Polyamine Nylon 66 Is 45% Carbon/Glass Reinforced Heat Stabilized Polyamide 66

• Feature: Oxidative Degradable
• CAS No.: 32131-17-2
• Formula: (C12h22n2o2)N
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Model NO.: PA66-75CG45HSL BK409
• EINECS: 211-024-8
• Material: Polyamide(Nylon 6.66)/PA
• Usage: General Plastics, Engineering Plastics, Specialty Plastics
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Injection
• Color: Black
• Form: Resin Pellets
• Chemical Substances: Nylon
• Processing Mode: Injection Molding/Extrusion
• UV: Fr
• Use: Electrical Appliances, Auto Parts, Office Supplies
• Certificates: ISO9001:2008.SGS.RoHS
• Filler: 10%-60% Glass Fiber
• Transport Package: Bag
• Specification: 25KG
• Trademark: Forever
• Origin: China
• HS Code: 390740000
• Production Capacity: 50000t/Year
• Package Size: 75.00cm * 55.00cm * 15.00cm
• Package Gross Weight: 25.010kg

Product Description

Polyamine Nylon 66 is 45% Carbon/Glass Reinforced Heat Stabilized Polyamide 66
 Heat-conducting nylon

Product Description

Product Description
75CG45HSL BK409 is a 45% Carbon/Glass Reinforced, Heat Stabilized, Polyamide 66.
General
Form                                        Resin Pellets
Filler	45 % Carbon Fiber/Glass   Fiber
Feature                                     Good Thermal
Physical                                                                                 Nominal Value                                       Test Method
Dry: Moulding shrinkage, parallel                                       0.2 %			ISO 294-4, ISO 2577
Dry: Moulding shrinkage, normal                                       0.6 %			ISO 294-4, ISO 2577
Density, dry                                                                           1.42 g/cm³                                              ISO 1183
Mechanical                                                                            Nominal Value                                      Test Method
Dry: Tensile Modulus                                                           17500 MPa                                             ISO 527-1/-2
Dry: Stress at break                                                               175 MPa                                                 ISO 527-1/-2
Dry: Strain at break                                                               2.9 %                                                       ISO 527-1/-2
Dry: Flexural Modulus                                                          15500 MPa                                              ISO 178
Dry: Flexural Strength                                                          300 MPa                                                  ISO 178
Dry: Charpy Impact Strength(Temperature; 23 °C)             80 kJ/m²                                                 ISO 179 1eU
Dry: Charpy Notched Impact Strength                                                                                               ISO 179 1eA
Temperature; 23 °C                                                            15 kJ/m²
Temperature; -40 °C                                                           19 kJ/m²
Thermal                                                                                 Nominal Value                                      Test Method
Dry: Melting Temperature(18° F/min)                                 256 °C                                                     ISO 11357-1/-3
Dry: Temp. of deflection under load                                                                                                  ISO 75-1/-2
Load; 1.82 MPa                                                                    218 °C
Load; 0.45 MPa                                                                    238 °C
FMVSS Class		B
Burning rate(1 mm)		< 100 mm/min
Electrical		Nominal Value	Test Method
Dry: Volume resistivity, conductive plastics		3 ohms ·cm	ASTM D4496
Processing		Nominal Value
Injection
Drying Recommended		YES
Drying Temperature		80 °C
Drying Time, Dehumidified Dryer		2 - 4 h
Processing Moisture Content		< = 0.02 %
Melt Temperature Optimum		290 °C
Min. melt temperature		280 °C
Max. melt temperature		305 °C
Max. screw tangential speed		0.2 m/s
Mold Temperature Optimum		100 °C
Min. mold temperature		70 °C
Max. mould temperature		120 °C
Hold pressure range		50 - 100 MPa
Hold pressure time		3 s/mm
Ejection Temperature		210 °C

 

 

                                                                                                                  Forever Co.,Ltd

 

With almost 20 years in the modified engineering plastics,Forever Plastics is a high-tech manufacture integrating R&D, production and sales of high-performance resin or polymer ,including PC,PP,PA6,PA66, PBT,PET, PC/ABS, PC/PBT, PC/PET alloy compounds,TPE,TPU, PE for rotomolding with the property of the flame retardant, glass fiber reinforced, high glossy, UV resistance.....with the annual output value of USD 65 million in 2021. 

Our customers are Osram,Cree,,Siemens,etc. for years in the electrical&electronics components, Automotive parts, House appliance,LED lights.....