| Customization: | Available |
|---|---|
| Feature: | Plastics |
| CAS No.: | 25766-59-0 |
|
Still deciding? Get samples of US$ 1/kg
Order Sample
|
| Shipping Cost: | Contact the supplier about freight and estimated delivery time. |
|---|
| Payment methods: |
|
|---|---|
| Support payment in USD |
| Secure payments: | Every payment you make at Made-in-china.com is protected by the platform. |
|---|
| Refund policy: | Claim a refund if your order doesn't ship, is missing, or arrives with product issues. |
|---|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
High Gloss Rigidity Good Tensilea ABS Lamp Clock Cases and Home Appliance Buttons
https://forever-plastics.en.made-in-china.com/product-list-1.html
| Product Description | |||||
| Features: High Gloss; Ultra High Rigidity; Good Tensile Strength Applications: Phone Cases; Lamp Holders; Toys; Office Supplies; Clock Cases and Home Appliance Buttons High Stiffness | |||||
| General | |||||
| Form | Resin Pellets | ||||
| Feature |
High Mechanical Strength | High Reflection Good Stretchability |
Good Hardness | ||
| And Rigidity | |||||
| Household electric | |||||
| Uses | |||||
| Electrical applications | Office supplies | Telephone | |||
| Physical | Nominal Value | Test Method | |||
| Density / Specific Gravity(23 °C) | 1.06 g/cm³ | ISO 1183 | |||
| Melt Volume-Flow Rate, MVR(220 °C;10 kg) | 20 cm³/10 min | ISO 1133 | |||
| Molding Shrinkage | 0.40 - 0.70 % | ISO 294-4 | |||
| Mechanical | Nominal Value | Test Method | |||
| Tensile Strength, Yield(50 mm/min) | 50.0 MPa | ISO 527-2/50 | |||
| Tensile Strength, Break(50 mm/min) | 36.0 MPa | ISO 527-2/50 | |||
| Tensile Elongation, Break(50 mm/min) | 60 % | ISO 527-2/50 | |||
| Flexural Modulus(2 mm/min) | 2300 MPa | ISO 178 | |||
| Flexural Strength(2 mm/min) | 79.0 MPa | ISO 178 | |||
| C harpy Notched Impact Strength | ISO 179 | ||||
| -30 °C | 8.0 kJ/m² | ||||
| 23 °C | 14 kJ/m² | ||||
| Notched Izod Impact | ISO 180/1A | ||||
| -30 °C | 7.0 kJ/m² | ||||
| 23 °C | 13 kJ/m² | ||||
| Thermal Nominal Value | Test Method | ||||
| Deflection Temperature Under Load, Unannealed(1.8 MPa) | 83.0 °C | ISO 75-2/A | |||
| Deflection Temperature Under Load, Annealed(1.8 MPa) | 98.0 °C | ISO 75-2/A | |||
| Vicat Softening Temperature | |||||
| 5 kg;50 ºC/hr | 100 °C | ISO 306/B50 | |||
| 50 ºC/hr;1 kg | 104 °C | ISO 306/A50 | |||
| CLTE, Flow | 8.4E-5 | ISO 11359-2 | |||
| Flame Rating(1.5 mm) | HB | UL 94 | |||
| Processing | Nominal Value | ||||
| Drying Temperature<Injection> | 80 - 85 °C | ||||
| Drying Time<Injection> | 2.0 - 4.0 hr | ||||
| Rear Temperature<Injection> | 180 - 220 °C | ||||
| Middle Temperature<injection> | 190 - 230 °C | ||||
| Front Temperature<Injection> | 190 - 230 °C | ||||
| Mold Temperature<Injection> | 30 - 70 °C | ||||