UV-stabilized. Good clarity, heat resistance, property retention and dimensional stability. | |||||
General | |||||
Form Resin Pellets | |||||
Feature | Outdoor Good Thermal |
High Clarity | Good Dimensional | ||
UL Yellow Card | E45587-236897 | ||||
Appliances Lighting Applications Automotive Under The | |||||
Uses |
Lenses | Electronic Displays A t ti E t i |
Lawn And Garden Equipment |
||
armaceu ca s | u omo ve x er or | u omo ve n er or | |||
Constraction | Household Applications | Outdoor | |||
Physical | Nominal Value | Test Method | |||
Density / Specific Gravity | 1.20 g/cm³ | ASTM D792 | |||
Melt Mass-Flow Rate, MFR(300 °C;1.2 kg) | 25 g/10min | ASTM D1238 | |||
Molding Shrinkage, Flow(3.2 mm) | 0.50 - 0.70 % | Internal Method | |||
Mechanical | Nominal Value | Test Method | |||
Tensile Strength, Yield(50 mm/min;Type I) | 62.0 MPa | ASTM D638 | |||
Tensile Strength, Break(50 mm/min;Type I) | 65.0 MPa | ASTM D638 | |||
Tensile Elongation, Break(50 mm/min;Type I) | 110 % | ASTM D638 | |||
Flexural Modulus(1.3 mm/min;50 mm;Span) | 2300 MPa | ASTM D790 | |||
Flexural Strength, Yield(1.3 mm/min;50 mm;Span) | 93.0 MPa | ASTM D790 | |||
Notched Izod Impact(23 °C) | 640 J/m | ASTM D256 | |||
Instrumented Dart Impact, Energy at Peak(23 °C) | 54.0 J | ASTM D3763 | |||
Tensile Impact Strength(Type S) | 378 kJ/m² | ASTM D1822 | |||
Thermal | Nominal Value | Test Method | |||
Deflection Temperature Under Load, Unannealed(1.8 MPa;6.4 mm) | 126 °C | ASTM D648 | |||
RTI Elec | 100 °C | UL 746 | |||
RTI Imp | 100 °C | UL 746 | |||
RTI Str | 100 °C | UL 746 | |||
Flame Rating(1.5 mm) | V-2 | UL 94 | |||
Optical | Nominal Value | Test Method | |||
Transmittance (2.5e+3 µm) | 88.0 % | ASTM D1003 | |||
Haze(2.5e+3 µm) | 1.00 % | ASTM D1003 | |||
Processing | Nominal Value | ||||
Drying Temperature<Injection> | 120 °C | ||||
Drying Time<Injection> | 3.0 - 4.0 hr | ||||
Suggested Max Moisture<Injection> | 0.020 % | ||||
Suggested Shot Size<Injection> | 40 - 60 % | ||||
Rear Temperature<Injection> | 250 - 270 °C | ||||
Middle Temperature<injection> | 260 - 280 °C | ||||
Front Temperature<Injection> | 270 - 295 °C | ||||
Nozzle Temperature<Injection> | 265 - 290 °C | ||||
Processing Temp, Melt<Injection> | 270 - 295 °C | ||||
Mold Temperature<Injection> | 70 - 95 °C | ||||
Back Pressure<Injection> | 0.300 - 0.700 MPa | ||||
Screw Speed <Injection> | 40 - 70 rpm | ||||
Vent Depth <Injection> | 0.025 - 0.076 mm | ||||
Drying Time, Cumulative<Injection> | 48 hrs |