Resin Plastic Raw Material Fr V0 Virgin Polyamide6 30GF/GF40/GF50 Granule Nylon 6 Pellet GF25 PA6 GF 30

• Feature: Oxidative Degradable
• Material: Polyamide(Nylon 6.66)/PA
• Usage: General Plastics, Engineering Plastics, Specialty Plastics
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Model NO.: KFHG6S
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Injection
• Color: White
• Form: Resin Pellets
• Chemical Substances: Nylon
• Processing Mode: Injection Molding/Extrusion
• UV: Fr
• Use: Electrical Appliances, Auto Parts, Office Supplies
• Certificates: ISO9001:2008.SGS.RoHS
• Filler: 30% Glass Fiber
• Transport Package: Bag
• Specification: 25KG
• Trademark: Forever
• Origin: China
• HS Code: 390740000
• Production Capacity: 50000t/Year

Product Description

Resin Plastic Raw Material Fr V0 Virgin Polyamide6 30GF/GF40/GF50 Granule Nylon 6 Pellet GF25 PA6 GF 30

30% Glass Reinforced, Heat Stabilized, Flame Retardant, High Flow

 

Product Description
30% Glass Reinforced, Heat Stabilized, Flame Retardant, High Flow
General
Form	Resin Pellets
Filler	30 % Glass Fiber
Physical		Nominal Value	Test Method
Density		1.59 g/cm³	dry;ISO 1183
Water Absorption		4.5 %	ISO 62
Moisture Absorption		1.30 %	ISO 62
Linear Mold Shrinkage, Flow		0.21 %	ISO 294-4
Linear Mold Shrinkage, Transverse		0.77 %	ISO 294
Mechanical		Nominal Value	Test Method
Tensile Strength, Ultimate			ISO 527-1/2
		100 MPa
		150 MPa
Elongation at Break			ISO 527-1/2
		2.5 %
		5.0 %
Tensile Modulus			ISO 527-1/2
		7030 MPa
		1.15E+4 MPa
Charpy Impact Unnotched			ISO 179 1eU
Temperature; 23 °C		59.8 kJ/m²
Temperature; -30 °C		59.8 kJ/m²
Temperature; 23 °C		59.8 kJ/m²
Temperature; -30 °C		59.8 kJ/m²
Charpy Impact, Notched			ISO 179 1eA
Temperature; -30 °C		12 kJ/m²
Temperature; -30 °C		12 kJ/m²
Temperature; 23 °C		13 kJ/m²
Temperature; 23 °C		15 kJ/m²

Thermal	Nominal Value	Test Method
CTE, Flow	20.0 µm/m-°C	ISO 11359-1/-2
CTE, linear, Transverse to Flow	110 µm/m-°C	dry;ISO 11359-1/- 2
Melting Point(10°C/min)	220 °C	ISO 11357-1/-3
Deflection Temperature Pressure; 0.46 MPa Pressure; 1.8 MPa	215 °C 205 °C	ISO 75-1/-2
Flammability, UL94 Thickness; 1.5 mm Thickness; 0.749 mm	V-0 V-0	IEC 60695-11-10
Electrical	Nominal Value	Test Method
Volume Resistivity	1.00e+13 ohms·cm 1.00e+15 ohms·cm	IEC 60093
Surface Resistance	1.00e+14 Ohms	IEC 60093
Dielectric Constant Frequency; 1000000 Hz Frequency; 100 Hz Frequency; 1000000 Hz Frequency; 100 Hz	3.4 3.5 4.0 10	IEC 60250
Dissipation Factor Frequency; 100 Hz Frequency; 1000000 Hz Frequency; 1000000 Hz Frequency; 100 Hz	0.0060 0.012 0.070 0.30	IEC 60250
Comparative Tracking Index	325 V

 

Processing	Nominal Value
Injection
Drying Temperature	80.0 °C
Drying Time	4.0 - 8.0 hr
Rear Temperature	230 - 250 °C
Middle Temperature	230 - 260 °C
Front Temperature	230 - 260 °C
Nozzle Temperature	250 - 280 °C
Melt Temperature	245 - 270 °C
Mold Temperature	40 - 80 °C
Injection Rate	Moderate-Fast
Back Pressure	3.00 - 10.0 MPa
Screw Compression Ratio	2.5:1.0

    

                                                                                                                  Forever Co.,Ltd

With almost 20 years in the modified engineering plastics,Forever Plastics is a high-tech manufacture integrating R&D, production and sales of high-performance resin or polymer ,including PC,PP,PA6,PA66, PBT,PET, PC/ABS, PC/PBT, PC/PET alloy compounds,TPE,TPU, PE for rotomolding with the property of the flame retardant, glass fiber reinforced, high glossy, UV resistance.....with the annual output value of USD 65 million in 2021. 

Our customers are Osram,Cree,,Siemens,etc. for years in the electrical&electronics components, Automotive parts, House appliance,LED lights.....