Polyamide 6 Non-Phosphorous and Non-Halogenated Flame Retardant System Reinforced

• Feature: Oxidative Degradable
• CAS No.: 32131-17-2
• Formula: (C12h22n2o2)N
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Model NO.: PA6-C 52G4
• EINECS: 211-024-8
• Material: Polyamide(Nylon 6.66)/PA
• Usage: General Plastics, Engineering Plastics, Specialty Plastics
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Injection
• Color: Black
• Form: Resin Pellets
• Chemical Substances: Nylon
• Processing Mode: Injection Molding/Extrusion
• UV: Fr
• Use: Electrical Appliances, Auto Parts, Office Supplies
• Certificates: ISO9001:2008.SGS.RoHS
• Filler: 5%-60% Glass Fiber/Mineral
• Transport Package: Bag
• Specification: 25KG
• Trademark: Forever
• Origin: China
• HS Code: 390740000
• Production Capacity: 50000t/Year
• Package Size: 75.00cm * 55.00cm * 15.00cm
• Package Gross Weight: 25.010kg

Product Description

 polyamide 6  non-phosphorous and Non-halogenated flame retardant system reinforced
 Heat-conducting nylon

Product Description

Product Description
PROTECT C 52G4 MZ25 WT R9003 is a polyamide 6 based on a non-phosphorous and Non- halogenated flame retardant system, reinforced with 25% of mineral filler, heat stabilized, for injection moulding. This grade offers a robust glow wire resistance, combined with enhanced processing behavior suitable for thin wall parts.
General
Form                                        Resin Pellets
Filler                                         25 % Mineral
Chlorinated  Flame R   t     d      t
Uses                                          Connector                         Electrical
Physical                                                                                 Nominal Value                                       Test Method
Density / Specific Gravity                                                     1.37 g/cm³                                             ISO 1183
Water Absorption(24 hr, 23°C)                                            1 %                                                         ISO 62
Water Absorption at Saturation(24 hr, 23°C)                      6 %                                                         ISO 62
Molding shrinkage, parallel(72 hr, 23°C, 50% RH)              0.6 %
Molding shrinkage, normal(72 hr, 23°C, 50% RH)              0.8 %
Mechanical	Nominal Value	Test Method
Tensile Modulus 1 mm/min/dry 1 mm/min/conditioned	6900 MPa 2400 MPa	ISO 527-1/-2
Stress at break dry conditioned	75 MPa 35 MPa	ISO 527-1/-2
Strain at break	3 %	ISO 527-1/-2
Flexural Modulus 2 mm/min/dry 2 mm/min/conditioned 2 mm/min	6300 MPa 2500 MPa 6000 MPa	ISO 178 ISO 178 ASTM D790
Flexural Strength 2 mm/min/dry 2 mm/min/conditioned 2 mm/min	125 MPa 50 MPa 120 MPa	ISO 178 ISO 178 ASTM D790
C harpy Impact Strength, Unnotched dry; 23 ºC conditioned; 23 -30 °C	35 kJ/m² 80 kJ/m² 45 kJ/m²	ISO 179 1eU
C harpy Notched Impact Strength dry; 23 ºC conditioned; 23 -30 °C	3 kJ/m² 4.5 kJ/m² 2.5 kJ/m²	ISO 179 1eA
Notched Izod Impact Strength(23 ºC)	2 kJ/m²	ISO 180/1A
Thermal	Nominal Value	Test Method
Melting Temperature(10°C/min)	222 °C	ISO 11357-1
Temp. of deflection under load 0.45 MPa 1.8 MPa	200 °C 130 °C	ISO 75
Flammability 0.75 mm 1.5 mm 3 mm	V-2 V-2 V-2	UL 94
Electrical	Nominal Value	Test Method
Comparative Tracking Index(Solution A)	525 V	IEC 60112
Dielectric Strength(1 mm)	35 kV/mm	IEC 60243-1
Processing		Nominal Value
Drying Temperature		80 °C
Drying Time		2 - 4 h
Suggested Max Moisture		0.2 %
Rear Temperature		230 - 235 °C
Middle Temperature		235 - 240 °C
Front Temperature		240 - 250 °C
Mould Temperature<Injection>		60 - 90 °C

 

                                                                                                                  Forever Co.,Ltd

 

With almost 20 years in the modified engineering plastics,Forever Plastics is a high-tech manufacture integrating R&D, production and sales of high-performance resin or polymer ,including PC,PP,PA6,PA66, PBT,PET, PC/ABS, PC/PBT, PC/PET alloy compounds,TPE,TPU, PE for rotomolding with the property of the flame retardant, glass fiber reinforced, high glossy, UV resistance.....with the annual output value of USD 65 million in 2021. 

Our customers are Osram,Cree,,Siemens,etc. for years in the electrical&electronics components, Automotive parts, House appliance,LED lights.....