPa | ISO 178 | |||||
Flexural Stress, at Break(13 mm/min) | 95.0 MPa | ISO 178 | |||||
Flexural Stress, Yield(1.3 mm/min;50 mm;Span) | 95.0 MPa | ASTM D790 | |||||
Notched Izod Impact | |||||||
23 °C | 400 J/m | ASTM D256 | |||||
23 °C;80*10*3 mm | 40 kJ/m² | ISO 180/1A | |||||
Instrumented Dart Impact, Total Energy(23 °C) | 70.0 J | ASTM D3763 | |||||
Thermal | Nominal Value | Test Method | |||||
Deflection Temperature Under Load, Unannealed 1.8 MPa;3.2 mm 80*10*4 mm;1.8 MPa;4 mm;64 mm;Span |
123 °C 123 °C |
ASTM D648 ISO 75-2/Af |
|||||
Vicat Softening Temperature(50 °C/h;50 N;Rate A;Loading 2) | 140 °C | ASTM D1525 | |||||
Ball Pressure Test(123 - 127 °C) | Pass | IEC 60695-10-2 | |||||
CLTE, Flow(-40 - 40 °C) | 6.8E-5 cm/cm/°C | ASTM E831 | |||||
CLTE, Transverse(-40 - 40 °C) | 6.7E-5 cm/cm/°C | ASTM E831 | |||||
Flame Rating(1.5 mm) | V-0 | UL 94 | |||||
Glow Wire Flammability Index(1 mm) | 960 °C | IEC 60695-2-12 | |||||
Glow Wire Ignition Temperature [GWIT] 1 mm 1.5 mm |
850 °C 850 °C |
IEC 60695-2-13 | |||||
Electrical | Nominal Value | Test Method | |||||
Comparative Tracking Index[CTI] | PLC 3 | UL 746 | |||||
High Amp Arc Ignition, HAI, Surface | PLC 1 | UL 746 | |||||
Hot-wire Ignition, HWI | PLC 3 | UL 746 | |||||
Processing | Nominal Value | ||||||
Drying Temperature<Injection> | 120 °C | ||||||
Drying Time<Injection> | 2.0 - 4.0 hr | ||||||
Suggested Max Moisture<Injection> | 0.020 % | ||||||
Hopper Temperature<Injection> | 60 - 80 °C | ||||||
Rear Temperature<Injection> | 260 - 280 °C | ||||||
Middle Temperature<injection> | 270 - 290 °C | ||||||
Nozzle Temperature<Injection> | 270 - 290 °C |