Product Description | ||||
LNP THERMOCOMP MF004AS compound is based on Polypropylene (PP) resin containing 20% glass fiber. Added features of this grade include: Heat Stabilized. | ||||
General | ||||
Form | Resin Pellets | |||
Filler | 20 % Glass Fiber | |||
Feature | Good Thermal Good Hardness | Structural | ||
UL Yellow Card | E121562-101284109 | |||
Uses Consumer | Electrical | |||
Physical | Nominal Value | Test Method | ||
Density / Specific Gravity | 1.034 g/cm³ 1.03 g/cm³ |
ASTM D792 ISO 1183 |
||
Moisture Absorption(23 °C;50% RH/24 hrs) | 0.03 % | ASTM D570 | ||
Mold Shrinkage, Flow | ||||
24 hrs | 0.4 - 0.7 % | ASTM D955 | ||
24 hrs | 0.72 % | ISO 294 | ||
Mold Shrinkage, XFlow | ||||
24 hrs | 0.9 - 1 % | ASTM D955 | ||
24 hrs | 0.95 % | ISO 294 | ||
Mechanical | Nominal Value | Test Method | ||
Izod Impact, Unnotched | ||||
23 °C | 325 J/m | ASTM D4812 | ||
80*10*4;23 °C | 20 kJ/m² | ISO 180/1U | ||
Izod Impact, Notched | ||||
23 °C | 48 J/m | ASTM D256 | ||
80*10*4;23 °C | 5 kJ/m² | ISO 180/1A | ||
Instrumented Dart Impact, Energy at Peak(23 °C) | 8 J | ASTM D3763 | ||
Multiaxial Impact | 1 J | ISO 6603 | ||
Tensile Stress, Break | ||||
63 MPa | ASTM D638 | |||
65 MPa | ISO 527 | |||
Tensile Strain, Break | ||||
2.3 % | ASTM D638 | |||
2.2 % | ISO 527 | |||
Tensile Modulus | ||||
50 mm/min | 4550 MPa | ASTM D638 | ||
1 mm/min | 5100 MPa | ISO 527 | ||
Flexural Stress | ||||
92 MPa | ASTM D790 | |||
104 MPa | ISO 178 | |||
Flexural Modulus | ||||
4340 MPa | ASTM D790 | |||
5600 MPa | ISO 178 |
Thermal | Nominal Value | Test Method |
UL Recognized(≥ 0.75 mm) | HB | UL 94 |
Heat Deflection Temperature[HDT], Unannealed 0.45 MPa;3.2 mm 3.2 mm;1.82 MPa |
160 °C 149 °C |
ASTM D648 |
CTE, XFlow -40 - 40 °C -40 - 40 °C |
7.4E-05 1/°C 7.4E-05 1/°C |
ASTM E831 ISO 11359-2 |
HDT/Af(1.8) | 145 °C | ISO 75/Af |
Relative Temp Index, Elec | 105 °C | UL 746B |
Relative Temp Index, Mechanical with Impact | 105 °C | UL 746B |
Relative Temp Index, Mechanical without Impact | 105 °C | UL 746B |
Electrical | Nominal Value | Test Method |
Hot-wire Ignition, HWI ≥ 1.5 mm ≥ 0.75 mm |
PLC 3 PLC4 |
UL 746A |
High Amp Arc Ignition, HAI( ≥ 0.75 mm) | PLC 0 | UL 746A |
High Voltage Arc Tracking Rate, HVTR | PLC 0 | UL 746A |
Processing | Nominal Value | |
Drying Temperature<Injection> | 80 °C | |
Drying Time<Injection> | 4 hrs | |
Melt Temperature<Injection> | 225 - 250 °C | |
Front, Zone 3 Temperature<Injection> | 240 - 250 °C | |
Middle, Zone 2 Temperature<Injection> | 215 - 225 °C | |
Rear, Zone 1 Temperature<Injection> | 195 - 205 °C | |
Mold Temperature<Injection> | 30 - 50 °C | |
Back Pressure<Injection> | 0.2 - 0.3 MPa | |
Screw Speed <Injection> | 30 - 60 rpm |