ABS Resin TV front and rearframes and car audio consoles Weather Resistant
https://forever-plastics.en.made-in-china.com/product-list-1.html
Product Description | |||||
Features: Light Fast; Heat Resistant; 1.5mm V-0; 1.5mm 5VB; 2.5mm 5VA Applications: Displays; Chassis; Modems; Power Panels; Power Outlets; Car Batteries; projectors; large all-in-ones; coffee machines; TV front and rear frames and car audio consoles Weather Resistant |
|||||
General | |||||
Form | Resin Pellets | ||||
Feature | Outdoor | Good Thermal | |||
UL Yellow Card E56070-565072 | |||||
Light Covers Printer Parts Panel | |||||
Uses Projector Housing Socket Printer Chassis | |||||
Components | |||||
Physical Nominal Value Test Method | |||||
Density / Specific Gravity(23 °C) 1. 19 g/cm³ ISO 1183 | |||||
Melt Volume-Flow Rate, MVR(220 °C;10 kg) 28 cm³/ 10 min ISO 1133 | |||||
Molding Shrinkage 0.30 - 0.60 % ISO 294 -4 | |||||
Mechanical Nominal Value Test Method | |||||
Tensile Strength, Yield(50 mm/min) 36.0 MPa ISO 527 -2/50 | |||||
Tensile Strength, Break(50 mm/min) 27.0 MPa ISO 527 -2/50 | |||||
Tensile Elongation, Break(50 mm/min) 10 % ISO 527 -2/50 | |||||
Flexural Modulus(2 mm/min) 1700 MPa ISO 178 | |||||
Flexural Strength(2 mm/min) 55.0 MPa ISO 178 | |||||
C harpy Notched Impact Strength ISO 179 | |||||
-30 °C 7.0 kJ/m² | |||||
23 °C 13 kJ/m² | |||||
Notched Izod Impact ISO 180/1A | |||||
-30 °C 7.0 kJ/m² | |||||
23 °C 13 kJ/m² | |||||
Thermal | Nominal Value | Test Method | |||
Deflection Temperature Under Load, Unannealed(1.8 MPa) | 82.0 °C | ISO 75-2/A | |||
Deflection Temperature Under Load, Annealed(1.8 MPa) | 92.0 °C | ISO 75-2/A | |||
Vicat Softening Temperature | |||||
5 kg;50 ºC/hr | 90.0 °C | ISO 306/B50 | |||
50 ºC/hr;1 kg | 101 °C | ISO 306/A50 | |||
CLTE, Flow | 8.46E-5 cm/cm/°C | ISO 11359-2 | |||
Flame Rating 1.5 mm 1.5 mm 2.5 mm |
V-0 5VB 5VA |
UL 94 | |||
Processing | Nominal Value | ||||
Drying Temperature<Injection> | 80 - 85 °C | ||||
Drying Time<Injection> | 2.0 - 4.0 hr | ||||
Rear Temperature<Injection> | 180 - 210 °C | ||||
Middle Temperature<injection> | 190 - 220 °C | ||||
Front Temperature<Injection> | 190 - 220 °C | ||||
Mold Temperature<Injection> | 40 - 70 °C | ||||
Injection Pressure<Injection> | 4.90 - 7.85 MPa | ||||
Injection Rate<Injection> | Slow - Moderate | ||||
Holding Pressure<Injection> | 1.96 - 4.90 MPa | ||||
Back Pressure<Injection> | 0.490 - 0.981 MPa | ||||
Cushion<Injection> | 3.18 mm |