Product Description | |||
(DOMOLEN P2-102-V30-N) Polypropylene, 30% glass fiber reinforced, improved flowability, for injection moulding, natural color | |||
General | |||
Form | Resin Pellets | ||
Filler | 30 % Glass Fiber | ||
Physical | Nominal Value | Test Method | |
Density | 1.12 g/cm³ | ISO 1183 | |
Melt Mass-Flow Rate, MFR(230 °C;2.16 kg) | 20 g/10min | ISO 1133 | |
Molding Shrinkage, Across Flow(50% RH;23 °C;72 hr) | 0.40 - 0.60 % | ISO 2577 | |
Molding Shrinkage, Flow(50% RH;23 °C;72 hr) | 0.10 - 0.30 % | ISO 2577 | |
Mechanical | Nominal Value | Test Method | |
Tensile Modulus | 5100 MPa | ISO 527-2/1 | |
Tensile Stress, Break | 60.0 MPa | ISO 527-2/5 | |
Tensile Strain, Break | 2.5 % | ISO 527-2/5 | |
Charpy Notched Impact Strength | ISO 179 1eA | ||
-30 °C | 4.7 kJ/m² | ||
23 °C | 6.1 kJ/m² | ||
Charpy Unnotched Impact Strength | ISO 179 1eU | ||
-30 °C | 20 kJ/m² | ||
23 °C | 25 kJ/m² | ||
Thermal | Nominal Value | Test Method | |
Heat Deflection Temperature, Unannealed 0.45 MPa 1.8 MPa |
140 °C 104 °C |
ISO 75-2/B ISO 75-2/A |
|
Vicat Softening Temperature | 77.0 °C | ISO 306/B50 | |
Melting Point | 167 °C | ISO 11357-3 | |
Burning rate | < 100 mm/min | FMVSS 302 | |
Flame Rating(1.5 - 3 mm) | HB | UL 94 | |
Processing | Nominal Value | ||
Processing Temp, Melt<Injection> | 200 - 280 °C | ||
Mold Temperature<Injection> | 20 - 60 °C |