Free Milky Translucent White Good Weather Resistance Light Diffusion PC Granules for LED

• Feature: Oxidative Degradable
• Material: Polyamide(Nylon 6.66)/PA
• Usage: General Plastics, Engineering Plastics, Specialty Plastics
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Model NO.: SLX1271D
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Injection
• Color: White
• Form: Resin Pellets
• Chemical Substances: Nylon
• Processing Mode: Injection Molding/Extrusion
• UV: Fr
• Use: Electrical Appliances, Auto Parts, Office Supplies
• Certificates: ISO9001:2008.SGS.RoHS
• Light Transmittance: 92%
• Transport Package: Bag
• Specification: 25KG
• Trademark: Forever
• Origin: China
• HS Code: 390740000
• Production Capacity: 50000t/Year

Product Description

 Free Milky Translucent white Good weather resistance Light diffusion PC Granules for Led

 

LNP ELCRES SLX1271D is a low viscosity, weatherable polycarbonate copolymer blend with enhanced UV   stabilization available in diffusive colors. It offers the potential for selective plating on PC/ABS in intricate   geometries via a 2K molding process. The material is an ideal material for automotive exterior applications.
 

Product Description
LNP ELCRES SLX1271D is a low viscosity, weatherable polycarbonate copolymer blend with enhanced UV   stabilization available in diffusive colors. It offers the potential for selective plating on PC/ABS in intricate   geometries via a 2K molding process. The material is an ideal material for automotive exterior applications.
General
Form	Resin Pellets
Feature                                     Excellent Processability    Outdoor                            Diffusive
Uses	Automotive	Electrical
Physical		Nominal Value		Test Method
Density		1.21 g/cm³		ISO 1183
Moisture Absorption(23 °C;50% RH/Equilibrium)		0.15 %		ISO 62-4
Water Absorption(23 °C;saturated)		0.32 %		ISO 62-1
Melt Volume Rate, MVR(1.2 kg;MVR at 300 °C)		16 cm³/10 min		ASTM D1238
Specific Gravity		1.2		ASTM D792
Melt Flow Rate[MFR](300 °C;1.2 kgf)		18 g/10min		ASTM D1238
Mold Shrinkage, Flow		0.75 %		SABIC Method
Mechanical		Nominal Value		Test Method
Notched Izod Impact Strength				ISO 180/1A
notched;80*10*3;23 °C 0		10 kJ/m²
80*10*3;0 °C;Notched		9 kJ/m²
notched;80*10*3;-30 °C 0		7 kJ/m²
Charpy Impact, V-Notched				ISO 179 1eA
23 °C;Edgew;80*10*3;sp=62mm 0		8 kJ/m²
-30 °C;Edgew;80*10*3;sp=62mm 0		7 kJ/m²
Multi-Axial Instrumented Impact, Total Energy				ISO 6603-2
23 °C		110 J
-30 °C		108 J
Izod Impact, Notched				ASTM D256
0 °C		99 J/m
23 °C		239 J/m
-30 °C		98 J/m
Instrumented Dart Impact, Total Energy(23 °C)		57 J		ASTM D3763
Instrumented Dart Impact, Peak force(23 °C)		5900 N		ASTM D3763

 

Tensile Modulus 1 mm/min 5 mm/min	2256 MPa 2292 MPa	ISO 527 ASTM D638
Tensile Stress, Yield 50 mm/min 50 mm/min;Type I	66 MPa 65 MPa	ISO 527 ASTM D638
Tensile Stress, Break 50 mm/min 50 mm/min;Type I	68 MPa 62 MPa	ISO 527 ASTM D638
Tensile Strain, Yield 50 mm/min 50 mm/min;Type I	6.2 % 6.3 %	ISO 527 ASTM D638
Tensile Strain, Break 50 mm/min 50 mm/min;Type I	115 % 83 %	ISO 527 ASTM D638
Flexural Modulus 2 mm/min 1.3 mm/min;50 mm;span	2255 MPa 2480 MPa	ISO 178 ASTM D790
Flexural Strength 2 mm/min 1.3 mm/min;50 mm;span	97 MPa 98 MPa	ISO 178 ASTM D790

 

Thermal	Nominal Value	Test Method
HDT/Af(1.8)	123 °C	ISO 75/Af
HDT/Bf(0.45)	134 °C	ISO 75/Bf
Vicat Softening Temperature
Rate B/50	138 °C	ISO 306
Rate B/120	139 °C	ISO 306
Rate B/50	138 °C	ASTM D1525
Rate B/120	139 °C	ASTM D1525
CTE, Flow 23°C to 50°C 23°C to 50°C	7.1e-05 1/°C 7.1e-05 1/°C	ISO 11359-2 ASTM E831
CTE, XFlow 23°C to 50°C 23°C to 50°C	7.2e-05 1/°C 7.2e-05 1/°C	ISO 11359-2 ASTM E831
Heat Deflection Temperature[HDT], Unannealed 3.2 mm;1.82 MPa 0.45 MPa;3.2 mm	123 °C 133 °C	ASTM D648
Processing		Nominal Value
Drying Temperature<Injection>		120 °C
Drying Time<Injection>		2 - 4 hrs
Maximum Moisture Content<Injection>		0.02 %
Melt Temperature<Injection>		280 - 310 °C
Rear, Zone 1 Temperature<Injection>		260 - 280 °C
Middle, Zone 2 Temperature<Injection>		270 - 290 °C
Front, Zone 3 Temperature<Injection>		280 - 310 °C
Nozzle Temperature<Injection>		270 - 290 °C
Mold Temperature<Injection>		80 - 110 °C

 

                                                                                                                  Forever Co.,Ltd

With almost 20 years in the modified engineering plastics,Forever Plastics is a high-tech manufacture integrating R&D, production and sales of high-performance resin or polymer ,including PC,PP,PA6,PA66, PBT,PET, PC/ABS, PC/PBT, PC/PET alloy compounds,TPE,TPU, PE for rotomolding with the property of the flame retardant, glass fiber reinforced, high glossy, UV resistance.....with the annual output value of USD 65 million in 2021. 