Feature: | Oxidative Degradable |
---|---|
CAS No.: | 32131-17-2 |
Formula: | (C12h22n2o2)N |
Samples: |
BAG
|
---|
Customization: |
---|
Shipping Cost:
Estimated freight per unit. |
about shipping cost and estimated delivery time. |
---|
Payment Method: | |
---|---|
Initial Payment Full Payment |
Currency: | US$ |
---|
Return&refunds: | You can apply for a refund up to 30 days after receipt of the products. |
---|
Suppliers with verified business licenses
PA66 housings of high stiffness and dimensional stability such as coil formers
https://forever-plastics.en.made-in-china.com/product/rJwRvlcdZpWD/China-Nylon-PA6-GF33-PA66-Granules-PA6-with-30GF-Polyamide-PA66-30-GF-PA6-Material.html Heat-conducting nylon
Product Description | |||||
A3WG6 is a 30% glass fiber reinforced and heat resistance injection molding PA66 grade for machinery components and housings of high stiffness and dimensional stability. Applications Typical applications include lamp socket housings, cooling fans, insulating profiles for aluminum window frames, water containers for automotive cooling systems. |
|||||
General | |||||
Form | Resin Pellets | ||||
Filler | 30 % Glass Fiber | ||||
Feature | Good Thermal Fuel Resistant | Good Dimensional Ec 1907/2006 (Reach) |
Good Hardness | ||
UL Yellow Card | E41871-101468834 | ||||
Uses | Profiles Containers |
Automotive Mechanical Parts |
Housing | ||
Physical | Nominal Value | Test Method | |||
Density, dry | 1.36 g/cm³ | ASTM D792 ISO 1183 |
|||
Dry: Melt Volume-Flow Rate, MVR(275 °C;5 kg) | 40 cm³/10 min | ISO 1133 | |||
Dry: Molding Shrinkage - Flow(3.18 mm) | 0.30 % | No Standard | |||
Dry: Water Absorption, Saturation | 5.5 % | ASTM D570 | |||
23 °C | 5.5 % | ISO 62 | |||
Dry: Water Absorption, Equilibrium | |||||
50% RH | 1.7 % | ASTM D570 | |||
50% RH;23 °C | 1.7 % | ISO 62 | |||
Mechanical | Nominal Value | Test Method | |||
Dry: Tensile Modulus(23 °C) | 10000 MPa | ISO 527-2 | |||
Condition: Tensile Modulus(23 °C) | 7200 MPa | ISO 527-2 | |||
Dry: Tensile Strength, Break 23 °C 23 °C 120 °C |
186 MPa 190 MPa 93.0 MPa |
ASTM D638 ISO 527-2 ISO 527-2 |
|||
Condition: Tensile Strength, Break 23 °C 120 °C |
130 MPa 74.0 MPa |
ISO 527-2 | |||
Dry: Tensile Elongation, Break 23 °C 23 °C 120 °C |
3.0 % 3.0 % 7.4 % |
ASTM D638 ISO 527-2 ISO 527-2 |
|||
Condition: Tensile Elongation, Break 23 °C 120 °C |
5.0 % 6.4 % |
ISO 527-2 | |||
Dry: Flexural Modulus 23 °C 23 °C |
8480 MPa 8600 MPa |
ASTM D790 ISO 178 |
|||
Dry: Charpy Notched Impact Strength -30 °C 23 °C |
11 kJ/m² 13 kJ/m² |
ISO 179 | |||
Condition: Charpy Notched Impact Strength(23 °C) | 22 kJ/m² | ISO 179 | |||
Dry: Charpy Unnotched Impact Strength -30 °C 23 °C |
70 kJ/m² 85 kJ/m² |
ISO 179 | |||
Condition: Charpy Unnotched Impact Strength(23 °C) | 100 kJ/m² | ISO 179 | |||
Dry: Notched Izod Impact -40 °C 23 °C 23 °C |
91 J/m 110 J/m 12 kJ/m² |
ASTM D256 ASTM D256 ISO 180 |
|||
Thermal | Nominal Value | Test Method | |||
Dry: Deflection Temperature Under Load, Unannealed 0.45 MPa 1.8 MPa |
250 °C 250 °C |
ISO 75-2/B;ASTM D648 ISO 75-2/A;ASTM D648 |
|||
Dry: Peak Melting Temperature | 260 °C | ASTM D3418;ISO 3146 | |||
Dry: CLTE, Flow | 1.0E-5 cm/cm/°C 2.5E-5 cm/cm/°C |
ASTM E831 No Standard |
|||
Dry: CLTE, Transverse | 6.5E-5 cm/cm/°C | No Standard | |||
Dry: RTI Elec 0.71 mm 1.5 mm 3 mm |
125 °C 125 °C 125 °C |
UL 746 | |||
Dry: RTI Imp 1.5 mm 3 mm |
115 °C 120 °C |
UL 746 | |||
Dry: RTI Str 1.5 mm 3 mm |
115 °C 130 °C |
UL 746 | |||
Dry: Flame Rating 0.71 mm 1.5 mm 3 mm |
HB HB HB |
UL 94 | |||
Electrical Nominal Value Test Method | |||||
Dry: Volume Resistivity | |||||
1.5 mm 1.0e+15 ohms ·cm ASTM D257 | |||||
1.0e+15 ohms ·cm IEC 60093 | |||||
Condition: Volume resistivity | |||||
1.5 mm 1.0E+12 ohms ·cm ASTM D257 | |||||
1.0E+12 ohms ·cm IEC 60093 | |||||
Dry: Dielectric Constant(1.0e+6 Hz) 3.50 IEC 60250 | |||||
Condition: Dielectric Constant(1.0e+6 Hz) 5.60 IEC 60250 | |||||
Dry: Dissipation Factor IEC 60250 | |||||
100 Hz 0.014 | |||||
1.0e+6 Hz 0.014 | |||||
Condition: Dissipation factor IEC 60250 | |||||
100 Hz 0.23 | |||||
1.0e+6 Hz 0.30 | |||||
Dry: Comparative Tracking Index 450 V IEC 60112 | |||||
Condition: Comparative Tracking Index 450 V IEC 60112 | |||||
Processing Nominal Value | |||||
Drying Temperature<Injection> 80 °C | |||||
Drying Time<Injection> 2.0 - 4.0 hr | |||||
Suggested Max Moisture<Injection> 0.12 % | |||||
Processing Temp, Melt<Injection> 280 - 305 °C | |||||
Mold Temperature<Injection> 80 - 90 °C | |||||
Injection Pressure<Injection> 3.50 - 12.5 MPa | |||||
Injection Rate<Injection> Fast |