Polyamide 6 30% Mineral Filler Flame Retardant Halogen and Red Phosphorous Free

• Feature: Oxidative Degradable
• CAS No.: 32131-17-2
• Formula: (C12h22n2o2)N
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Model NO.: PA6-FR 6M30V0E
• EINECS: 211-024-8
• Material: Polyamide(Nylon 6.66)/PA
• Usage: General Plastics, Engineering Plastics, Specialty Plastics
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Injection
• Color: Black
• Form: Resin Pellets
• Chemical Substances: Nylon
• Processing Mode: Injection Molding/Extrusion
• UV: Fr
• Use: Electrical Appliances, Auto Parts, Office Supplies
• Certificates: ISO9001:2008.SGS.RoHS
• Filler: 10%-50% Glass Fiber
• Transport Package: Bag
• Specification: 25KG
• Trademark: Forever
• Origin: China
• HS Code: 390740000
• Production Capacity: 50000t/Year
• Package Size: 75.00cm * 55.00cm * 15.00cm
• Package Gross Weight: 25.010kg

Product Description

Polyamide 6, 30% mineral filler, flame retardant, halogen and red phosphorous free
 Heat-conducting nylon

Product Description

Product Description
( 6M30V0EF) Polyamide 6, 30% mineral filler, flame retardant, halogen and red phosphorous free, for injection moulding.
General
Form                                        Resin Pellets
Filler                                         30 % Mineral
		Non-Brominated & Non-
Feature		Chlorinated Flame
		Retardant
Physical		Nominal Value		Test Method
Density / Specific Gravity		1.42 g/cm³		ISO 1183
Molding Shrinkage, Across Flow(50% RH;23 °C;72 hr)		0.60 - 0.80 %		ISO 2577
Molding Shrinkage, Flow(50% RH;23 °C;72 hr)		0.50 - 0.70 %		ISO 2577
Mechanical		Nominal Value		Test Method
Tensile Modulus		5800 MPa		ISO 527-2/1
Tensile Stress, Break		70.0 MPa		ISO 527-2/5
Tensile Strain, Break		2.0 %		ISO 527-2/5
Flexural Modulus(2 mm/min)		5500 MPa		ISO 178
Flexural Stress(2 mm/min)		110 MPa		ISO 178
C harpy Notched Impact Strength(23 °C)		3.0 kJ/m²		ISO 179 1eA
C harpy Unnotched Impact Strength(23 °C)		30 kJ/m²		ISO 179 1eU
Notched Izod Impact Strength(23 °C)		3.5 kJ/m²		ISO 180/1A
Unnotched Izod Impact Strength(23 °C)		25 kJ/m²		ISO 180/1U
Thermal		Nominal Value		Test Method
Heat Deflection Temperature, Unannealed
0.45 MPa		200 °C		ISO 75-2/B
1.8 MPa		115 °C		ISO 75-2/A
Vicat Softening Temperature		200 °C		ISO 306/B50
Melting Point		221 °C		ISO 11357-3
Burning rate		< 100 mm/min		FMVSS 302
Flame Rating(1.5 mm)		V-0		UL 94
Glow Wire Flammability Index(1 - 3 mm)		960 °C		IEC 60695-2-12
Glow Wire Ignition Temperature [GWIT](1 - 3 mm)		750 °C		IEC 60695-2-13
Electrical	Nominal Value		Test Method
Surface Resistivity	1.0E+13 ohms		IEC 60093
Volume Resistivity	1.0e+15 ohms ·cm		IEC 60093
Comparative Tracking Index, Solution A	600 V		IEC 60112
Processing			Nominal Value
Drying Temperature<Injection>			75 - 85 °C
Drying Time<Injection>			2.0 - 4.0 hr
Processing Temp, Melt<Injection>			240 - 270 °C
Mold Temperature<Injection>			80 - 100 °C

 

                                                                                                                  Forever Co.,Ltd

 

With almost 20 years in the modified engineering plastics,Forever Plastics is a high-tech manufacture integrating R&D, production and sales of high-performance resin or polymer ,including PC,PP,PA6,PA66, PBT,PET, PC/ABS, PC/PBT, PC/PET alloy compounds,TPE,TPU, PE for rotomolding with the property of the flame retardant, glass fiber reinforced, high glossy, UV resistance.....with the annual output value of USD 65 million in 2021. 