33% Glass Reinforced Heat Stabilized Polyamide 66 Automotive Specifications

• Feature: Oxidative Degradable
• CAS No.: 32131-17-2
• Formula: (C12h22n2o2)N
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Model NO.: PA66-70G33HS1L BK
• EINECS: 211-024-8
• Material: Polyamide(Nylon 6.66)/PA
• Usage: General Plastics, Engineering Plastics, Specialty Plastics
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Injection
• Color: Black
• Form: Resin Pellets
• Chemical Substances: Nylon
• Processing Mode: Injection Molding/Extrusion
• UV: Fr
• Use: Electrical Appliances, Auto Parts, Office Supplies
• Certificates: ISO9001:2008.SGS.RoHS
• Filler: 10%-50% Glass Fiber
• Transport Package: Bag
• Specification: 25KG
• Trademark: Forever
• Origin: China
• HS Code: 390740000
• Production Capacity: 50000t/Year
• Package Size: 75.00cm * 55.00cm * 15.00cm
• Package Gross Weight: 25.010kg

Product Description

33% Glass Reinforced Heat Stabilized Polyamide 66 Automotive Specifications
 Heat-conducting nylon

Product Description

Product Description
33% Glass Reinforced, Heat Stabilized, Polyamide 66. Automotive Specifications : ASTM D4066 PA012 G35 , ASTM D6779 PA012G35 ,CHRYSLER MS-DB-41 CPN1900 , DELPHI 7826921 , DELPHI DX300293 , DELPHI M- 53103 , DELPHI M-5543 , FORD ESE-M4D287-A , FORD ESE-M4D287-B , FORD ESE-M4D287-B Color: Black , FORD WSK-M4D663-A , FORD WSS-M4D673-B1 ,GM GMP.PA66.013 ,GM GMW3038P-PA66-GF35H , PSA    Peugeot-Citroë n SPA X62 4100.
General
Form		Resin Pellets
Filler		33 % Glass Fiber
Feature		Good Thermal
UL Yellow Card                         E41938-234409
Physical			Nominal Value				Test Method
Density, dry			1.39 g/cm³				ISO 1183
Dry: Molding Shrinkage, Across Flow			1.1 %				ISO 294-4
Dry: Molding Shrinkage, Flow			0.30 %				ISO 294-4
Dry: Water Absorption, Saturation(23 °C;2 mm)			5.7 %				ISO 62
Dry: Water Absorption, Equilibrium(50% RH;23 °C;2			mm) 1.8 %				ISO 62
Dry: Fogging - G-value, condensate			6.0E-4 g				ISO 6452
Dry: Emission of Organic Compounds			10.0 µgC/g				VDA 277
Dry: Odor			3.00				VDA 270
Mechanical				Nominal Value		Test Method
Dry: Tensile Modulus				11000 MPa		ISO 527-2
Condition: Tensile Modulus				8000 MPa		ISO 527-2
Dry: Tensile Stress, Break				200 MPa		ISO 527-2
Condition: Tensile Stress, Break				140 MPa		ISO 527-2
Dry: Tensile Strain, Break				3.0 %		ISO 527-2
Condition: Tensile Strain, Break				5.4 %		ISO 527-2
Dry: Flexural Modulus				9500 MPa		ISO 178
Condition: Flexural Modulus				6000 MPa		ISO 178
Dry: Flexural Stress				280 MPa		ISO 178
Condition: Flexural Stress				195 MPa		ISO 178
Dry: Charpy Notched Impact Strength -40 °C 23 °C				10 kJ/m² 13 kJ/m²		ISO 179 1eA
Condition: Charpy Notched Impact Strength -40 °C 23 °C				10 kJ/m² 17 kJ/m²		ISO 179 1eA
Dry: Charpy Unnotched Impact Strength(23 °C)				75 kJ/m²		ISO 179 1eU
Condition: Charpy Unnotched Impact Strength(23 °C)				80 kJ/m²		ISO 179 1eU
Dry: Notched Izod Impact Strength -40 °C 23 °C				10 kJ/m² 12 kJ/m²		ISO 180/1A
Notched Izod Impact Strength: condition -40 °C 23 °C				10 kJ/m² 15 kJ/m²			ISO 180/1A
Thermal				Nominal Value			Test Method
Dry: Heat Deflection Temperature, Unannealed 0.45 MPa 1.8 MPa				261 °C 252 °C			ISO 75-2/B ISO 75-2/A
Dry: Melting Temperature(10 °C;min)				262 °C			ISO 11357-3
Dry: CLTE, Flow -40 - 23 °C 55 - 160 °C				1.8E-5 cm/cm/°C 2.4E-5 cm/cm/°C 1.3E-5 cm/cm/°C			ISO 11359-2
Dry: CLTE, Transverse -40 - 23 °C 55 - 160 °C				8.3E-5 cm/cm/°C 6.5E-5 cm/cm/°C 1.4E-4 cm/cm/°C			ISO 11359-2
Dry: Burning rate(1 mm;FMVSS 302)				28 mm/min			ISO 3795
Dry: Flame Rating 0.75 mm 1.5 mm				HB HB			UL 94;IEC 60695- 11-10;-20
Dry: FMVSS Flammability				B			FMVSS 302
Electrical				Nominal Value			Test Method
Dry: Comparative Tracking Index[CTI]				PLC 1			UL 746
Dry: Comparative Tracking Index				400 V			IEC 60112
Processing					Nominal Value
Drying Temperature<Injection>					80 °C
Drying Time - Desiccant Dryer<Injection>					2.0 - 4.0 hr
Suggested Max Moisture<Injection>					0.20 %
Processing Temp, Melt<Injection>					275 - 295 °C
Melt Temperature, Optimum<Injection>					285 °C
Mold Temperature<Injection>					70 - 120 °C
Mold Temperature, Optimum<Injection>					100 °C
Holding Pressure<Injection>					50.0 - 100 MPa
Drying Recommended <Injection>					YES
Hold Pressure Time<Injection>					3.00 s/mm
Maximum Screw Tangential Speed <Injection>					12 m/min
Dry: Ejection Temperature					210 °C

 

 

                                                                                                                  Forever Co.,Ltd

 

With almost 20 years in the modified engineering plastics,Forever Plastics is a high-tech manufacture integrating R&D, production and sales of high-performance resin or polymer ,including PC,PP,PA6,PA66, PBT,PET, PC/ABS, PC/PBT, PC/PET alloy compounds,TPE,TPU, PE for rotomolding with the property of the flame retardant, glass fiber reinforced, high glossy, UV resistance.....with the annual output value of USD 65 million in 2021. 

Our customers are Osram,Cree,,Siemens,etc. for years in the electrical&electronics components, Automotive parts, House appliance,LED lights.....