Feature: | Plastics |
---|---|
CAS No.: | 25766-59-0 |
Formula: | C6h4c(CH3)2c6h4oco2-]N |
Samples: |
---|
Customization: |
---|
Shipping Cost:
Estimated freight per unit. |
about shipping cost and estimated delivery time. |
---|
Payment Method: | |
---|---|
Initial Payment Full Payment |
Currency: | US$ |
---|
Return&refunds: | You can apply for a refund up to 30 days after receipt of the products. |
---|
Suppliers with verified business licenses
General | ||||
Form Resin Pellets | ||||
Filler 15 % Stainless Steel Fiber | ||||
Electrically Conductive | Emi/Rfi Shielding | High Impact | ||
Feature | Non-Brominated & Non-Chlorinated Flame Retardant | Non-Chlorinated | ||
Uses |
Consumer Electrical |
Packaging | Industria | |
Physical | Nominal Value | Test Method | ||
Mold Shrinkage, Flow(24 hrs) | 0.4 - 0.7 % | ISO 294 | ||
Mold Shrinkage, XFlow(24 hrs) | 0.5 % | ISO 294 | ||
Density / Specific Gravity | 1.29 g/cm³ | ISO 1183 | ||
Mechanical | Nominal Value | Test Method | ||
Izod Impact, Unnotched | ||||
23 °C | 1790 J/m | ASTM D4812 | ||
80*10*4;23 °C | 85 kJ/m² | ISO 180/1U | ||
Izod Impact, Notched | ||||
23 °C | 124 J/m | ASTM D256 | ||
80*10*4;23 °C | 14 kJ/m² | ISO 180/1A | ||
Tensile Stress, Yield | 57 MPa | ISO 527 | ||
Tensile Stress, Break | 55 MPa | ISO 527 | ||
Tensile Strain, Yield | 3.8 % | ISO 527 | ||
Tensile Strain, Break | 4 - 8 % | ISO 527 | ||
Tensile Modulus(1 mm/min) | 2800 MPa | ISO 527 | ||
Flexural Stress | 80 MPa | ISO 178 | ||
Flexural Modulus | 2600 MPa | ISO 178 |
Thermal | Nominal Value | Test Method |
CTE, Flow(-40 - 40 °C) | 5.6E-05 1/°C | ISO 11359-2 |
CTE, XFlow(-40 - 40 °C) | 6.7e-05 1/°C | ISO 11359-2 |
HDT/Bf(0.45) | 136 °C | ISO 75/Bf |
HDT/Af(1.8) | 125 °C | ISO 75/Af |
Electrical | Nominal Value | Test Method |
Volume Resistivity | 1.0E+04 ohms ·cm | ASTM D257 |
Surface Resistivity | 100 - 1.0E+04 ohms | ASTM D257 |
Processing | Nominal Value | |
Drying Temperature<Injection> | 120 °C | |
Drying Time<Injection> | 4 hrs | |
Maximum Moisture Content<Injection> | 0.02 % | |
Melt Temperature<Injection> | 305 - 325 °C | |
Front, Zone 3 Temperature<Injection> | 320 - 330 °C | |
Middle, Zone 2 Temperature<Injection> | 310 - 320 °C | |
Rear, Zone 1 Temperature<Injection> | 295 - 305 °C | |
Mold Temperature<Injection> | 95 - 120 °C | |
Back Pressure<Injection> | 0.2 - 0.3 MPa | |
Screw Speed <Injection> | 30 - 60 rpm |