Injection molding grade with 30% glass fibers for parts requiring enhanced fire resistance (eg potentiometer parts, plug-and-socket connectors, switches). |
General |
Form |
|
Resin Pellets |
Filler |
|
30 % Glass Fiber |
Feature |
|
Ec 1907/2006 (Reach) |
UL Yellow Card |
E41871-233791 |
Uses Switches Connector Electrical Engineering |
Physical |
Nominal Value |
Test Method |
Density / Specific Gravity |
1.65 g/cm³ |
ISO 1183 |
Melt Volume-Flow Rate, MVR(275 °C;2.16 kg) |
8.0 cm³/10 min |
ISO 1133 |
Molding Shrinkage, Across Flow |
1.0 % |
No Standard |
Molding Shrinkage, Flow |
0.20 % |
No Standard |
Water Absorption, Saturation(23 °C) |
0.40 % |
ISO 62 |
Water Absorption, Equilibrium(50% RH;23 °C) |
0.20 % |
ISO 62 |
Viscosity Number(1;solution 0;5 g/ml Phenole/1;2 Dichlorbenzol 1) |
108 cm³/g |
ISO 307 |
Mechanical |
Nominal Value |
Test Method |
Tensile Modulus |
11300 MPa |
ISO 527-2 |
Tensile Stress, Break |
145 MPa |
ISO 527-2 |
Tensile Strain, Break |
2.3 % |
ISO 527-2 |
C harpy Notched Impact Strength(23 °C) |
10 kJ/m² |
ISO 179 1eA |
C harpy Unnotched Impact Strength |
|
ISO 179 1eU |
-30 °C |
55 kJ/m² |
|
23 °C |
60 kJ/m² |
|
Thermal |
Nominal Value |
Test Method |
Heat Deflection Temperature, Unannealed |
|
|
0.45 MPa |
220 °C |
ISO 75-2/B |
1.8 MPa |
205 °C |
ISO 75-2/A |
Melting Point |
223 °C |
ISO 11357-3 |
Glow Wire Flammability Index(1 mm) |
960 °C |
IEC 60695-2-12 |
Oxygen Index |
32 % |
ISO 4589-2 |
Electrical |
Nominal Value |
Test Method |
Surface Resistivity |
1.0E+13 ohms |
IEC 60093 |
Volume Resistivity |
1.0E+16 ohms ·cm |
IEC 60093 |
Relative Permittivity(1.0e+6 Hz) |
3.90 |
IEC 60250 |
Dissipation Factor(1.0e+6 Hz) |
0.015 |
IEC 60250 |
Comparative Tracking Index, Solution A |
200 V |
IEC 60112 |
Processing |
|
Nominal Value |
Drying Temperature<Injection> |
|
80 - 120 °C |
Drying Time<Injection> |
|
4.0 hr |
Hopper Temperature<Injection> |
|
80 °C |
Rear Temperature<Injection> |
|
240 °C |
Middle Temperature<injection> |
|
245 °C |
Front Temperature<Injection> |
|
250 °C |
Nozzle Temperature<Injection> |
|
250 °C |
Processing Temp, Melt<Injection> |
|
250 - 275 °C |
Mold Temperature<Injection> |
|
60 - 100 °C |
Screw Speed <Injection> |
|
< 15 m/min |