Lds Laser Direct Structuring Improved Impact Resin Pellets Laser Markable Polycarbonate

• Feature: Plastics
• CAS No.: 25766-59-0
• Formula: C6h4c(CH3)2c6h4oco2-]N
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Model NO.: PC-3724
• EINECS: 618-371-8
• Material: Polycarbonates/PC
• Usage: General Plastics, Engineering Plastics, Specialty Plastics
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Injection
• Color: Black
• Form: Resin Pellets
• Chemical Substances: Polycarbonate
• Processing Mode: Injection Molding/Extrusion
• UV: Fr
• Use: Electrical Appliances, Auto Parts, Office Supplies
• Certificates: ISO9001:2008.SGS.RoHS
• Filler: 10%-50% Glass Fiber
• Transport Package: Bag
• Specification: 25KG
• Trademark: Forever
• Origin: China
• HS Code: 390740000
• Production Capacity: 50000t/Year
• Package Size: 75.00cm * 55.00cm * 15.00cm
• Package Gross Weight: 25.010kg

Product Description

LDS Laser Direct Structuring Improved Impact Resin Pellets  Laser Markable polycarbonate

Product Description

LDS (Laser Direct Structuring), Improved Impact
General
Form	Resin Pellets
Feature	Lds	Ductile		Laser Markable
UL Yellow Card                         E340159-101357462
Uses                                          Laser Direct Structuring			Cell Phone Cases
Physical			Nominal Value	Test Method
Density / Specific Gravity			1.23 g/cm³	ISO 1183
Melt Mass-Flow Rate, MFR(260 °C;5 kg)			14 g/10min	ISO 1133
Melt Volume-Flow Rate, MVR(260 °C;5 kg)			14 cm³/10 min	ISO 1133
Molding Shrinkage, Across Flow			0.50 - 0.70 %	Internal Method
Molding Shrinkage, Flow			0.50 - 0.70 %	Internal Method
Mechanical			Nominal Value	Test Method
Tensile Modulus			2250 MPa	ISO 527-2/1
Tensile Stress, Yield			49.0 MPa	ISO 527-2/50
Tensile Strain, Yield			4.0 %	ISO 527-2/50
Tensile Strain, Break			> 50 %	ISO 527-2/50
Flexural Modulus(2 mm/min)			2200 MPa	ISO 178
Flexural Stress(2 mm/min)			77.0 MPa	ISO 178
C harpy Unnotched Impact Strength -30 °C 23 °C			No Break No Break	ISO 179
Notched Izod Impact Strength -20 °C 23 °C			40 kJ/m² 55 kJ/m²	ISO 180/4A
Multi-Axial Instrumented Impact Energy(23 °C)			35.0 J	ISO 6603-2
Thermal			Nominal Value	Test Method
Heat Deflection Temperature, Unannealed(1.8 MPa)			100 °C	ISO 75-2/A
Vicat Softening Temperature			122 °C	ISO 306
CLTE, Flow			7.0E-5 cm/cm/°C	ISO 11359-2
CLTE, Transverse			7.0E-5 cm/cm/°C	ISO 11359-2
Electrical			Nominal Value	Test Method
Surface Resistivity			> 1.0E+15 Ohms	IEC 60093
Volume Resistivity			> 1.0E+15 Ohms ·cm	IEC 60093
Dielectric Constant(1.0e+6 Hz)			3.00	IEC 60250
Dissipation Factor(1.0e+6 Hz)			6.0E-3	IEC 60250
Processing				Nominal Value
Drying Temperature - Hot Air Dryer<Injection>				100 - 110 °C
Drying Time - Hot Air Dryer<Injection>				4.0 - 6.0 hr
Rear Temperature<Injection>				260 - 280 °C
Middle Temperature<injection>				260 - 280 °C
Front Temperature<Injection>				260 - 280 °C
Nozzle Temperature<Injection>				250 - 270 °C
Mold Temperature<Injection>				40 - 80 °C

                                                                                                                  Forever Co.,Ltd

 

With almost 20 years in the modified engineering plastics,Forever Plastics is a high-tech manufacture integrating R&D, production and sales of high-performance resin or polymer ,including PC,PP,PA6,PA66, PBT,PET, PC/ABS, PC/PBT, PC/PET alloy compounds,TPE,TPU, PE for rotomolding with the property of the flame retardant, glass fiber reinforced, high glossy, UV resistance.....with the annual output value of USD 65 million in 2021. 

Our customers are Osram,Cree,,Siemens,etc. for years in the electrical&electronics components, Automotive parts, House appliance,LED lights.....