PPA Resin and It Uses a Non-Halogenated Flame Retardant Ppapolycarbonate Virgin

• Feature: Oxidative Degradable
• CAS No.: 32131-17-2
• Formula: (C12h22n2o2)N
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Model NO.: PPA-FR42G30NH BK337
• EINECS: 211-024-8
• Material: Polyamide(Nylon 6.66)/PA
• Usage: General Plastics, Engineering Plastics, Specialty Plastics
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Injection
• Color: Black
• Form: Resin Pellets
• Chemical Substances: Nylon
• Processing Mode: Injection Molding/Extrusion
• UV: Fr
• Use: Electrical Appliances, Auto Parts, Office Supplies
• Certificates: ISO9001:2008.SGS.RoHS
• Filler: 10%-60% Glass Fiber
• Transport Package: Bag
• Specification: 25KG
• Trademark: Forever
• Origin: China
• HS Code: 390740000
• Production Capacity: 50000t/Year
• Package Size: 75.00cm * 55.00cm * 15.00cm
• Package Gross Weight: 25.010kg

Product Description

15% Glass Reinforced PA4T Improved flow Flame Retardant Halogen free
 Heat-conducting nylon

Product Description

Product Description
HTNFR42G30NH BK337 is a 30% glass reinforced, flame retardant high performance polyamide resin developed for improved reflow soldering performance in connector applications. It is also a PPA resin and it uses a non-halogenated flame retardant.
General
Form                                        Resin Pellets
Filler                                         30 % Glass Fiber
Chlorinated  Flame R   t     d       t
Uses                                          Connector
Physical                                                                                 Nominal Value                                       Test Method
Resin ID, ISO 1043                                                                PA-GF30FR(40)                                      ISO 1043
Part Marking Code, ISO 11469                                            PA-GF30FR(40)                                      ISO 11469
Part Marking Code                                                               >PPA-GF30FR                                        SAE J344
Density, dry                                                                           1.47 g/cm³                                              ISO 1183
Dry: Molding Shrinkage, Across Flow                                 0.90 %                                                     ISO 294-4
Dry: Molding Shrinkage, Flow                                             0.40 %                                                     ISO 294-4
Dry: Bio based Carbon Content                                            21 %                                                        ISO 16620-2
Dry: Humidity absorption                                                    1 %                                                          Sim. to ISO 62
Mechanical	Nominal Value		Test Method
Dry: Tensile Modulus	12000 MPa		ISO 527-1/-2
Condition: Tensile Modulus	12000 MPa		ISO 527-1/-2
Dry: Tensile Stress, Break	134 MPa		ISO 527-1/-2
Condition: Tensile Stress, Break	110 MPa		ISO 527-1/-2
Dry: Tensile Strain, Break	1.7 %		ISO 527-1/-2
Condition: Tensile Strain, Break	1.4 %		ISO 527-1/-2
Dry: Flexural Modulus	11300 MPa		ISO 178
Condition: Flexural Modulus	11000 MPa		ISO 178
Dry: Flexural Stress	210 MPa		ISO 178
Dry: Charpy Notched Impact Strength -30 °C 23 °C	6.0 kJ/m² 7.0 kJ/m²		ISO 179 1eA
Dry: Charpy Unnotched Impact Strength -30 °C 23 °C	35 kJ/m² 35 kJ/m²		ISO 179 1eU
Poisson's Ratio	0.33
Thermal	Nominal Value		Test Method
Dry: Glass Transition Temperature(10 °C;min)	80.0 °C		ISO 11357-2
Conditioned: Glass Transition Temperature, Tg(10 °C;min)	50.0 °C		ISO 11357-2
Dry: Melting Temperature	314 °C		ISO 11357-3
Deflection Temperature Under Load, Annealed, Annealing cycle(1.8 MPa)	277 °C		ISO 75-1/-2
Dry: CLTE, Flow -40 - 23 °C 55 - 160 °C	2.0E-5 cm/cm/°C 1.7E-5 cm/cm/°C 2.0E-5 cm/cm/°C		ISO 11359-2
Dry: CLTE, Transverse -40 - 23 °C 55 - 160 °C	5.1E-5 cm/cm/°C 4.3E-5 cm/cm/°C 8.4E-5 cm/cm/°C		ISO 11359-2
Dry: RTI Elec 0.4 mm 1.5 mm 3 mm	130 °C 130 °C 130 °C		UL 746
Dry: RTI Imp 0.4 mm 1.5 mm 3 mm	115 °C 115 °C 120 °C		UL 746
Dry: RTI Str 0.4 mm 1.5 mm 3 mm	125 °C 125 °C 130 °C		UL 746
Dry: Flame Rating(0.4 mm)	V-0		UL 94;IEC 60695- 11-10;-20
Dry: Glow Wire Flammability Index 0.4 mm 1.5 mm 3 mm	960 °C 960 °C 960 °C		IEC 60695-2-12
Dry: Glow Wire Ignition Temperature 0.4 mm 1.5 mm 3 mm	750 °C 800 °C 825 °C		IEC 60695-2-13
Electrical	Nominal Value		Test Method
Dry: Volume Resistivity	> 1E+11 ohms ·cm		IEC 62631-3-1
Dry: Electric Strength	33 kV/mm		IEC 60243-1
Dry: Comparative Tracking Index	600 V		IEC 60112
Dry: Comparative Tracking Index[CTI](3 mm)	PLC 0		UL 746A
Dry: Dielectric Constant 23 °C;1.0e+9 Hz 23 °C;1.0e+10 Hz	3.7 3.8		ASTM D2520 B
Dry: Dissipation Factor 23 °C;1.0e+9 Hz 23 °C;1.0e+10 Hz	0.116 0.1		ASTM D2520 B
Processing		Nominal Value
Drying Temperature<Injection>		100 °C
Drying Time - Desiccant Dryer<Injection>		6.0 - 8.0 hr
Suggested Max Moisture<Injection>		0.10 %
Processing Temp, Melt<Injection>		325 - 335 °C
Mold Temperature<Injection>		110 - 130 °C
Drying Recommended <Injection>		YES

 

 

                                                                                                                  Forever Co.,Ltd

 

With almost 20 years in the modified engineering plastics,Forever Plastics is a high-tech manufacture integrating R&D, production and sales of high-performance resin or polymer ,including PC,PP,PA6,PA66, PBT,PET, PC/ABS, PC/PBT, PC/PET alloy compounds,TPE,TPU, PE for rotomolding with the property of the flame retardant, glass fiber reinforced, high glossy, UV resistance.....with the annual output value of USD 65 million in 2021. 