| Customization: | Available |
|---|---|
| Feature: | Plastics |
| CAS No.: | 25766-59-0 |
|
Still deciding? Get samples of US$ 1/kg
Order Sample
|
| Shipping Cost: | Contact the supplier about freight and estimated delivery time. |
|---|
| Payment methods: |
|
|---|---|
| Support payment in USD |
| Secure payments: | Every payment you make at Made-in-china.com is protected by the platform. |
|---|
| Refund policy: | Claim a refund if your order doesn't ship, is missing, or arrives with product issues. |
|---|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
| Product Description | |||||||
| MVR (330°C/2.16kg) 10 cm³/10 min; high viscosity; UV stabilized; 'softening temperature (VST/B 120) =184°C; injection molding - melt temperature 330 - 340°C; Covers for brake lights and indicator lights; car interior light covers; Domestic lamp covers; Headlamp lenses; Covers for ships' lights; Connector pieces for halogen systems | |||||||
| General | |||||||
| Form | Resin Pellets | ||||||
| Feature | Anti-Static | Outdoor | High Viscosity | ||||
| UL Yellow Card E41613-233131 | |||||||
| Uses | Automotive Backlights Connector |
Lighting Applications Automotive | |||||
| Physical | Nominal Value | Test Method | |||||
| Density / Specific Gravity(23 °C) | 1.15 g/cm³ | ISO 1183 | |||||
| Melt Mass-Flow Rate, MFR(2.16 kg;330 °C) | 10 g/10min | ISO 1133 | |||||
| Melt Volume-Flow Rate, MVR(2.16 kg;330 °C) | 10 cm³/10 min | ISO 1133 | |||||
| Molding Shrinkage, Across Flow(2 mm;60x60x2mm) | 0.85 % | ISO 294-4 | |||||
| Molding Shrinkage, Flow(2 mm;60x60x2mm) | 0.85 % | ISO 294-4 | |||||
| Water Absorption, Saturation(23 °C) | 0.30 % | ISO 62 | |||||
| Water Absorption, Equilibrium(50% RH;23 °C) | 0.12 % | ISO 62 | |||||
| Ball Indentation Hardness | 121 MPa | ISO 2039-1 | |||||
| Mechanical | Nominal Value | Test Method | |||||
| Tensile Modulus(23 °C) | 2400 MPa | ISO 527-2/1 | |||||
| Tensile Stress, Yield(23 °C) | 72.0 MPa | ISO 527-2/50 | |||||
| Tensile Strain, Yield(23 °C) | 6.8 % | ISO 527-2/50 | |||||
| Nominal Tensile Strain at Break(23 °C) | > 50 % | ISO 527-2/50 | |||||
| Flexural Modulus(2 mm/min;23 °C) | 2400 MPa | ISO 178 | |||||
| Flexural Stress(2 mm/min;23 °C) | 108 MPa | ISO 178 | |||||
| C harpy Unnotched Impact Strength | ISO 179 1eU | ||||||
| -30 °C | No Break | ||||||
| 23 °C | No Break | ||||||
| Thermal | Nominal Value | Test Method | |||||
| Heat Deflection Temperature, Unannealed 0.45 MPa 1.8 MPa |
174 °C 159 °C |
ISO 75-2/B ISO 75-2/A |
|||||
| Vicat Softening Temperature | 184 °C | ISO 306/B120 | |||||
| CLTE, Flow(23 - 55 °C) | 6.5E-5 cm/cm/°C | ISO 11359-2 | |||||
| CLTE, Transverse(23 - 55 °C) | 6.5E-5 cm/cm/°C | ISO 11359-2 | |||||
| RTI Elec | 150 °C | UL 746 | |||||
| RTI Imp | 130 °C | UL 746 | |||||
| RTI Str | 150 °C | UL 746 | |||||
| Flame Rating(1.5 mm) | HB | UL 94 | |||||
| Glow Wire Flammability Index | 850 °C | IEC 60695-2-12 | |||||
| Oxygen Index, Procedure A | 25 % | ISO 4589-2 | |||||
| Electrical | Nominal Value | Test Method | |||||
| Surface Resistivity | 1.0E+16 ohms | IEC 60093 | |||||
| Volume Resistivity(23 °C) | 1.0E+17 ohms ·cm | IEC 60093 | |||||
| Electric Strength(23 °C;1 mm) | 35 kV/mm | IEC 60243-1 | |||||
| Relative Permittivity 100 Hz;23 °C 23 °C;1.0e+6 Hz |
2.90 2.80 |
IEC 60250 | |||||
| Dissipation Factor 100 Hz;23 °C 23 °C;1.0e+6 Hz |
1.0E-3 8.0E-3 |
IEC 60250 | |||||
| Comparative Tracking Index, Solution A | 450 V | IEC 60112 | |||||
| Comparative Tracking Index, Solution B | 100 V | IEC 60112 | |||||
| Optical | Nominal Value | Test Method | |||||
| Refractive Index, Method A | 1.573 | ISO 489 | |||||
| Transmittance (1.0e+3 µm) | 89.0 % | ISO 13468-2 | |||||
| Chemical | Nominal Value | Test Method | |||||
| Electrolytical Corrosion(23 °C) | A1 | IEC 60426 | |||||
| Processing | Nominal Value | ||||||
| Drying Temperature - Dry Air Dryer<Injection> | 130 °C | ||||||
| Drying Time - Dry Air Dryer<Injection> | 2.0 - 4.0 hr | ||||||
| Suggested Max Moisture<Injection> | < 0.020 % | ||||||
| Suggested Shot Size<Injection> | 30 - 70 % | ||||||
| Rear Temperature<Injection> | 315 - 325 °C | ||||||
| Middle Temperature<injection> | 320 - 330 °C | ||||||
| Front Temperature<Injection> | 325 - 335 °C | ||||||
| Nozzle Temperature<Injection> | 315 - 340 °C | ||||||
| Processing Temp, Melt<Injection> | 320 - 340 °C | ||||||
| Mold Temperature<Injection> | 100 - 140 °C | ||||||
| Back Pressure<Injection> | 10.0 - 20.0 MPa | ||||||
| Vent Depth <Injection> | 0.025 - 0.050 mm | ||||||