Flame-retardant polyamide 66 33% glass-fiber reinforced for injection moulding
https://forever-plastics.en.made-in-china.com/product/rJwRvlcdZpWD/China-Nylon-PA6-GF33-PA66-Granules-PA6-with-30GF-Polyamide-PA66-30-GF-PA6-Material.html Heat-conducting nylon
Product Description | |||
Descriptions: DSC201AG6 is one of the brands which made by Polyamide66 that filled Glass Fiber/Mineral Filler 30% and reinforced goods. It provides good mechanical strength, dimensions stability and good abrasion resistance property. Applications: DSC201AG6 is one of the most-used for good mechanical property, dimensions stability and good abrasion resistance property goods, such as Bushing of Automotive parts, etc. |
|||
General | |||
Form Resin Pellets | |||
Filler 30 % Glass Fiber/Mineral | |||
Feature Abrasion Resistant | Good Dimensional | ||
Uses Bushings | Automotive | ||
Physical | Nominal Value | Test Method | |
Density / Specific Gravity | 1.40 g/cm³ | ASTM D792 | |
Molding Shrinkage, Flow | 0.50 - 0.90 % | No Standard | |
Water Absorption(24 hr;23 °C) | 0.70 % | ASTM D570 | |
Rockwell Hardness, R-Scale | 122 | ASTM D785 | |
Mechanical | Nominal Value | Test Method | |
Tensile Strength | 157 MPa | ASTM D638 | |
Tensile Elongation, Break | 3.0 % | ASTM D638 | |
Flexural Modulus | 8340 MPa | ASTM D790 | |
Flexural Strength | 216 MPa | ASTM D790 | |
Notched Izod Impact | 78 J/m | ASTM D256 | |
Thermal | Nominal Value | Test Method | |
Deflection Temperature Under Load, Unannealed 0.45 MPa 1.8 MPa |
260 °C 250 °C |
ASTM D648 | |
Melting Temperature | 260 °C | DSC | |
Flame Rating | HB | UL 94 | |
Electrical | Nominal Value | Test Method | |
Volume Resistivity | 1.0e+15 ohms ·cm | ASTM D257 | |
Dielectric Strength | 25 kV/mm | ASTM D149 | |
Processing | Nominal Value | ||
Drying Temperature<Injection> | 80 - 100 °C | ||
Drying Time<Injection> | 4.0 - 5.0 hr | ||
Suggested Max Moisture<Injection> | < 0.20 % | ||
Rear Temperature<Injection> | 270 - 280 °C | ||
Middle Temperature<injection> | 280 - 285 °C | ||
Front Temperature<Injection> | 285 - 290 °C | ||
Nozzle Temperature<Injection> | 280 - 285 °C | ||
Processing Temp, Melt<Injection> | 280 - 285 °C | ||
Mold Temperature<Injection> | 80 - 120 °C | ||
Speed <Injection> | 40 - 70 % | ||
Pressure 1st<Injection> | 30 - 60 % | ||
Pressure 2nd <Injection> | 30 - 60 % | ||
Holding Pressure<Injection> | 10 - 20 % |