Feature: | Plastics |
---|---|
CAS No.: | 63440-93-7 |
Formula: | C24h24o8 |
Samples: |
25kg/bag
|
---|
Customization: |
---|
Shipping Cost:
Estimated freight per unit. |
about shipping cost and estimated delivery time. |
---|
Payment Method: | |
---|---|
Initial Payment Full Payment |
Currency: | US$ |
---|
Return&refunds: | You can apply for a refund up to 30 days after receipt of the products. |
---|
Suppliers with verified business licenses
General |
|||
Form |
Resin Pellets |
||
Feature |
30 % Pcr |
||
Usage Electronic Displays |
Electrical Engineering |
||
Physical |
Nominal Value |
Test Method |
|
Density / Specific Gravity |
1.19 g/cm³ |
ASTM D792 |
|
Melt Mass-Flow Rate, MFR(260 °C;2.16 kg) |
20 g/10min |
ASTM D1238 |
|
Molding Shrinkage, Across Flow(3.2 mm) |
0.30 - 0.50 % |
Internal Method |
|
Molding Shrinkage, Flow(3.2 mm) |
0.30 - 0.50 % |
Internal Method |
|
Water Absorption(24 hr;23 °C) |
0.11 % |
ASTM D570 |
|
Mechanical |
Nominal Value |
Test Method |
|
Tensile Modulus(50 mm/min) |
2500 MPa |
ASTM D638 |
|
Tensile Strength, Yield(50 mm/min;Type I) |
60.0 MPa |
ASTM D638 |
|
Tensile Strength, Break(50 mm/min;Type I) |
47.0 MPa |
ASTM D638 |
|
Tensile Elongation, Yield(50 mm/min;Type I) |
4.0 % |
ASTM D638 |
|
Tensile Elongation, Break(50 mm/min;Type I) |
60 % |
ASTM D638 |
|
Flexural Modulus(1.3 mm/min;50 mm;Span) |
2400 MPa |
ASTM D790 |
|
Flexural Strength, Yield(1.3 mm/min;50 mm;Span) |
90.0 MPa |
ASTM D790 |
|
Notched Izod Impact |
|||
23 °C |
500 J/m |
ASTM D256 |
|
23 °C;80*10*3 mm |
55 kJ/m² |
ISO 180/1A |
|
Instrumented Dart Impact, Total Energy(23 °C) |
50.0 J |
ASTM D3763 |
Thermal |
Nominal Value |
Test Method |
Deflection Temperature Under Load, Unannealed 0.45 MPa;6.4 mm 1.8 MPa;3.2 mm 1.8 MPa;6.4 mm |
90.0 °C 75.0 °C 82.0 °C |
ASTM D648 |
Vicat Softening Temperature(50 °C/h;50 N;Rate A;Loading 2) |
92.0 °C |
ASTM D1525 |
CLTE, Flow(-40 - 60 °C) |
7.1E-5 cm/cm/°C |
ASTM E831 |
CLTE, Transverse(-40 - 60 °C) |
7.6E-5 cm/cm/°C |
ASTM E831 |
RTI Elec |
60.0 °C |
UL 746B |
RTI Imp |
60.0 °C |
UL 746B |
RTI Str |
60.0 °C |
UL 746B |
Flame Rating > 1.5 mm > 2 mm |
V-0 5VB |
UL 94 |
Electrical |
Nominal Value |
Test Method |
Hot-wire Ignition, HWI( > 3 mm) |
PLC 2 |
UL 746A |
Processing |
Nominal Value |
|
Drying Temperature<Injection> |
80 - 90 °C |
|
Drying Time<Injection> |
3.0 - 4.0 hr |
|
Suggested Max Moisture<Injection> |
0.040 % |
|
Suggested Shot Size<Injection> |
30 - 80 % |
|
Rear Temperature<Injection> |
220 - 255 °C |
|
Middle Temperature<injection> |
220 - 265 °C |
|
Front Temperature<Injection> |
245 - 275 °C |
|
Nozzle Temperature<Injection> |
245 - 275 °C |
|
Processing Temp, Melt<Injection> |
245 - 275 °C |
|
Mold Temperature<Injection> |
60 - 80 °C |
|
Back Pressure<Injection> |
0.300 - 0.700 MPa |
|
Screw Speed <Injection> |
40 - 70 rpm |
|
Vent Depth <Injection> |
0.038 - 0.076 mm |
|
Drying Time, Cumulative<Injection> |
8 hr |