Good Flow Resin Pellets PA4t 30% Glass Reinforcedfor Electrical Applications

• Feature: Oxidative Degradable
• CAS No.: 32131-17-2
• Formula: (C12h22n2o2)N
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Model NO.: PA4T-K11
• EINECS: 211-024-8
• Material: Polyamide(Nylon 6.66)/PA
• Usage: General Plastics, Engineering Plastics, Specialty Plastics
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Injection
• Color: Black
• Form: Resin Pellets
• Chemical Substances: Nylon
• Processing Mode: Injection Molding/Extrusion
• UV: Fr
• Use: Electrical Appliances, Auto Parts, Office Supplies
• Certificates: ISO9001:2008.SGS.RoHS
• Filler: 5%-60% Glass Fiber
• Transport Package: Bag
• Specification: 25KG
• Trademark: Forever
• Origin: China
• HS Code: 390740000
• Production Capacity: 50000t/Year
• Package Size: 75.00cm * 55.00cm * 15.00cm
• Package Gross Weight: 25.010kg

Product Description

 Good Flow  Resin Pellets PA4T 30% Glass Reinforcedfor Electrical  applications
 Heat-conducting nylon

Product Description

Product Description
30% Glass Reinforced, PA4T, for E&E applications, Good Flow
General
Form	Resin Pellets
Filler	30 % Glass Fiber
Feature	Excellent Processability
UL Yellow Card                         E47960-100921605
Uses	Electrical
Physical		Nominal Value	Test Method
Density, dry		1.43 g/cm³	ISO 1183
Dry: Molding	Shrinkage, Across Flow	1.3 %	ISO 294-4
Dry: Molding	Shrinkage, Flow	0.40 %	ISO 294-4
Dry: Water Absorption, Equilibrium(50% RH;23 °C)		2.1 %	ISO 62
Mechanical		Nominal Value	Test Method
Dry: Tensile Modulus 120 °C 160 °C 200 °C		11000 MPa 8000 MPa 5000 MPa 5000 MPa	ISO 527-2
Dry: Tensile Stress, Break 120 °C 160 °C 200 °C		180 MPa 130 MPa 90.0 MPa 75.0 MPa	ISO 527-2
Dry: Tensile Strain, Break 120 °C 160 °C 200 °C		2.0 % 2.8 % 4.6 % 5.8 %	ISO 527-2
Dry: Flexural Modulus 160 °C 200 °C		10000 MPa 5000 MPa 4000 MPa	ISO 178
Dry: Flexural Stress		290 MPa	ISO 178
Dry: Charpy Notched Impact Strength(23 °C)		10 kJ/m²	ISO 179 1eA
Dry: Charpy Unnotched Impact Strength(23 °C)		55 kJ/m²	ISO 179 1eU
Thermal		Nominal Value	Test Method
Dry: Heat Deflection Temperature, Unannealed(1.8 MPa)		305 °C	ISO 75-2/A
Dry: Melting Temperature(10 °C/min)		325 °C	ISO 11357-3
Dry: CLTE, Flow		3.0E-5 cm/cm/°C	ASTM D696
Dry: CLTE, Transverse		5.0E-5 cm/cm/°C	ASTM D696
Dry: Thermal Index - 5000 hr		174 °C	IEC 60216
Dry: Flammability Classification 0.8 mm 1.5 mm		HB HB	IEC 60695-11-10, - 20
Electrical		Nominal Value	Test Method
Dry: Volume Resistivity		> 1.0E+15 Ohms ·cm	IEC 60093
Condition: Volume resistivity		> 1.0E+15 Ohms ·cm	IEC 60093
Dry: Electric Strength		33 kV/mm	IEC 60243-1
Condition: Electric Strength		33 kV/mm	IEC 60243-1
Dry: Relative permittivity 100 Hz 1.0e+6 Hz 1.0e+9 Hz 1.0e+10 Hz		5.00 4.50 3.90 3.80	IEC 60250
Condition: Relative Permittivity 100 Hz 1.0e+6 Hz 1.0e+9 Hz 1.0e+10 Hz		5.00 4.50 4.00 3.90	IEC 60250
Dry: Comparative Tracking Index		600 V	IEC 60112
Condition: Comparative Tracking Index		600 V	IEC 60112

                                                                                                                  Forever Co.,Ltd

 

With almost 20 years in the modified engineering plastics,Forever Plastics is a high-tech manufacture integrating R&D, production and sales of high-performance resin or polymer ,including PC,PP,PA6,PA66, PBT,PET, PC/ABS, PC/PBT, PC/PET alloy compounds,TPE,TPU, PE for rotomolding with the property of the flame retardant, glass fiber reinforced, high glossy, UV resistance.....with the annual output value of USD 65 million in 2021. 